Polyimide fiber spinning solution based on 2, 2-double [4-(2, 4-diaminophenoxy) phenyl group] hexafluoropropane and preparation method thereof

A technology of diaminophenoxy, polyimide fiber, applied in the direction of fiber chemical characteristics, single-component synthetic polymer rayon, textiles and papermaking, etc., to achieve the effects of being conducive to industrialization, convenient source and simple operation

Inactive Publication Date: 2012-08-22
DONGHUA UNIV +1
View PDF11 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0023] At present, developed countries such as the United States and Russia are stepping up research on polyimide fibers. Because high-strength and high-modulus polyimide fibers are reinforcing agents for advanced composite materials, they are used in the manufacture of aviation, spacecraft and rockets. There are few, but the research on this fiber in developed countries has never been interrupted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Add 54.8 grams (0.1 moles) of 2,2-bis[4-(2,4-diaminophenoxy)phenyl]hexafluoropropane and 400 milliliters of N-methyl-2-pyrrolidone into the reaction kettle, After stirring and dissolving, add 29.6 grams (0.2 moles) of phthalic anhydride powder, stir and react for 0.5 hours, cool in an ice-water bath to below 5°C, add 10.9 grams (0.05 moles) of pyromellitic dianhydride powder, and stir for 0.5 hour, then, add 16.1 grams (0.05 mole) 3,3 ', 4,4'-tetracarboxybenzophenone dianhydride powder, keep the reaction temperature below 5°C, stir and react for 2 hours to obtain a homogeneous transparent viscous Thick 2,2-bis[4-(2,4-diaminophenoxy)phenyl]hexafluoropropane based polyimide fiber spinning dope.

[0038] Using BROOKFIELD's CAP2000+ laminar viscometer to measure its viscosity at 80°C is 1549mPa.s.

[0039] Take an appropriate amount of the above-mentioned polyimide fiber spinning stock solution, apply it evenly on a clean flat glass sheet, put it into a blast high-temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a polyimide fiber spinning solution based on 2, 2-double [4-(2, 4-diaminophenoxy) phenyl group] hexafluoropropane and a preparation method thereof. The structural formula of components of the spinning solution is shown as below. The preparation method includes adding the 2, 2-double [4-(2, 4-diaminophenoxy) phenyl group] hexafluoropropane and a high-polar aprotic organic solvent into a reaction kettle, stirring for dissolution at the room temperature, adding phthalic anhydride, stirring for reaction for half an hour, cooling until the temperature is under 5 DEG C through an ice-water bath, adding 3, 3', 4, 4'-tetracarboxy benzophenone dianhydride, stirring for reaction for half an hour, adding pyromellitic dianhydride, maintaining the reaction temperature under 5 DEG C, and obtaining the solution after stirring for reaction for 2-4 hours. The polyimide fiber spinning solution based on the 2, 2-double [4-(2, 4-diaminophenoxy) phenyl group] hexafluoropropane and the preparation method thereof have the advantages that molecular weight of resin is easy to control, molecular structure is easy to regulate, preparation of high-performance polyimide fibers is facilitated, reaction condition of the preparation method is mild, and industrialization of products is facilitated.

Description

technical field [0001] The invention belongs to the field of polyimide fiber spinning stock solution and its preparation, in particular to a polyimide based on 2,2-bis[4-(2,4-diaminophenoxy)phenyl]hexafluoropropane Amine fiber spinning dope and its preparation method. Background technique [0002] Polyimide is a kind of polymer material with excellent comprehensive properties. It has particularly excellent heat resistance, low temperature resistance, flame retardancy, electrical properties and mechanical properties. It is widely used in electronic microelectronics, aerospace, High-tech fields such as lasers and optoelectronics. [0003] There have been many reports on the research and development work in the field of polyimide resins: [0004] Chinese invention patent CN101265328A discloses a preparation method of a negative photosensitive polyimide based on 2,2-bis[4-(2,4-diaminophenoxy)phenyl]hexafluoropropane. The preparation method uses 2,2-bis[4-(2,4-diaminophenoxy)p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/78C08G73/10
Inventor 虞鑫海陈梅芳
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products