Production process for environment friendly laser card paper

A production process and environment-friendly technology, applied in papermaking, paper coatings, textiles and papermaking, etc., can solve problems affecting the clarity of laser graphics, easy deformation of plastic films, and increased material costs, so as to reduce the transfer of laser graphics information process, ease of transfer, and the effect of improving productivity

Active Publication Date: 2012-07-18
GUANGDONG ZHUANGLI COLOR PRINTING
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But even so, it is still necessary to use plastic film as the information transfer medium between the laser molded plate and the cardboard, and there are still the following deficiencies: (1) There are many processes (including molding, vacuum aluminum plating, transfer, and peeling), and the production efficiency is low. Low; (2) equipment investment is large; (3) using plastic film as the information transfer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0036] Example 1

[0037] In this embodiment, the production process of environmentally friendly laser cardboard sequentially includes the following steps:

[0038] (1) Use a corona machine to corona treat the cardboard surface (the side that needs to be coated with laser imaging paint). After corona treatment, the dyne value of the cardboard surface is 40; the cardboard uses gold cardboard;

[0039] (2) Use a coating machine to evenly coat a layer of laser imaging paint on the cardboard, and the laser imaging paint is dried and cured (using hot air drying, the temperature of the 5 drying sections of the drying channel is set to 90℃, After 110°C, 125°C, 110°C, 90°C), a transparent surface coating is formed on the cardboard, the thickness of the transparent surface coating is 2.0μm; then the cardboard with the transparent surface coating is cooled by a cooling roller ( The cooling temperature is 20℃); then the rewinding device rewinds the jammed paper;

[0040] (3) Use a laser mold pl...

Example Embodiment

[0054] Example 2

[0055] In this embodiment, the production process of environmentally friendly laser cardboard sequentially includes the following steps:

[0056] (1) Use a corona machine to corona treat the cardboard surface (the side that needs to be coated with laser imaging paint), and the dyne value of the cardboard surface after corona treatment is 50; the cardboard is silver cardboard;

[0057] (2) Use a coating machine to uniformly coat a layer of laser imaging paint on the cardboard, and the laser imaging paint is dried and cured (using hot air drying, the temperature of the 5 drying sections of the drying channel is set to 95 ℃, After 120°C, 135°C, 120°C, 95°C), a transparent surface coating is formed on the cardboard, the thickness of the transparent surface coating is 4.0μm; then the cardboard with the transparent surface coating is cooled by a cooling roller ( The cooling temperature is 10℃), after cooling, the jammed paper is reeled by the reeling device;

[0058] (3)...

Example Embodiment

[0072] Example 3

[0073] In this embodiment, the production process of environmentally friendly laser cardboard sequentially includes the following steps:

[0074] (1) Use a corona machine to corona treat the surface of the cardboard (the side that needs to be coated with laser imaging paint), and the dyne value of the cardboard surface after corona treatment is 45; the cardboard is white cardboard;

[0075] (2) Use a coating machine to evenly coat a layer of laser imaging paint on the cardboard, and the laser imaging paint is dried and cured (using hot air drying, the temperature of the 5 drying sections of the drying channel is set to 90℃, After 115℃, 130℃, 115℃, 90℃), a transparent surface coating is formed on the cardboard, the thickness of the transparent surface coating is 3.0μm; then the cardboard with the transparent surface coating is cooled by a cooling roller ( The cooling temperature is 15℃), after cooling, the winding device will rewind;

[0076] (3) Use a laser mold pl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a production process for environment friendly laser card paper. The production process comprises the following steps: (1) uniformly coating one layer of laser imaging coating on the card paper by using a coating machine, and drying and solidifying the laser imaging coating to form transparent surface coating on the card paper; and (2) impressing the surface of the transparent surface coating by using a laser mold pressing plate with laser graphic information, and transferring the laser graphic information on the laser mold pressing plate on the transparent surface coating to obtain the laser card paper. Compared with the traditional production process for the laser card paper, the production process for the environment friendly laser card paper has the following beneficial effects that (1) the process is environment friendly; (2) the technological process is optimized, the process steps are simplified and equipment configuration and material consumption are reduced, so cost is saved, and production efficiency is improved; (3) the production is easy to control, so that the laser graphic information is easy to transfer, the anti-fake effect is obvious, quality problem caused by deformation of the base material is avoided, and the product quality is stable; and (4) the laser image text on the laser card paper is clear.

Description

technical field [0001] The invention relates to the technical field of cardboard processing, in particular to an environment-friendly production process of laser cardboard. Background technique [0002] Laser cardboard is a kind of packaging material with laser graphic information. It has anti-counterfeiting effect and strong aesthetic feeling. It is widely used in the outer packaging of tobacco, wine, cosmetics, medicine and other products. [0003] At present, the production process of most laser cardboards is relatively complicated, and must be coated (coating the molded layer on the plastic film), molded (the laser graphics are molded on the molded layer), vacuum aluminum plating (vacuum plated on the molded layer) Aluminum, forming the aluminum layer), transfer (bonding the aluminum layer and the cardboard together), peeling (peeling off the plastic film) and other processes. [0004] There is also a production process of laser cardboard. By improving the plastic film,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H21/40D21H19/52D21H19/60
Inventor 曾丽丽邱赞业陈蓬生陈鹏晋
Owner GUANGDONG ZHUANGLI COLOR PRINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap