One-component water-based semi-gloss varnish and preparation method thereof

A matte varnish, one-component technology, applied in the field of coatings, can solve problems such as poor chemical resistance, poor hand feeling, and low hardness, and achieve the effects of low physical hazards, reduced environmental pollution, and overcoming fullness

Active Publication Date: 2011-04-20
HUIZHOU CHANGRUNFA PAINT
View PDF5 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, my country's water-based coatings are now in the initial stage of technology, especially the one-component water-based matte varnish, which has technical defects such as insufficient fullness, low hardness, poor hand feeling, and poor chemical resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The one-component water-based matte varnish of the present embodiment, its raw material formula is made up of each component of following percentage by weight:

[0038] Water-based acrylic emulsion 50.0 %;

[0039] Waterborne aliphatic polyurethane emulsion 20.0 %;

[0040] Coalescing aid 7.0%;

[0041] Defoamer 0.6%;

[0042] Dispersant 0.5%;

[0043] Matting powder 1.0 %;

[0044] Wax additive 1.0%;

[0045] Hand additive 0.5%;

[0046] Thickener 0.5%;

[0047] Cross-linking agent 0.3%;

[0048] Water 18.6%.

[0049] The above-mentioned water-based acrylic emulsion is Opeldi AC 2514;

[0050] The above-mentioned aqueous aliphatic polyurethane emulsion is Bayer XP2557;

[0051] Above-mentioned film-forming aid is dipropylene glycol butyl ether;

[0052] The above-mentioned defoamer adopts silicone defoamer BYK024;

[0053] The above-mentioned dispersant adopts polyacrylic acid amine salt SN-5040;

[0054] The above matting powder adopts silica matting powd...

Embodiment 2

[0066] The one-component water-based matte varnish of the present embodiment, its raw material formula is made up of each component of following percentage by weight:

[0067] Water-based acrylic emulsion 60.0 %;

[0068] Waterborne aliphatic polyurethane emulsion 10.0 %;

[0069] Coalescing agent 6.0%;

[0070] Defoamer 0.6%;

[0071] Dispersant 0.5%;

[0072] Matting powder 1.0 %;

[0073] Wax additive 1.0%;

[0074] Hand additive 0.5%;

[0075] Thickener 0.5%;

[0076] Cross-linking agent 0.3%;

[0077] Water 19.6%.

[0078] The above water-based acrylic emulsion adopts DSM A-639;

[0079] The above water-based aliphatic polyurethane emulsion adopts Opeldi CUR-995;

[0080] Above-mentioned coalescent aid adopts propylene glycol butyl ether;

[0081] The above-mentioned defoamer adopts organosilicon defoamer TeGo 810;

[0082] The above-mentioned dispersant adopts polyacrylic acid amine salt SN-5040;

[0083] The above matting powder adopts silica matting powder...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a one-component water-based semi-gloss varnish and a preparation method thereof. The one-component water-based semi-gloss varnish comprises the raw material formulas in percentage by mass: 30-60% of water-based acrylic emulsion, 5-30% of water-based aliphatic series polyurethane emulsion, 3-10% of film forming assistant, 0.01-2% of antifoaming agent, 0.01-2% of dispersing agent, 0.1-5% of extinction powder, 0.01-2% of wax assistant, 0.01-2% of hand feeling assistant, 0.01-2% of thickening agent, 0.01-2% of cross-linking agent and 5-40% of water. The one-component water-based semi-gloss varnish of the invention has the advantages of super strong hand feeling, high fullness, high hardness, good chemical resistance, very low bodily injury on production and construction workers, and very low environmental pollution.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to water-based coatings, in particular to a one-component water-based matte varnish with super strong hand feeling and a preparation method thereof. Background technique [0002] At present, most of the wood coatings used in my country are solvent-based, and these wood coatings contain a large amount of volatile organic compounds (VOC), which seriously endanger the health of production and construction personnel. [0003] With the enhancement of people's awareness of environmental protection, traditional solvent-based coatings are facing severe challenges, while water-based coatings have the advantages of non-toxic, non-flammable, and non-polluting environment, and have attracted more and more attention. [0004] Water-based coatings combine the high performance of solvent-based coatings with the low VOC content of water-based coatings, which have good environmental effects and rel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D175/04C09D7/12
Inventor 许田
Owner HUIZHOU CHANGRUNFA PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com