Water-based viscoelastic damping soundproof sealant

A technology of sound insulation, sealing and viscoelasticity, applied in other chemical processes, chemical instruments and methods, etc., can solve the problems of ineffective sound insulation, poor sound insulation, low bonding strength, etc. Sound insulation effect, damping effect of wide temperature range

Active Publication Date: 2013-10-30
SHANGHAI HOOSUN INTELLIGENT TECH CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these materials will shrink due to drying (curing), thermal expansion and contraction, aging and other reasons will cause cracking, low bond strength and fall off
More importantly, these materials are not professional sound insulation and sealing products, which have poor sound blocking effect and cannot play a good sound insulation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based viscoelastic damping soundproof sealant
  • Water-based viscoelastic damping soundproof sealant
  • Water-based viscoelastic damping soundproof sealant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Weigh each component raw material according to the following composition formula:

[0022]

[0023] The preparation process is as follows: first, add plasticizer, dispersant and flame retardant into the water-based acrylic emulsion, stir to make the mixture uniform, then uniformly add inorganic filler, and stir at high speed for 0.3 to 1.5 hours to obtain the product.

[0024] The water-based viscoelastic damping and sound-insulating sealant is in the form of a paste when it is not dry, and it is in a soft state after being surface-dried at room temperature for 1 hour.

[0025] The temperature range where the damping value of the water-based viscoelastic damping and sound-insulating sealant described in this embodiment is above 0.7 is -15 to 65°C as measured by the US ASTME756-83 vibration damping material testing system.

[0026] The bond strength of the water-based viscoelastic damping and sound-insulating sealant described in this embodiment was measured by a bond...

Embodiment 2

[0028] Weigh each component raw material according to the following composition formula:

[0029]

[0030]

[0031] The preparation process is as follows: First, add plasticizer, dispersant, flame retardant, bactericide, surfactant, and defoamer into the water-based acrylic emulsion, stir to mix evenly, then add inorganic filler evenly, and stir for 0.3 to 1.5 hours. Instantly.

[0032] The water-based viscoelastic damping and sound-insulating sealant is in the form of a paste when it is not dry, and it is in a soft state after being surface-dried at room temperature for 1 hour.

[0033] The temperature range where the damping value of the water-based viscoelastic damping and sound-insulating sealant described in this embodiment is above 0.7 is -17 to 78° C. as measured by the American ASTME756-83 vibration damping material testing system.

[0034] The bond strength of the water-based viscoelastic damping and sound-insulating sealant described in this embodiment was mea...

Embodiment 3

[0036] Weigh each component raw material according to the following composition formula:

[0037]

[0038] The preparation process is the same as described in Example 2.

[0039] The water-based viscoelastic damping and sound-insulating sealant is in the form of a paste when it is not dry, and it is in a soft state after being surface-dried at room temperature for 1 hour.

[0040] The temperature range where the damping value of the water-based viscoelastic damping sound-insulating sealant described in this embodiment is above 0.7 is -7 to 70° C. measured by the US ASTME756-83 vibration damping material testing system.

[0041] The bond strength of the water-based viscoelastic damping and sound-insulating sealant described in this embodiment was measured by a bond strength tester (tensile testing machine) to be 0.75 MPa.

[0042] The use method of the water-based viscoelastic damping and soundproof sealant of the present invention needs to be continuously filled inside the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based viscoelastic damping soundproof sealant which comprises the following components: 100 parts by mass of waterborne acrylic acid emulsion, 10-80 parts by mass of fillers, 2-18 parts by mass of plasticizers, 0.5-15 parts by mass of fire retardants, 0-1.5 parts by mass of bactericides, 0.1-5 parts by mass of dispersants, 0-2 parts by mass of surfactants, 0-3 parts by mass of antifoaming agents; the waterborne acrylic acid emulsion is an interpenetrating network polymer emulsion. The water-based viscoelastic damping soundproof sealant of the invention has the advantages of high damping capacity, wide damping temperature range, high bonding property, no solidification, no contraction, long-lasting viscoelasticity, and the like, can form a damping platform with a damping value of above 0.7 and a temperature range of up to above 75 DEG C, reaches a bonding strength of not less than 0.6 Mpa, can absorb sound vibrational energy which is converted into heat energy and is released, can be used for sealing and joint filling, and has excellent soundproof effect.

Description

technical field [0001] The invention relates to a sealant, in particular to a water-based viscoelastic damping and sound-insulating sealant. Background technique [0002] With the improvement of people's living standards, sound insulation projects have gradually become a job that is highly valued by people, such as residences, cinemas, KTV, bars, recording studios, soundproof rooms, soundproof enclosures, soundproof windows, soundproof doors, etc. However, when people carry out sound insulation treatment, they ignore the importance of gap sound insulation and sealing. [0003] Due to the diffraction phenomenon of sound waves, sound waves of certain frequencies will continue to propagate through the holes, making the sound insulation ability of the sound insulation component worse. Therefore, the gap is the natural enemy of sound insulation management, and it is a good channel for noise transmission. In order to obtain a good sound insulation effect, the gap on the sound ins...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L33/00C08K13/02C08K3/26C08K3/34C08K3/22C08K5/46C08K5/10C09K3/10
Inventor 汪承磊李源林
Owner SHANGHAI HOOSUN INTELLIGENT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com