Method for preparing C5/C9 copolymerized petroleum resin

A technology for copolymerizing petroleum resin and raw materials, which is applied in the field of preparation of C5/C9 copolymerized petroleum resin, and can solve the problem of low comprehensive utilization rate

Active Publication Date: 2012-10-10
HENGHE MATERIALS & SCI TECH CO LTD
View PDF8 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the comprehensive utilization rate of C5 / C9 fraction in my country is very low (less than 10%), and it is mainly used as fuel for cracking furnace to prepare ethylene

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing C5/C9 copolymerized petroleum resin
  • Method for preparing C5/C9 copolymerized petroleum resin
  • Method for preparing C5/C9 copolymerized petroleum resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6

[0081] The following table 9 is the embodiment of preparing C5 / C9 petroleum resin, raw material C is Pd / Al 2 o 3 The processes of catalyst selective hydrogenation, Friedel-Crafts catalyst pretreatment and subsequent catalyst removal, raw material rectification to remove oligomers, solvent dilution, and resin polymerization liquid catalyst removal are as follows:

[0082] (1) Thermal prepolymerization

[0083] Mix the raw materials A, B, and D to obtain the polymerization raw material E, and then transport it to a high-pressure reactor with stirring for thermal prepolymerization to obtain the dimerization product F of carbopentaolefins and styrene or methylstyrene;

[0084] (2) Catalytic polymerization

[0085] The above-mentioned dimerization product F is used as raw material, mixed with a solvent at a mass ratio of 1:0.1~1.0, and a gaseous boron trifluoride catalyst is added to catalyze polymerization to obtain a dark yellow to brown polymerization liquid, which is a mixtur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing C5/C9 copolymerized petroleum resin. The method comprises the following steps of: mixing crude m-pentadiene, crude cyclopentadiene and selectively hydrogenated and pretreated C9 material D uniformly, performing pre-polymerization at the temperature of between 180 and 230 DEG C to obtain a dimmer mixture F of C10 and C15, blending hydro-cracking aviation kerosene serving as a solvent, performing catalytic polymerization for 2 to 5 hours at the temperature of between 30 and 65 DEG C by using gaseous boron trifluoride as a catalyst to obtain deep yellow to brown polymerization solution, rectifying under reduced pressure to remove the solvent and oligomers, and thus obtaining the C5/C9 copolymerized petroleum resin. The prepared C5/C9 resin is good in compatibility and light in color; the preparation method is reasonable and strong in pertinence; the hue, the compatibility and the thermal stability of the resin are remarkably improved; and the resin can be widely applied in the fields of ink, coating, papermaking, plastics and the like.

Description

technical field [0001] The invention belongs to the field of petroleum resin modification, in particular to a preparation method of C5 / C9 copolymerized petroleum resin. Background technique [0002] Petroleum resin is a solid or viscous liquid polymer with relatively low molecular weight, which is obtained by polymerizing the by-product C5 / C9 fraction of the ethylene plant as the main raw material. It has the characteristics of low acid value, good miscibility, low melting point, good adhesion, water resistance and chemical resistance. At present, it has been widely used in road marking paint, ink, rubber processing, adhesives and other fields. According to the monomer and molecular structure of the resin, it can be divided into aromatic petroleum resin, aliphatic petroleum resin and alicyclic petroleum resin. [0003] C9 petroleum resin is a kind of aromatic petroleum resin, which is polymerized from ethylene by-product C9 as a raw material. C5 petroleum resin is an import...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F240/00
Inventor 孙向东王斌彭振博李爱元
Owner HENGHE MATERIALS & SCI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap