Method for manufacturing moderate intensity aluminium alloy wire with 57% electric conductivity
A medium-strength aluminum alloy, conductivity technology, applied in the direction of metal/alloy conductors, root rods/rods/wires/strip conductors, etc., can solve the problems of unstable manufacturing process, tensile strength does not reach stable production, etc., to achieve crystallization Good condition, obvious effect, excellent performance effect
Active Publication Date: 2011-05-04
SHANGHAI ZHONGTIAN ALUMINUM WIRE
View PDF4 Cites 37 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, due to the defects of manufacturing equipment and the instability of manufacturing process, the main properties of high-conductivity medium-strength aluminum alloy wire, conductivity and tensile strength, have not yet reached the goal of stable production.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0028] The present invention will be further described below in conjunction with accompanying drawing and embodiment process:
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM

Abstract
The invention provides a method for manufacturing a moderate intensity aluminium alloy wire with 57% electric conductivity, and relates to a method for manufacturing a moderate intensity aluminium alloy wire of which the electric conductivity reaches 57% (IACS), which comprises the following steps of: (1) selecting aluminum matrixes and aluminum moderate alloy ingots; (2) carrying out on-the-spot sample analysis and regulation; placing the selected aluminum ingots into a shaft furnace to be melted to obtain an aluminum liquid; and refining with a refining agent; (3) casting and crystallizing: enabling the aluminium alloy liquid in a tilting holding furnace to pass through a trough, and filtering with a ceramic filter plate, and adding a rear earth to ensure the rear earth content to be 0.05-0.15%; continuously casting in an aluminium alloy continuous casting machine to form the aluminium alloy ingots; and rolling the aluminium alloy ingots to obtain moderate intensity aluminium alloy rods by an aluminium alloy continuous mill; (4) solutionizing and quenching: carrying out homogenizing heat treatment on the aluminium alloy rods; and (5) drawing, ageing and twisting: drawing the aluminium alloy rods treated by the former process into the aluminium alloy wires with the required diameter on an aluminium alloy drawing machine, and twisting the aluminium alloy wires by using a frame-type wire twisting machine to manufacture the moderate intensity aluminium alloy wires with 57% electric conductivity in IACS.
Description
technical field [0001] The invention relates to a method for manufacturing a medium-strength aluminum alloy wire with a conductivity of 57% (IACS), which is a high-conductivity aluminum alloy manufacturing technology. More precisely, it is a method of manufacturing high-conductivity medium-strength aluminum alloy wire. Background technique [0002] In the past, my country did not develop and apply medium-strength aluminum alloys for electrical conduction, but with the development of overhead lines to large capacity and ultra-high voltage, the use of split wires and wires with large cross-sections and heat resistance has gradually developed. In this way, not only heat-resistant aluminum alloy wires are required, but also medium-strength or high-strength aluminum alloy wires are required to replace ordinary steel-cored aluminum stranded wires, medium-strength or high-strength aluminum alloy stranded wires to increase the carrying capacity of the wires. [0003] At present, in...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline

Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/08C22C1/02C22F1/05H01B1/02H01B5/02
Inventor 薛驰薛济萍陆伟尤伟任冯爱军缪小林徐一峰
Owner SHANGHAI ZHONGTIAN ALUMINUM WIRE
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com