Glazed low-temperature bright-red glaze and production process for ceramic products thereof

A ceramic product, bright red technology, applied in the field of ceramics, can solve the problems affecting the appearance quality of the product, the color material is not easily adsorbed, the color glaze is easy to fall off, etc., and achieves the effect of easy mass production, enhanced water content, and reduced sintering temperature.

Inactive Publication Date: 2011-06-22
潮州市波士发陶瓷制作有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] On the other hand, because the overglaze color is glazed on the surface of the ceramic product after high-temperature firing, the surface of the high-temperature fired ceramic product is relatively smooth, does not absorb water, and the color material is not easy to absorb, which leads to the surface of the over-glaze color product being easy to absorb. Disadvantages such as uneven glaze application and easy fall off of colored glaze have seriously affected the appearance quality of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1. Preparation of low-temperature frit: the weight percentage of the chemical composition of the low-temperature frit is: Li 2 O 2.4%, KNaO 6.3%, SiO 2 45.7%, Fe 2 o 3 0.03%, Al 2 o 3 6.4%, CaO 4.6%, B 2 o 3 28.9%, SrO 3.6%, ZrO 1.0%, and F 1.2%. The melting temperature of the frit is 1200°C, and the holding time is 30 minutes. After water quenching, it is crushed and dried for future use.

[0021] 2. Glaze batching: by weight percentage, 40% of brilliant red pigment and 60% of the above-mentioned low-temperature frit are mixed into synthetic material, and then 200ml of sodium polypropionate and 320ml of water are added in every kilogram of synthetic material.

[0022] 3. Ball milling: Mix the above ingredients evenly, add them into a ball mill and mill them for 12 hours.

[0023] 4. Screening: the above ball-milled glaze slurry is screened with a fineness of 320 mesh.

[0024] 5. Glazing: Apply glaze on the ceramic products fired at high temperature by dipping...

Embodiment 2

[0027] 1. Preparation of low-temperature frit: the weight percentage of the chemical composition of the low-temperature frit is: Li 2 O 2.4%, KNaO 7.9%, SiO 2 43.1%, Fe 2 o 3 0.03%, Al 2 o 3 6.9%, CaO4.8%, B 2 o 3 27.1%, SrO 6.1%, ZrO 1.0%, and F 1.6%. The melting temperature of the frit is 1240°C, and the holding time is 30 minutes. After water quenching, it is crushed and dried for future use.

[0028] 2, glaze material batching: be mixed into synthetic material by bright red pigment 43% and above-mentioned low-temperature frit 57% by weight percentage, add sodium polypropionate 220ml and water 340ml in every kilogram of synthetic material again.

[0029] 3. Ball milling: Mix the above ingredients evenly, add them into a ball mill and mill them for 12 hours.

[0030] 4. Screening: the above ball-milled glaze slurry is screened with a fineness of 320 mesh.

[0031] 5. Glazing: Glazing is applied on the high-temperature fired ceramic body by dipping glaze and dried in...

Embodiment 3

[0034] 1. Preparation of low-temperature frit: the weight percentage of the chemical composition of the low-temperature frit is: Li 2 O 1.4%, KNaO 7.4%, SiO 2 45.8%, Fe 2 o 3 0.03%, Al 2 o 3 4.9%, CaO 5.6%, B 2 o 3 28.5%, SrO 4.6%, ZrO 1.0%, and F 1.6%. The melting temperature of the frit is 1250°C, and the holding time is 30 minutes. After water quenching, it is crushed and dried for future use.

[0035] 2, glaze material batching: be mixed into synthetic material by bright red pigment 45% and above-mentioned low-temperature frit 55% by weight percentage, add sodium polypropionate 250ml and water 350ml in every kilogram of synthetic material again.

[0036] 3. Ball milling: Mix the above ingredients evenly, add them into a ball mill and mill them for 12 hours.

[0037] 4. Screening: the above ball-milled glaze slurry is screened with a fineness of 320 mesh.

[0038] 5. Glazing: Apply glaze on the ceramic products fired at high temperature by dipping glaze, and dry in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a glazed low-temperature bright-red glaze and a production process for ceramic products thereof, and belongs to the technical field of ceramics. The glazed low-temperature bright-red glaze is prepared by mixing 40 to 45 weight percent of bright-red pigment and 55 to 60 weight percent of low-temperature clinker, wherein the low-temperature clinker comprises the following components in percentage by weight: 1.2 to 2.4 percent of Li2O, 6.3 to 7.7 percent of KNaO, 43.1 to 46.2 percent of SiO2, 0.03 percent of Fe2O3, 4.9 to 6.9 percent of Al2O3, 4.9 to 5.6 percent of CaO, 27.2 to 28.9 percent of B2O3, 3.6 percent of SrO, 1.0 percent of ZrO and 1.2 to 1.6 percent of F. The production process for the ceramic products of the glazed low-temperature bright-red glaze comprises the following steps of: preparing the glaze, adding a deflocculating agent and water, mixing uniformly, performing ball milling, sieving, glazing, drying in the shade, and roasting. The technology is easy to implement; and the products have the characteristics of firm combination of blanks and the glaze, bright colors, high gloss and hardness, no toxin and the like.

Description

technical field [0001] The invention relates to a production process of an on-glaze low-temperature brilliant red glaze and ceramic products thereof, belonging to the technical field of ceramics. Background technique [0002] At present, overglaze coloring is a decoration method widely used in ceramic products. The traditional overglaze color production process is to add 30-50% lead oxide, so that the firing temperature range of the ceramic overglaze pigment is wide and the color is pure. However, lead is harmful to the environment and human body during the production and use of ceramic pigments. Therefore, many research and development institutions and manufacturers are trying to find an additive that can replace lead oxide, and at the same time make ceramic glazes have the characteristics of low firing temperature and bright color. At present, there have been the use of Bi 2 o 3 The advantages of low melting point instead of lead oxide. But bismuth is also toxic, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 吴波利柯为郁
Owner 潮州市波士发陶瓷制作有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap