High-ductility electrogas welding self-shielded flux-cored wire

A technology of flux-cored welding wire and electric welding, which is applied in the direction of welding medium, welding equipment, welding/cutting medium/material, etc. It can solve the problems of large heat input, poor welding process performance and poor impact toughness of weld metal

Active Publication Date: 2012-07-11
KUSN GINTUNE WELDING
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the occasion of rapid welding of heavy-duty joints of thick plates, such as: steel structures, box columns, heavy structures, reinforcing plates, etc., due to the high efficiency of vertical and vertical single-pass welding, the easy assembly of the base metal, and easy operation of the equipment, no need Long-term welder training has led to large-scale applications. The supporting welding material is low-alloy steel self-shielding flux-cored wire. Due to the large heat input during welding, the welding process performance and the impact toughness of the weld metal are often poor. meet actual needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-ductility electrogas welding self-shielded flux-cored wire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] The present invention is combined by steel strip and flux, welding core adopts the carbon steel steel strip of low P, S, and wherein steel strip component sees Table 1:

[0041] Table 1: Steel strip composition (based on steel strip, wt%)

[0042] C

Si

mn

Al

0.01-0.055

0.01-0.03

0.10-0.30

0.005~0.060

P

S

Fe

0.007-0.015

0.007-0.015

margin

[0043] The welding flux accounts for 20% to 30% of the total weight of the welding wire, and the welding wire composition is shown in Table 2 (weight percentage):

[0044] Table 2: Welding flux composition (based on the weight in the welding wire, wt%)

[0045] Fluoride

carbonate

Oxide

mn

Si

2.0~6.0

0.2~1.0

1.0~4.0

1.0~4.0

0.2~1.2

Mo

Cr

V

Ni

Fe

0.1~1.0

0.05~0.2

0.05~0.2

0.4~2.0

margin

[0046] In order to underst...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-ductility electrogas welding self-shielded flux-cored wire, which comprises a steel strip and a welding flux wrapped in the steel strip. The weight factor of the welding flux in the overall weight of the wire is 0.2-0.3, and by weight percent, the steel strip comprises 0.01-0.055% of C (carbon), 0.01-0.03% of Si (silicon), 0.10-0.30% of Mn (manganese), 0.005-0.060% of Al (aluminum), 0.007-0.015% of P (phosphorus), 0.007-0.015% of S (sulfur) and the balance Fe (ferrum). By the overall weight of the wire, the wire comprises 2.0-6.0% of fluoride, 1.0-4.0% of oxide, 0.2-1.0% of carbonate, 1.0-4.0% of Mn, 0.2-1.2% of Si, 0.4-2.0% of Ni (nickel), 0.1-1.0% of Mo (molybdenum), 0.05-0.2% of Cr (chromium), 0.05-0.2% of V (vanadium) and the balance Fe. When the wire is used for welding, weld strength is higher than 500MPa, impacting energy at the temperature of -30 DEG C is higher than 50J, and the wire is mainly applicable to occasions of heavy and rapid welding for thick plates.

Description

technical field [0001] The invention belongs to the field of welding materials, and relates to a high-toughness electric welding self-protecting flux-cored welding wire. Background technique [0002] In the case of rapid welding of heavy-duty joints of thick plates, such as: steel structures, box columns, heavy structures, reinforcing plates, etc., due to the high efficiency of vertical and vertical single-pass welding, the easy assembly of the base metal, and easy operation of the equipment, no need Long-term welder training has led to large-scale applications. The supporting welding material is low-alloy steel self-shielding flux-cored wire. Due to the large heat input during welding, the welding process performance and the impact toughness of the weld metal are often poor, so it cannot be used. meet actual needs. Contents of the invention [0003] In order to overcome the above defects, the present invention provides a high toughness electric welding self-shielded flux...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/30B23K35/36
Inventor 蔡鸿祥庄石城
Owner KUSN GINTUNE WELDING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products