Preparation method of multi-functional liquid glue
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A liquid glue, multi-functional technology, used in adhesives, adhesive types, unsaturated alcohol copolymer adhesives, etc., can solve the problems of human health, strong limitations, etc. , the effect of strong stickiness
Active Publication Date: 2013-07-10
JIANGSU XINGDA STATIONERY GRP
View PDF1 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0006] However, 502 glue, Baide glue and other glues contain organic solvents such as toluene, benzene, and acetone, which have an impact on human health and have relatively strong limitations in use.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] Add the raw materials according to the following proportions by weight: at 23°C, add 5 parts of deionized water and 10 parts of polyvinyl alcohol to the reaction kettle, heat up to 90°C, add 25 parts of butyl acetate, glycerin 15 parts of alcohol, heat preservation reaction for 1 hour, lower to 23 ℃, add 8 parts of ethanol, 20 parts of polyvinyl acetate, and then add appropriate amount of preservative and defoamer, static defoaming.
Embodiment 2
[0021] Add the raw materials according to the following proportions by weight: at 20°C, add 5 parts of deionized water and 15 parts of polyvinyl alcohol to the reaction kettle, heat up to 90°C, add 20 parts of butyl acetate, glycerin 20 parts of alcohol, keep warm for 1 hour, lower to 20 ℃, add 15 parts of ethanol, 15 parts of polyvinyl acetate, and then add appropriate amount of preservative and defoamer, static defoaming.
Embodiment 3
[0023] Add the raw materials according to the following proportions by weight: at 25°C, add 5 parts of deionized water and 12 parts of polyvinyl alcohol to the reaction kettle, heat up to 90°C, add 22 parts of butyl acetate, glycerin 18 parts of alcohol, heat preservation reaction for 1 hour, lowered to 23 ℃, then added 10 parts of ethanol, 17 parts of polyvinyl acetate, and then added appropriate amount of preservative and defoamer, static defoaming.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a preparation method of multi-functional liquid glue. The preparation method comprises: adding 5 parts by weight of deionized water and 10 to 15 parts by weight of polyvinyl alcohol into a reaction vessel under room temperature; heating the materials to a temperature of 90 DEG C; after the materials are completely dissolved, adding 20 to 25 parts by weight of butyl acetate and 15 to 20 parts by weight of glycerin; leaving the materials to react for 1 hour with preserved temperature; cooling the materials to room temperature; adding 8 to 15 parts by weight of ethanol,15 to 20 parts by weight of polyvinyl acetate, a proper amount of an antiseptic agent and a proper amount of an antifoaming agent; leaving the material to de-foam by standing. The technology of the invention is simple. Once the component proportions, the temperatures, and the reaction times are controlled accurately, the preparation can be successful. During the whole process, no wasting is caused, and no pollution is generated. The production process remains in a clean condition. The produced liquid glue is a single-component liquid glue which is easy to use and is multi-purposed. The liquid glue has strong viscosity and can be widely applied for gluing papers, card boards, fabrics, cork, leather, wood materials, ceramics, colored glaze, cards, plastics, and the like.
Description
technical field [0001] The invention relates to a preparation method of multifunctional liquid glue. Background technique [0002] Liquid glue has good viscosity and can be used to paste paper products. It is a high-quality office and school supplies. [0003] However, the commonly used liquid glue is only used to paste paper, and when other materials need to be pasted, more glues such as 502 glue and Baide glue are used. [0004] 502 glue is a one-component instant curing adhesive synthesized by advanced production technology, mainly based on α-ethyl cyanoacrylate, adding tackifier, stabilizer, toughening agent, polymerization inhibitor, etc. [0005] 502 glue is a kind of strong glue, colorless and transparent, good fluidity, easy to volatilize, and polymerize and solidify when it meets water. And 502 glue is one-component, fast curing, easy to use, strong adhesion, wide range of bonding materials, can be used for steel, non-ferrous metals, rubber, leather, plastics, cer...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.