Method for preparing anode made of copper-phosphorus alloy

An alloy anode and alloy technology, applied in the direction of electrodes, etc., can solve the problems of uneven structure and unstable plating speed, and achieve the effect of dense structure.

Active Publication Date: 2012-06-27
KONFOONG MATERIALS INTERNATIONAL CO LTD
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the internal structure of the above-mentioned copper-phosphorus alloy anode is not uniform, and delamination occurs. figure 1 A schematic diagram showing the internal structure of the copper-phosphorus alloy anode described above, where the shaded area indicates an uneven area where the plating rate is unstable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing anode made of copper-phosphorus alloy
  • Method for preparing anode made of copper-phosphorus alloy
  • Method for preparing anode made of copper-phosphorus alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The present invention mainly adopts the method of combining multiple times of plastic deformation with a specific deformation rate and annealing treatment at a specific temperature, and strictly controls the deformation rate of plastic deformation, the temperature and time of annealing to realize the production of internal grains that meet the requirements of electroplating Copper-phosphorus alloy anodes that are homogeneous and free from delamination.

[0032] The inventor's dedicated research and repeated practice improvements have obtained the optimal method for making copper-phosphorus alloy anodes, the process flow of which is as follows figure 2 As shown, it mainly includes the following steps:

[0033] Step S11, preheating the ingot, the material of the ingot is copper-phosphorus alloy;

[0034] Step S12, forging the preheated ingot;

[0035] Step S13, performing the first cooling treatment on the forged ingot;

[0036] Step S14, performing homogenization ann...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
heightaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A method for preparing an anode made of a copper-phosphorus alloy comprises the following steps in sequence: preheating an ingot made of the copper-phosphorus alloy; forging the ingot; conducting homogenized annealing treatment on the ingot; conducting cold rolling on the ingot to form a blank; conducting recrystallization annealing treatment on the blank; and machining the blank, so as to form the anode made of the copper-phosphorus alloy. According to the method, the combination of repeated plastic deformation with a specific deformation rate and annealing treatment under specific temperature is mainly adopted, and the deformation rate of the plastic deformation, the temperature during the annealing treatment, and the time of the annealing treatment are controlled, so as to produce the anode meeting the requirements on compact and uniform internal structure and no lamination for electroplating.

Description

technical field [0001] The invention relates to the field of electroplating, in particular to a method for preparing a copper-phosphorus alloy anode for electroplating. Background technique [0002] Electroplating is the process of plating a thin layer of other metals or alloys on some metal surfaces using the principle of electrolysis. It uses the principle of electrolysis to attach a layer of metal film to the surface of metal or other material parts, so as to prevent corrosion, improve wear resistance, conductivity, reflectivity and enhance the appearance. [0003] In the plating tank filled with electroplating solution, the cleaned and specially pretreated parts to be plated are used as the cathode, and the plated metal is used as the anode, and the two poles are respectively connected to the negative and positive poles of the DC power supply. The electroplating solution is composed of an aqueous solution containing metal plating compounds, conductive salts, buffers, pH...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D17/10C22F1/08
Inventor 姚力军相原俊夫大岩一彦潘杰王学泽陈勇军
Owner KONFOONG MATERIALS INTERNATIONAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com