Acrylonitrile butadiene styrene (ABS)/ nerchinskite composite material and preparation method thereof

A composite material and halloysite technology, applied in the field of plastic materials, can solve the problems of unfavorable market promotion and application of ABS/PMMA composite materials, high preparation cost and high price of ABS/PMMA composite materials, and achieve good environmental benefits and social benefits. Value, overcoming scratches, easy to operate effect

Inactive Publication Date: 2012-08-01
宁波康德新材料有限公司
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This technical scheme improves the surface hardness, tensile strength and bending performance of the ABS / PMMA composite material by adding PMMA and MBS to the ABS resin, and has higher gloss, but the price of PMMA is very high, which leads to the ABS / PMMA The preparation cost of composite materials is very high, which is not conducive to the market promotion and application of ABS / PMMA composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylonitrile butadiene styrene (ABS)/ nerchinskite composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] 1) Vacuum-dry halloysite (200 mesh, Xingtai Yuanyuan Clay Co., Ltd.) at 80°C for 4 hours, and then dry the halloysite with silane coupling agent KH570 [i.e. γ-(methylpropylene Acyloxy)propyltrimethoxysilane] is premixed in a premixer (200 rpm) according to a weight ratio of 99.5:0.5 to obtain pretreated halloysite;

[0052] 2) Take 6.5 kilograms of ABS (Toray, Japan, T-300, melt index is 10), 2.5 kilograms of pretreated halloysite and maleic anhydride grafted polypropylene (353D, U.S. DuPont, grafting rate 1.0) respectively. ) 1.0 kg is premixed in a premixer (200 revs / min) to obtain a mixed material;

[0053] 3) adding the mixed material into a twin-screw extruder for melt blending, extruding, and granulating to obtain a granular ABS / halloysite composite material. Among them, the temperature of each section of the mixed material in the twin-screw extruder is respectively: the temperature of the feeding section is 210°C, the temperature of the compression section is 22...

Embodiment 2

[0056] 1) Vacuum-dry halloysite (200 mesh, Xingtai Yuanyuan Clay Co., Ltd.) at 80°C for 4 hours, and then dry halloysite with silane coupling agent KH-560 (γ-glycidyl ether Oxytrimethoxysilane) is premixed in a premixer (200 rpm) according to a weight ratio of 99.5:0.5 to obtain pretreated halloysite;

[0057] 2) 6.5 kilograms of ABS (Toray, Japan, T-300, melt index is 10), 3.0 kilograms of pretreated halloysite and maleic anhydride grafted polypropylene (353D, U.S. Dupont, grafting ratio of 1.0) were weighed respectively ) 0.5 kg is premixed in a premixer (200 revs / min) to obtain a mixed material;

[0058] 3) adding the mixed material into a twin-screw extruder for melt blending, extruding, and granulating to obtain a granular ABS / halloysite composite material. Among them, the temperature of each section of the mixed material in the twin-screw extruder is respectively: the temperature of the feeding section is 210°C, the temperature of the compression section is 220°C, the t...

Embodiment 3

[0061] 1) Vacuum-dry halloysite (200 mesh, Xingtai Yuanyuan Clay Co., Ltd.) at 80°C for 4 hours, and then dry the halloysite with silane coupling agent KH570 [i.e. γ-(methylpropylene Acyloxy)propyltrimethoxysilane] is premixed in a premixer (200 rpm) according to a weight ratio of 99.5:0.5 to obtain pretreated halloysite;

[0062] 2) Take respectively 6.5 kilograms of ABS (Toray Japan, T-300, a melt index of 10), 3.2 kilograms of pretreated halloysite and maleic anhydride grafted polypropylene (353D, U.S. DuPont, with a graft ratio of 1.0 ) 0.3 kg is premixed in a premixer (200 revs / min) to obtain a mixed material;

[0063] 3) adding the mixed material into a twin-screw extruder for melt blending, extruding, and granulating to obtain a granular ABS / halloysite composite material. Among them, the temperature of each section of the mixed material in the twin-screw extruder is respectively: the temperature of the feeding section is 210°C, the temperature of the compression sectio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an acrylonitrile butadiene styrene (ABS) / nerchinskite composite material, which is prepared from 49 to 70 weight percent of ABS copolymer, 15 to 35 weight percent of nerchinskite, 3 to 20 weight percent of compatilizer and 0 to 1 weight percent of lubricating agent. The mechanical properties such as hardness and toughness of the composite material are improved by adding the nerchinskite, the compatilizer and the like into the ABS. The invention also discloses a preparation method for the ABS / nerchinskite composite material. The method comprises the following steps of: fully mixing the ABS copolymer, the nerchinskite, the compatilizer and the selectively added lubricating agent uniformly through mixing equipment to obtain a mixed material; and adding the mixed material into a double-screw extruder, performing melt blending, melt extrusion and granulation, and thus obtaining the ABS / nerchinskite composite material. The material has excellent and stable performance, facilitates industrialized production, and has good economic benefits and broad application prospect.

Description

technical field [0001] The invention relates to the field of plastic materials, in particular to an ABS / halloysite composite material and a preparation method thereof. Background technique [0002] With the rapid development of the plastic industry, its use has penetrated into various fields of the national economy and is widely used. China produces about 5 million tons of waste plastic every year. Acrylonitrile-butadiene-styrene terpolymer (ABS), as an important kind of plastic material, has also been widely used, mainly because ABS is a copolymer of acrylonitrile, butadiene and styrene, It has good comprehensive performance, good chemical corrosion resistance and good processing fluidity, as well as high heat resistance, toughness, impact resistance and rigidity. [0003] ABS is mainly used in household appliances, mechanical parts, office supplies, electronic devices, automobile industry and other fields, such as panels for the manufacture of electronic and electrical p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08K3/34C08K9/06C08L51/06C08L23/08
Inventor 康建训朱松波刘建海
Owner 宁波康德新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com