Asbestos fiber or non-asbestos fiber composite sealing material

A non-asbestos fiber and composite sealing technology, which is applied in other chemical processes, chemical instruments and methods, etc., can solve the problems of poor sealing performance and inability to use comprehensive properties of materials, and achieve improved sealing performance, comprehensive performance improvement, and important performance improvement Effect

Active Publication Date: 2011-10-12
CHINA NAT PULP & PAPER RES INST CO LTD
View PDF10 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015]In order to overcome the shortcomings of poor comprehensive performance of materials, especially poor sealing performance due to the inability to use low particle size fillers in the current papermaking fiber sealing material manufacturing technology, this paper The invention proposes a manufacturing technology of asbestos or non-asbestos fiber composite sealing material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Asbestos fiber or non-asbestos fiber composite sealing material
  • Asbestos fiber or non-asbestos fiber composite sealing material
  • Asbestos fiber or non-asbestos fiber composite sealing material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1: the weight ratio of each component in asbestos or non-asbestos fiber composite sealing material formula is:

[0031]

[0032] The mixed inorganic filler consists of 65% of 1 # Calcium Carbonate, 25% of 2 # calcium carbonate and 10% of 3 # Calcium carbonate graded. The average particle size of each filler used in gradation is shown in Table 1.

[0033] Table 1

[0034] Filling number

1 # calcium carbonate

2 # calcium carbonate

3 # calcium carbonate

Average particle size / micron

3.98

1.64

0.48

[0035] According to the above raw material proportioning, the formula of the invention example 1 and the single filler (sample 2: 100% 1 # Calcium carbonate filler; sample 3: 100% 3 # Calcium carbonate filler) the same formula were carried out papermaking method sheet test. The performance comparison of the three sealing material samples is shown in Table 2.

[0036] Table 2

[0037]

[0038] As ca...

Embodiment 2

[0039] Embodiment 2: the weight ratio of each component in asbestos or non-asbestos fiber composite sealing material formula is:

[0040]

[0041] where the mixed inorganic filler consists of 50% of 1 # Talc powder, 30% of 2 # Talc, 14% of 1 # Kaolin and 6% of 2 # Kaolin graded. The average particle size of each filler used in gradation is shown in Table 3.

[0042] table 3

[0043] serial number

1 # talcum powder

2 # talcum powder

1 # Kaolin

2 # Kaolin

Average particle size / micron

8.01

3.22

1.23

0.31

[0044] According to the above raw material proportioning, the formula of the invention example 2 and the single filler (sample 5: 100% 1 # Talc filler; sample 6: 100% 2 # The same formulation of kaolin filler) was carried out papermaking method sheet test respectively. The performance comparison of the three sealing material samples is shown in Table 4.

[0045] Table 4

[0046]

[0047] As can b...

Embodiment 3

[0048] Embodiment 3: the weight ratio of each component in asbestos or non-asbestos fiber composite sealing material formula is:

[0049]

[0050] The mixed inorganic filler consists of 45% of 1 # Talc, 28% of 2 # Talc, 17% of 1 # Kaolin and 10% of 3 # Calcium carbonate graded. The average particle size of each filler used in gradation is shown in Table 5.

[0051] table 5

[0052] serial number

1 # talcum powder

2 # talcum powder

1 # Kaolin

3 # calcium carbonate

Average particle size / micron

8.01

3.22

1.23

0.48

[0053] According to the above raw material proportioning, the formula of the invention example 3 and the single filler (sample 8: 100% 2 # Talc filler; sample 9: 100%3 # Calcium carbonate filler) the same formula were carried out papermaking method sheet test. The performance comparison of the three sealing material samples is shown in Table 6.

[0054] Table 6

[0055]

[0056] As can ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an asbestos fiber or non-asbestos fiber composite sealing material, in particular to a high-performance paper-making method material. The invention belongs to the crossing field of material science and paper-making technology. The fiber composite sealing material consists of asbestos fiber, non-asbestos fiber, latex, mixed inorganic filler and auxiliary aids, wherein the mixed inorganic filler is prepared by grading at least three and at most six fillers with different average particle sizes; and the average particle size of the higher grade of filler is 2.4 times of that of the adjacent lower grade of filler. As the invention accords with the most compact arrangement theory and the principle of different particle size grain grading is applied in the composition of the filler, the microporous material structure adopting compact arrangement can be obtained by using a little latex, the sealing property of the product and the important indexes such as mechanical strength and heat resistance can be greatly improved and the high-performance fiber composite sealing material can be obtained. By adopting filler grading, the paper machine papermaking performance of slurry can be improved.

Description

technical field [0001] The invention belongs to the intersecting field of material science and papermaking technology, and relates to an asbestos or non-asbestos fiber composite sealing material, in particular to a high-performance papermaking asbestos or non-asbestos fiber composite sealing material. Background technique [0002] Fiber composite sealing materials are mainly used to manufacture various sealing gaskets, and are widely used in the sealing of various vehicles, mechanical equipment and various pipeline joints. plays a key role. There are two types of fiber sealing materials: asbestos fiber products and non-asbestos fiber products. Inexpensive asbestos fibers were once the fiber of choice for sealing materials. However, with the development of science, the carcinogenic effect of asbestos fiber and the harm to human health have been widely recognized by people. Therefore, the use of asbestos has been banned in industrially developed countries. However, in Chin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K3/10C08L21/02C08K13/04C08K7/12C08L9/04C08L9/08
Inventor 庄金风李红羡羽佳文卓
Owner CHINA NAT PULP & PAPER RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com