12Cr2Mo1R heavy plate under critical hydrogen and heat treatment process thereof

A large-thickness, steel plate technology, applied in the field of large-thickness hydrogen-facing 12Cr2Mo1R steel plate and its heat treatment process, can solve the problems of performance degradation, large-thickness steel plate can not meet the performance parameters, etc., to achieve the improvement of mechanical properties, optimize normalizing and tempering Effect of temperature and holding time, good high temperature mechanical properties

Inactive Publication Date: 2011-03-09
WUYANG IRON & STEEL +1
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the steel plate develops in the direction of large thickness, it often encounters the problem of performance degradation in various aspects. If the thickness of the steel plate is directly increased on the basis of maintaining the existing ratio and proc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The large-thickness hydrogen-facing 12Cr2Mo1R steel plate of this embodiment is composed of the following components in weight percentage: C 0.12%, Si 0.05%, Mn 0.50%, P 0.004%, S 0.004%, Cr 2.42%, Mo 0.95%, Al 0.045%, Nb 0.017%, Cu 0.09%, Sb 0.001%, Sn 0.012%, As 0.010%, O 0.001%, N 0.006%, H 0.0001%, the balance is Fe and unavoidable impurities. The thickness of the steel plate is 155mm.

[0018] The heat treatment process of the present embodiment is as follows:

[0019] 1) Normalizing treatment: The rolled steel plate is subjected to normalizing treatment, the normalizing temperature is 930°C, and the holding time is 2min / mm (per millimeter steel plate thickness) + 90min;

[0020] 2) Water cooling treatment: water-cool the normalized steel plate with a quenching machine, and use high-pressure water and low-pressure water to cool it in sections. 3 / h, then carry out low-pressure water cooling, the water pressure is 6bar, and the water volume is 3100m 3 / h, the tra...

Embodiment 2

[0023] The large-thickness hydrogen-facing 12Cr2Mo1R steel plate of this embodiment is composed of the following components in weight percentage: C 0.13%, Si 0.08%, Mn 0.55%, P 0.003%, S 0.002%, Cr 2.35%, Mo 1.05%, Al 0.020%, Nb 0.020%, Cu 0.15%, Sb 0.001%, Sn 0.010%, As 0.010%, O 0.001%, N 0.004%, H 0.0001%, and the balance is Fe and unavoidable impurities. The thickness of the steel plate is 163mm.

[0024] The heat treatment process of the present embodiment is as follows:

[0025] 1) Normalizing treatment: the rolled steel plate is subjected to normalizing treatment, the normalizing temperature is 940°C, and the holding time is 2min / mm (per millimeter steel plate thickness) + 70min;

[0026] 2) Water cooling treatment: water-cool the normalized steel plate with a quenching machine, and use high-pressure water and low-pressure water to cool in sections. First, high-pressure water cooling is performed, with a water pressure of 12bar and a water volume of 3600m 3 / h, then c...

Embodiment 3

[0029] The large-thickness hydrogen-facing 12Cr2Mo1R steel plate of this embodiment is composed of the following components in weight percentage: C 0.15%, Si 0.10%, Mn 0.60%, P 0.005%, S 0.003%, Cr 2.50%, Mo 1.00%, Al 0.037%, Nb 0.013%, Cu 0.12%, Sb 0.002%, Sn 0.009%, N 0.004%, and the balance is Fe and unavoidable impurities. The thickness of the steel plate is 170mm.

[0030] The heat treatment process of the present embodiment is as follows:

[0031] 1) Normalizing treatment: The rolled steel plate is subjected to normalizing treatment, the normalizing temperature is 960°C, and the holding time is 2min / mm (per millimeter steel plate thickness) + 50min;

[0032] 2) Water-cooling treatment: water-cool the normalized steel plate with a quenching machine, and use high-pressure water and low-pressure water to cool in sections. 3 / h, then carry out low-pressure water cooling, the water pressure is 7bar, and the water volume is 3000m 3 / h, the traveling speed of steel plate coo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a 12Cr2Mo1R heavy plate under critical hydrogen, which comprises, by weight, 0.12 to 0.15 percent of C, equal to less than 0.10 percent of Si, 0.50 to 0.60 percent of Mn, equal to or less than 0.008 percent of P, equal to or less than 0.005 percent of S, 2.35 to 2.50 percent of Cr, 0.95 to 1.05 percent of Mo, 0.020 to 0.045 percent of Al, 0.013 to 0.020 percent of Nb, equal to or less than 0.15 percent of Cu, equal to or less than 0.003 percent of Sb, equal to or less than 0.015 percent of Sn, equal to or less than 0.016 percent of As, equal to or less than 0.002 percent of O, equal to or less than 0.008 percent of N, equal to or less than 0.0002 percent of H, and the balance Fe as well as unavoidable impurities. The standard of 12Cr2Mo1R heavy plate under critical hydrogen defined by national standard GB 713-2008 has been improved. Constituent elements of 12Cr2Mo1R heavy plate under critical hydrogen and the proportion of the elements have also been optimized. The thickness of the obtained 12Cr2Mo1R heavy plate under critical hydrogen is within 155-170 mm, thereby increasing the thickness of the plate while ensuring the mechanical properties of the plate to be compatible with the standards for plates with a thickness of less than 150 mm defined by national standard 713-2008.

Description

technical field [0001] The invention relates to a large-thickness hydrogen-facing 12Cr2Mo1R steel plate and a heat treatment process thereof, belonging to the technical field of iron and steel. Background technique [0002] The hydrogen 12Cr2Mo1R steel plate is formulated according to the national standard GB713-2008, but the maximum thickness of the hydrogen 12Cr2Mo1R steel plate in the national standard is 150mm. However, with the development of economy and technology, the market also has a great demand for thicker hydrogen-facing 12Cr2Mo1R steel plates, especially large-thickness hydrogen-facing steel plates greater than 150mm. However, when the steel plate develops in the direction of large thickness, it often encounters the problem of performance degradation in various aspects. If the thickness of the steel plate is directly increased on the basis of maintaining the existing ratio and process, the obtained large thickness steel plate cannot reach The performance parame...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/26C21D8/02
Inventor 尚建雄
Owner WUYANG IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap