Putty for wooden furniture

A wooden furniture and atomic ash technology, applied in the direction of filling slurry, etc., can solve the problems of lack of convenient and fast construction, complex atomic ash construction process, and deformation of wooden products, so as to reduce the number of repeated coating and grinding, good construction, and Delicate effect of putty film

Inactive Publication Date: 2012-04-25
杨双明
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the common problem in wood coating is that the wood products are deformed due to the change of the water content of the wood substrate, especially the deformation and shrinkage of the substrate before and after painting of large wooden furniture products, and during the substrate treatment process. damage the decorative coati

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of atomic putty for wooden furniture, the atomic putty is composed of a main agent and a curing agent, wherein the main agent is composed of the following components in parts by weight: 64 parts of unsaturated polyester resin, 12 parts of styrene, triene phosphate 2 parts of propyl ester, 5 parts of bentonite, 3 parts of white corundum, gas phase SiO 2 3 parts, 3 parts of attapulgite, 0.3 part of hydroquinone, 0.2 part of copper naphthenate, 0.4 part of dimethylaniline, 3 parts of titanium dioxide, 2 parts of cobalt naphthenate, wherein the curing agent is in parts by weight The meter consists of the following components: 10 parts of cyclohexanone peroxide, gas phase SiO 2 3 parts, 3 parts of titanium dioxide, 0.5 parts of polyvinylpyrrolidone.

Embodiment 2

[0017] A kind of atomic putty for wooden furniture, the atomic putty is composed of a main agent and a curing agent, wherein the main agent is composed of the following components in parts by weight: 66 parts of unsaturated polyester resin, 8 parts of styrene, triene phosphate 4 parts of propyl ester, 3 parts of bentonite, 5 parts of white corundum, gas phase SiO 2 2 parts, 5 parts of attapulgite, 0.1 part of hydroquinone, 0.4 part of copper naphthenate, 0.2 part of dimethylaniline, 8 parts of titanium dioxide, 1 part of cobalt naphthenate, wherein the curing agent is in parts by weight The meter consists of the following components: 14 parts of cyclohexanone peroxide, gas phase SiO 2 2 parts, 5 parts of titanium dioxide, 0.2 parts of polyvinylpyrrolidone.

Embodiment 3

[0019] A kind of atomic putty for wooden furniture, the atomic putty is composed of a main agent and a curing agent, wherein the main agent is composed of the following components in parts by weight: 64.5 parts of unsaturated polyester resin, 11 parts of styrene, triene phosphate 2.5 parts of propyl ester, 4.5 parts of bentonite, 3.5 parts of white corundum, gas phase SiO 2 2.8 parts, 3.5 parts of attapulgite, 0.25 parts of hydroquinone, 0.25 parts of copper naphthenate, 0.35 parts of dimethylaniline, 4 parts of titanium dioxide, 1.8 parts of cobalt naphthenate, wherein the curing agent is in parts by weight The meter consists of the following components: 11 parts of cyclohexanone peroxide, gas phase SiO 2 2.8 parts, 3.5 parts of titanium dioxide, 0.4 parts of polyvinylpyrrolidone.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a putty for wooden furniture. The putty mainly comprises a main agent and a curing agent, wherein the main agent consists of the following components in part by weight: 64 to 66 parts of unsaturated polyester resin, 8 t o12 parts of styrene, 2 to 4 parts of phosphoric acid triallyl ester, 3 to 5 parts of bentonite, 3 to 5 parts of white corundum, 2 to 3 parts of gas-phase SiO2, 3 to 5 parts of attapulgite, 0.1 to 0.3 part of hydroquinone, 0.2 to 0.4 part of copper naphthenate, 0.2 to 0.4 part of dimethylaniline, 3 to 8 parts of titanium white and 1 to 2 parts of cobalt naphthenate; and the curing agent consists of the following components in part by weight: 10 to 14 parts of cyclohexanone peroxide, 2 to 3 parts of gas-phase SiO2, 3 to 5 parts of titanium white and 0.2 to 0.5 part of polyvinylpyrrolidone.

Description

technical field [0001] The invention relates to the field of chemical coatings, in particular to putty for wooden furniture. Background technique [0002] Atomic ash is a kind of polymerized putty with unsaturated polyester as the main body, and its trade name is atomic ash. It is mainly used for caulking and leveling the surface of metal and non-metal materials before painting, so as to make the substrate smooth and smooth before painting, and to facilitate painting construction. With the continuous development of the domestic furniture coating and decoration industry, the requirements for the surface effect of furniture coating and interior wood decoration and decoration are also getting higher and higher. The appearance quality of products has attracted more and more attention from consumers, and high-quality coating indirectly puts forward higher and higher requirements for the treatment of substrates. Under the increasingly fierce competition among peers and the domes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/34
Inventor 卢齐元
Owner 杨双明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap