High-brightness long-afterglow luminescent indicator plate and preparation method thereof

A long afterglow luminous, high-brightness technology, applied to illuminated signs, instruments, display devices, etc., can solve the problems of low luminous intensity and short luminous time, and achieve the effect of simple preparation method and low glare

Inactive Publication Date: 2012-02-15
ANHUI HAISHENG NANO NEW MATERIAL TECH
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still problems of low luminous intensity and short luminous time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-brightness long-afterglow luminescent indicator plate and preparation method thereof
  • High-brightness long-afterglow luminescent indicator plate and preparation method thereof
  • High-brightness long-afterglow luminescent indicator plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention is illustrated by taking straight ahead and right-turn shared lane road traffic signs as an example. Depend on figure 1 and figure 2 It can be seen that the high-brightness and long-lasting luminescent signboard of the present invention includes a substrate 1, a reflective film 2 is provided on the front of the substrate 1, a graphic silk screen layer 3 is provided on the reflective film 2, and sodium distyrene biphenyl disulfonate is arranged on the silk screen layer 3 The fluorescent layer 4, the remaining reflective film 2 and the fluorescent layer 4 are provided with an anti-radiation UV varnish protective layer 5.

[0024] The signboard of the present invention is manufactured according to the shape, size and graphic design required by the relevant national industry standards. The graphic is a word, a picture or a combination thereof. The specific preparation method is:

[0025] a) Preparation of luminous paint: first weigh 2.8kg of crist...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-brightness long-afterglow luminescent indicator plate and a preparation method thereof. The preparation method comprises the following steps: pasting a reflective film on the front face of a substrate; spray-printing a luminous coating on the reflective film so as to form a graphical silkscreen; coating a diphenylethene-biphenyl sodium disulfonate fluorescent layer on the silkscreen; and coating a radiation-proof UV (ultraviolet) gloss oil protective layer on the reflective film which is not covered with graphs as well as the fluorescent layer. The preparation method of the luminous coating comprises the following steps: firstly pouring one third of a cristobalite transparent filler into a mixing tank, adding special light-transmitting resin, PE (polyethylene) resin and dioctyl phthalate (DOP), and then evenly stirring; and sequentially adding pigment, a nano rare-earth luminescent material, glass microspheres and the residual cristobalite transparent filler while stirring, and then evenly stirring for use. For the high-brightness long-afterglow luminescent indicator plate obtained by the preparation method, the brightness can reach 19,800mcd / m<2>, luminescence time can reach 10-14 hours in the case of single light absorption for 30 minutes, the minimum retro-reflection coefficient is cd.1*x<-1>m<-2> for various colors, the observation angle is 0.2 degree, and the incident angle is -4 degree. The high-brightness long-afterglow luminescent indicator plate has the advantages of endless cyclic energy storage, aging resistance, corrosion resistance, flame retardance, no toxicity, no harm, no radiation and energy conservation and is environmentally-friendly.

Description

technical field [0001] The invention relates to an energy-storage luminous signboard, in particular to a high-brightness, long-afterglow luminous signboard, and also relates to a preparation method of the luminous signboard. Background technique [0002] As an important medium in the field of personal and property safety, such as safety, traffic, warning, reminder, fire protection, signage plays an indispensable role in production and life. From the perspective of warning and prompting, signs are usually required to be eye-catching, easy to understand and durable. At present, most of the signs are made with ordinary reflective film technology, and the display effect is average. The display effect is even worse in dark environments such as night and rainy and foggy weather. It needs strong light to distinguish. Due to the rough manufacturing process and poor materials, many signs began to fade, rust, and image peeling off soon after they were put into use. Under the con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G09F13/20G09F13/16
Inventor 胡海生
Owner ANHUI HAISHENG NANO NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com