Method for reducing surface viscosity of bionic glue by using curing agents
A technology of curing agent and biomimetic glue, applied in the direction of application, adhesive type, ester copolymer adhesive, etc., can solve the problems of biomimetic glue agricultural products such as inconvenient harvesting, achieve good waterproof performance, good effect, and reduce viscosity Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] The preparation of embodiment 1 bionic glue
[0033] The composition and ratio of raw materials of bionic rubber are: 30kg butyl acrylate, 16kg methyl methacrylate, 3kg methacrylic acid, 600g sodium lauryl sulfate, 400g potassium persulfate, BRONOPOL (bromine Nitrol) antifungal agent 10g, mineral oil defoamer 100g, nonylphenol polyoxyethylene ether (OP-10) 300g, deionized water 49.59kg.
[0034] Prepare as follows:
[0035] (1) Add 10 kg of deionized water, 30 kg of butyl acrylate, 16 kg of methyl methacrylate, 3 kg of methacrylic acid, and 480 g of sodium lauryl sulfate into the reactor 1, and stir for 20 minutes at a speed of 50 rpm to obtain approximately Emulsion 59.48kg;
[0036] (2) Add 35.0 kg of deionized water, 120 g of sodium lauryl sulfate, and 80 g of potassium persulfate into the reactor 2, and stir and react for 10 minutes at 80° C. at a speed of 45 rpm; the reactor 2 is stirred at a speed of 45 rpm throughout;
[0037] (3) Extract 9.0 kg of emulsion fr...
Embodiment 2
[0040] The preparation of embodiment 2 liquid curing agent
[0041] Put polyvinyl alcohol into water at a ratio of 10% by mass, stir evenly, heat up to 80°C, react for 30 minutes, then cool down to 40°C, add organic fluorine surfactant at a ratio of 0.05% by mass, and stir Uniform, packaged and sealed for use.
Embodiment 3
[0042] The preparation of embodiment 3 liquid curing agent
[0043] Put polyvinyl alcohol into water at a mass percentage of 50%, stir evenly, heat up to 80°C, react for 30 minutes, cool down to 40°C, add organic fluorine surfactant at a mass percentage of 0.1%, and stir evenly , packaged and sealed for later use.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com