A production method and a technology for plastic blanks, applied in the field of plastic blanks, can solve the problems affecting the quality of ceramic products, low yield value, small extension deformation, etc., and achieve the effects of low production cost, high yield value, and large extension deformation.

Inactive Publication Date: 2011-08-31
XUYI KEYUAN NEW MATERIALS FACTORY
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main processes of plastic forming are spinning forming and rolling forming, which require uniform water content, consistent structure, good plasticity, high yield value and large elongation deformation of the billet, but some newly developed china clay raw materials have low yield value and elongation. The amount of deformation is small, which directly affects the quality of ceramic products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] Below in conjunction with embodiment the present invention will be further described:

[0028] 1. The production method of the attapulgite ceramic plastic blank is: (1) input the ingredients of the attapulgite ceramic plastic blank into a pulverizer for pulverization after mixing, and the fineness of the pulverized mixture is less than 0.25 mm; (2) the pulverized The mixture is added into the immersion tank for soaking and sodium treatment to form a wet mixture, and the soaking and sodium treatment time is controlled within 5 days; (3) the wet mixture is input into a pair of rollers and pressed into a sheet, the thickness of the sheet is less than 3 mm; (4) the sheet is input into the extruder to be extruded into a cylindrical strip, and the diameter of the cylindrical strip is controlled at 3 millimeters; (5) the cylindrical strip is input to the cement drying yard for drying. Drying, the water content of the cylindrical strips after drying is less than 15%; (6) Input ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production method for an attapulgite ceramic plastic mass. The key point of the technical scheme is that the production method comprises the following steps of: crushing ingredients of the attapulgite ceramic plastic mass, performing sodium treatment on the crushed mixture into a moist mixture, pressing the moist mixture into a sheet, extruding into a strip, airing the strip, grinding, removing iron from powder, adding water into the powder, extruding into a cylindrical strip, and packaging into the finished product of the attapulgite ceramic plastic mass. The attapulgite ceramic plastic mass consists of attapulgite clay, white bentonite, sepiolite, calcined clay, sodium metasilicate and sodium carbonate. The attapulgite ceramic plastic mass has uniform water content and consistent structure, and has the characteristics of good cohesiveness, plasticity, high yield value and large extension deformation; ceramic products prepared from the attapulgite ceramic plastic mass have the characteristics of small shrinkage, no deformation, high strength, and uniform texture; and the attapulgite ceramic plastic mass is suitable for producing the ceramic products.

Description

technical field [0001] The invention relates to a plastic blank, in particular to a production method of an attapulgite ceramic plastic blank. Background technique [0002] The composition of China clay is mainly kaolin, and contains feldspar, quartz stone, mica, iron ore and other rock fragments as the source of China clay. China clay is the main raw material of ceramics. The development of high-grade daily-use porcelain requires high-quality kaolin as raw material. With the rapid development of the domestic ceramic industry in 2009, the consumption of kaolin has also increased sharply. However, with the depletion of high-quality kaolin veins, the price of china clay has skyrocketed day by day. [0003] On the premise of ensuring the quality of china clay, develop new china clay raw materials to replace kaolin or reduce the amount of kaolin to protect our ecological environment and provide more sufficient raw material guarantee for the future development of high-grade daily...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/38C04B7/40
Inventor 柏正基许庆华林光霞
Owner XUYI KEYUAN NEW MATERIALS FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap