Formula and preparation method for non-toxic and environment-friendly polyvinyl chloride high-foaming glue for bottle cap

A polyvinyl chloride, non-toxic and environmentally friendly technology, applied in the field of plastic formulation and preparation, can solve the problems of uneven soft and hard foaming density, unsatisfactory sealing effect, insufficient foaming ratio, etc., and achieves low production cost and soft Appropriate hardness and uniform cell density

Inactive Publication Date: 2012-01-11
国家复合改性聚合物材料工程技术研究中心
View PDF1 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, although there have been researches on non-toxic and environmentally friendly high-foaming adhesives, there are problems such as insufficient foaming ratio, or uneven hardness and foaming density, and unsatisfactory sealing effects. Therefore, the development of new non-toxic and e

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formula and preparation method for non-toxic and environment-friendly polyvinyl chloride high-foaming glue for bottle cap

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1 of the present invention: The preparation method of non-toxic and environmentally friendly polyvinyl chloride bottle cap high styrofoam, calculated in parts by weight, pour 65 parts of acetyl tributyl citrate plasticizer into a mixing tank for stirring, and keep stirring Add 0.6 parts of EHM401 microsphere foaming agent, 2.5 parts of calcium zinc stabilizer and 15 parts of heavy calcium carbonate with a particle size of 1250 mesh at a speed of 200-250 rpm, and then keep the stirring speed at 1200-1300 Rpm, keep stirring for 3 minutes; then gradually add 100 parts of polyvinyl chloride paste resin with a degree of polymerization of 1000 while keeping the stirring speed at 200-250 rpm, and keep the stirring speed after the polyvinyl chloride paste resin is added. 1050~1150 revolutions / min, continue stirring until the polyvinyl chloride paste resin is completely infiltrated; finally keep the stirring speed at 1050~1150 revolutions / min, and the stirring temperature ...

Example Embodiment

[0028] Example 2 of the present invention: The preparation method of non-toxic and environmentally friendly polyvinyl chloride bottle cap high styrofoam, calculated in parts by weight, pour 70 parts of acetyl tributyl citrate plasticizer into a mixing tank for stirring, and keep stirring Add 1 part of EHM401 microsphere foaming agent, 2 parts of calcium zinc stabilizer and 30 parts of heavy calcium carbonate with a particle size of 1000 mesh at a speed of 200~250 rpm, and then keep the stirring speed at 1050~1150 rpm / Min, keep stirring for 4 minutes; then gradually add 100 parts of polyvinyl chloride paste resin with a degree of polymerization of 1000 while keeping the stirring speed at 200-250 rpm. After the polyvinyl chloride paste resin is added, keep the stirring speed at 1050~1150 rpm, continue to stir until the polyvinyl chloride paste resin is completely infiltrated; finally keep the stirring speed at 1050~1150 rpm, the stirring temperature is not higher than 42 ℃, conti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a formula and a preparation method for non-toxic and environment-friendly polyvinyl chloride high-foaming glue for bottle caps. In the formula, the foaming glue comprises the following components in part by weight: 90 to 100 parts of polyvinyl chloride resin, 60 to 70 parts of acetyl tributyl citrate, 1.8 to 2.4 parts of foaming agent, 0.6 to 1 part of dimethyl silicon oiland 10 to 30 parts of heavy calcium carbonate. In the formula, by regulating and controlling the plasticizing action of polyvinyl chloride (PVC) sealant strictly, the plasticizing action of the PVC sealant is matched with the decomposition temperature of the foaming agent, so the prepared PVC high foaming glue is high in foaming magnification, uniform in foaming density, appropriate in softness and hardness and good in a sealing effect, and basically reaches the performance of conventional sealing gaskets in which azodicarbonamide is taken as the foaming agent. The high-foaming glue is non-toxic, low in production cost, easy to produce and good in a using effect.

Description

technical field [0001] The invention relates to a plastic formula and a preparation method, in particular to a non-toxic and environment-friendly polyvinyl chloride bottle cap high foaming glue formula and a preparation method. Background technique [0002] At present, food contact materials have an important impact on food safety. Although inferior food contact materials do not cause immediate harm to consumers' bodies like viruses and bacteria, toxic and harmful substances will migrate when these products are used repeatedly for a long time into food, causing chronic poisoning through accumulation through consumption. From the scandal of toxic and carcinogenic polyvinyl chloride (PVC) cling film in 2005, to poisonous baby bottles, disposable foam lunch boxes, and the ban on the sale of more than 10 kinds of chili pepper products in Asia by Zurich and other countries, the safety of food packaging materials Sexual issues are getting more and more attention. [0003] As a p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L83/04C08K3/26C08K5/11C08J9/04
Inventor 徐国敏吉玉碧秦舒浩罗恒谭红胡智杨二钘张敏敏杨鸿波谢锋
Owner 国家复合改性聚合物材料工程技术研究中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap