Formula of matt glaze

A matte glaze and formula technology, applied in the field of ceramic glaze formula, can solve the problems of insufficient white color, insufficient glaze surface, insufficient high-grade, etc., and achieve the effect of reasonable proportion, delicate glaze and production control.

Inactive Publication Date: 2012-07-11
谢健城
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Alkaline matte glaze is easy to adjust, but the color is not white enough to achieve velvety whiteness, and the texture of the glaze is not good, and it is easy to reveal the color of the body, which is not high-end.
However, the glaze surfa

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0009] Example 1 The matte glaze of the present invention is prepared with the following formula: raw materials in parts by weight: 20 parts of potash feldspar, 8 parts of kaolin, 4 parts of raw talc, 15 parts of dolomite, 1 part of calcite, 30 parts of quartz, barium carbonate 10 parts, 8 parts boric acid.

Example Embodiment

[0010] Example 2 The matte glaze of the present invention is prepared with the following formula: raw materials in parts by weight: 10 parts of potash feldspar, 7 parts of kaolin, 56 parts of raw talc, 17 parts of dolomite, 4 parts of calcite, 40 parts of quartz, barium carbonate 8 parts, 6 parts boric acid.

Example Embodiment

[0011] Example 3 The matte glaze of the present invention is prepared with the following formula: raw materials in parts by weight: 15 parts of potash feldspar, 5 parts of kaolin, 6 parts of raw talc, 20 parts of dolomite, 3 parts of calcite, 50 parts of quartz, and barium carbonate 3 parts, 5 parts boric acid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a formula of matt glaze. According to the formula, the matt glaze comprises the following components in part by weight: 20 to 30 parts of potash feldspar, 3 to 8 parts of kaolin, 3 to 8 parts of raw talc, 15 to 25 parts of dolomite, 1 to 5 parts of calcite, 30 to 50 parts of quartz, 5 to 10 parts of barium carbonate, and 3 to 8 parts of boric acid. The matt glaze is simple in formula and reasonable in proportioning; and the matt glaze which is prepared according to the formula is fine and smooth in glaze surface, good in handfeel, and high in whiteness; and production is easy to control.

Description

technical field [0001] The invention relates to a formula of glaze for ceramics, in particular to a formula of matte glaze. Background technique [0002] Matte glaze is a special glaze between glossy glaze and matte glaze. The matte glaze is different from the transparent glossy glaze, which is a group of tiny crystals embedded in the glass matrix. After the glaze is completely melted, a part of its composition is separated into crystals during the cooling process. The end products are extremely tiny and regularly dispersed. The high-grade matte glaze is pure and elegant, smooth and mercerized, like suet to the touch, like satin or silk, white like velvet, and resistant to dirt. Under the same conditions, its thermal stability and compressive strength are better than ordinary glazed surfaces. After a large area of ​​paving, the color difference is small and the overall effect is good. Under the illumination of the light, it emits flickering light and lives in it. Like a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/86
Inventor 谢健城
Owner 谢健城
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap