Polyethylene compound used for electrolysis cathode plate sealing strip and preparation method thereof

An electrolytic cathode plate and polyethylene technology, which is applied in the field of metal wet electrolysis, can solve the problems of short life, electrolyte infiltration, and tight insulation and sealing strip clamping, so as to improve storage and service life, reduce catalytic degradation, Enhanced sealing effect

Inactive Publication Date: 2012-08-22
LIAOCHENG UNIV
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the creep characteristics of polymer materials, especially when the temperature of the medium electrolyte is high, creep phenomenon is more likely to occur, so that the insulating sealing strip of the above structure is not clamped tightly, and the sealing strip and the cathode plate have to be clamped. Apply sealant to the junction, which not only increases the cost, but also easily causes the electrolyte to penetrate into the cathode plate of the sealing strip due to the weak adhesion between the sealant and the sealing strip itself, so that the metal is restored to the sealing strip , under the action of mechanical force during peeling, the sealing strip is accelerated and destroyed
[0004] It can be seen that the sealing strip has defects such as poor toughness, poor sealing effect, short life, and easy aging.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene compound used for electrolysis cathode plate sealing strip and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The technical solution of the present invention will be described below in conjunction with the examples.

[0024] The materials used in the invention include: polyethylene resin, linear low-density polyethylene resin, functional polymer, antioxidant, metal deactivator, flow modifier, and appropriate amount of coloring agent.

[0025] The polyethylene resin is a copolymerized high-molecular-weight high-density polyethylene, and the requirements for various performance indicators are: the comonomer is α-olefin, and its density is ≥ 0.940g / cm 3 , Melt flow rate ≤ 1.0g / 10min.

[0026] The linear low density polyethylene resin is a copolymer, the comonomer is α-olefin, and its density is ≤0.926g / cm 3 , Melt flow rate ≤ 2.0g / 10min. The purpose of adding linear low density polyethylene resin is to further improve the toughness of the composition.

[0027] The modified material of the functional polymer ethylene copolymer or polyethylene, the comonomer of the ethylene copol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a compound used for an electrolysis cathode plate sealing strip and a preparation method thereof, belonging to the technical field of plastic processing and application and the technical field of wet electrolysis of metals such as copper. The components used for producing the electrolysis cathode plate sealing strip include 100 parts of polyethylene resin, 0.1-20 parts of linear low density polyethylene, 0.1-10 parts of functional polymer, 0.1-1 part of oxidization inhibitor, 0.05-1 part of metal deactivator, 0.1-5 parts of flow modifier and a proper amount of colorant according to weight parts. The compound has the characteristics of long service life, high adhesion strength with a cathode plate and smooth surface of the molded sealing strip.

Description

technical field [0001] The invention relates to a polyethylene compound material for electrolytic cathode plate sealing strips and a preparation method thereof, which has the characteristics of good bonding performance with the cathode plate and long service life, and belongs to the technical field of plastic processing application and the technical field of wet electrolysis of copper and other metals. Background technique [0002] At present, the industrial production of high-purity copper, manganese, and zinc mainly adopts the method of electrolysis. Among them, an important production part is the cathode plate. Negative charges are introduced through the electrodes, and divalent copper ions, manganese ions, and zinc ions are reduced on the cathode plate to form copper, manganese, and zinc, and then the cathode copper is stripped off by the stripping unit to form High purity metal. The cathode plate is mainly made of stainless steel or titanium. In order to achieve the pu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L51/06C08K13/02C08K5/13C08K5/17C08K5/524C08K5/20C08K5/25B29B9/06B29C47/92B29C48/92
CPCB29C48/0022B29C48/04
Inventor 滕谋勇邓爱霞赵笛葛祥才谢倩
Owner LIAOCHENG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap