Method for preparing copper based pantograph pan material

A pantograph sliding plate, copper-based technology, applied in the field of accessories used in transportation vehicles, can solve the problems of high resistivity and poor impact toughness, and achieve the effects of low resistivity, low wear and excellent electrical conductivity.

Inactive Publication Date: 2011-05-18
UNIV OF SCI & TECH BEIJING
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The skateboard has excellent friction and wear properties,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1

[0023] The dispersion strengthened copper powder, copper-plated graphite powder and additives tin and lead are mixed in a certain proportion, and the content of copper-plated graphite as lubricating material is 20wt%. The particle size of copper-plated graphite is 100μm, the copper content is 60 wt%, and the additives The content of tin is 4wt%, the content of lead additive is 2wt%, and the dispersion strengthened copper is the balance. The mixing time is 5 hours. Put the mixed material into the hot press at a temperature of 850℃ and a pressure of Perform hot pressing at 30 MPa and hold the pressure for 30 minutes to obtain a good performance electric locomotive pantograph skateboard material;

Example Embodiment

[0024] Example 2

[0025] The dispersion strengthened copper powder, copper-plated graphite powder and additives tin and lead are mixed in a certain proportion, and the content of copper-plated graphite as lubricating material is 25wt%. The particle size of copper-plated graphite is 125μm, the copper content is 50wt%, and the additive tin The content of the additive is 5wt%, the content of the additive lead is 3wt%, and the dispersion strengthened copper is the balance. The mixing time is 8 hours. Put the mixed material into the hot press at a temperature of 900℃ and a pressure of 40MPa Carry out hot pressing and hold the pressure for 40 minutes to obtain a good performance electric locomotive pantograph skateboard material;

Example Embodiment

[0026] Example 3

[0027] The dispersion strengthened copper powder, copper-plated graphite powder and additives tin and lead are mixed in a certain proportion. The content of copper-plated graphite as lubricating material is 30wt%. The particle size of copper-plated graphite is 150μm, the copper content is 40wt%, and the additive tin The content of the additive is 6wt%, the content of the additive lead is 4wt%, and the dispersion strengthened copper is the balance. The mixing time is 10 hours. Put the mixed material into the hot press at a temperature of 950℃ and a pressure of 50MPa Perform hot pressing under pressure and hold the pressure for 50 minutes to obtain a good performance electric locomotive pantograph slide material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for preparing a copper based pantograph pan material, belonging to the technical field of the preparation of a copper graphite self-lubricating composite material. The copper based pantograph pan material is prepared by the steps of: mixing dispersion-strengthening copper powder used as a base body, copper plated graphite used as a wear-reducing material and tin and lead powder used as additives uniformly by a mixing machine and then thermally pressing and sintering. The dispersion-strengthening copper powder is replaced with the traditional pure copper powder as the base body and has more excellent performance. Because the dispersion-strengthening copper has excellent high-temperature strength, rigidity and wear resistance and fusion welding resistance, the pantograph pan material prepared by adopting the dispersion-strengthening copper powder as the base body has more excellent wear resistance, fusion welding resistance and electrolytic corrosion resistance. The preparation method is simple, is easy to control the process, has no pollution, and is suitable for massive production.

Description

[0001] technical field [0002] The invention belongs to the technical field of preparation of copper-graphite self-lubricating composite materials. The composite material can be used to prepare electric locomotive pantograph slide plates, and belongs to an accessory used by transportation vehicles. [0003] Background technique [0004] With the rapid development of my country's high-speed railways, as the most important current-collecting components of high-speed trains, the amount of pantograph slides is increasing. Currently known pantograph slides are as follows: [0005] 1. Pure metal skateboard [0006] This type of skateboard is made of steel, copper and other materials. It is a pantograph skateboard product used by electric locomotives in the 1960s in my country. This type of skateboard has high mechanical strength, convenient material acquisition, long service life and low cost. However, due to the similar material of the slide plate and the wire, strong aff...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F3/02
Inventor 郭志猛罗骥曹慧钦杨薇薇
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap