Production method of high-performance conductive fiber

A technology for conductive fibers and production methods, applied in fiber processing, conductive/antistatic filament manufacturing, melting of filament raw materials, etc. Health index, low cost, long life effect

Inactive Publication Date: 2012-11-07
绍兴优伯纤维科技有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Resistance wire is a kind of metal material, and its anti-breaking performance must be limited to a certain extent. It is easy to break when it is used on textiles that often need to be folded and kneaded. Hard, even the resistance wire will protrude from the surface of the textile, which not only affects the appearance but also makes it uncomfortable to use
Although the above-mentioned carbon fiber filaments have high strength, they are brittle materials, and they will not be deformed but directly broken when the force is too large, so they are basically irreparable after damage, causing permanent damage, and their functions are relatively single, which cannot achieve ideal practicality. Require

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Preparation of conductive masterbatch: Grinding germanium alloy, nickel alloy and silver alloy into particles with a particle size below 100 nanometers, these particles are then sieved through a fine mesh, and the particles with a particle size below 100 nanometers are reserved for use. The diameter of the particles is re-grinded until all particles are less than 100 nanometers, and then three kinds of particles of germanium, nickel and silver are mixed to make conductive powder. 20%, silver particles 10%, and dry under the conditions of 95 ℃, drying time is 10 hours, put the dried conductive powder into a high-speed mixer, add dispersant 3%, antioxidant 0.08%, the dispersant is polyethylene wax 2000, and the antioxidant is compounded with 1010 and DLTP. The dispersant promotes the change of the surface physical properties of the conductive powder, and improves the adhesion between the conductive powder and the polyamide. The addition of the antioxidant can improve the ...

Embodiment 2

[0024] Preparation of conductive masterbatch: Grinding germanium alloy, nickel alloy and silver alloy into particles with a particle size below 100 nanometers, these particles are then sieved through a fine mesh, and the particles with a particle size below 100 nanometers are reserved for use. The diameter of the particles is re-grinded until all the particles are less than 100 nanometers, and then three kinds of particles of germanium, nickel and silver are mixed to make a conductive powder. 18%, silver particles 17%, and dried under separate drying conditions at 120°C for 8 hours, put the dried conductive powder into a high-speed mixer, add 2% dispersant, antioxidant 0.12%, the dispersant is polyethylene wax 2000, and the antioxidant is compounded with 1010 and DLTP. The dispersant can change the surface physical properties of the conductive powder and improve the adhesion between the conductive powder and polyamide. The addition of antioxidant can improve the polyamide In o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-performance conductive fiber which is prepared from PP resin slice and conductive master batch. The PP resin slice is always positioned in the core layer of the conductive master batch. The content of the conductive master batch in the conductive fiber is 15-35 wt%. The formula of the conductive master batch comprises: by weight, 65-85% of polyamide and 15-35% of a conductive powder. Raw materials of the conductive powder comprise: by weight, 65-85% of germanium particles, 10-20% of nickel particles and 5-15% of silver particles. The conductive powder comprises the following components of: by weight, 2-12% of a coupling agent, 1.5-6% of a dispersant and 0.01-0.25% of an anti-oxidant. A production method of the conductive fiber comprises the following steps of: carrying out cladding and dispersion on the conductive master batch, uniformly dispersing it on the outside surface of the fiber-grade PP resin slice, and spinning to obtain the high-performance conductive fiber. The conductive fiber has excellent softness, spinnability and compliance, is light in volume, has large tensile strength and good conductivity, is widely applied, can be used to manufacture various fabrics for heating, warming and conducting current, and also can be used in antistatic and health-care functional fabrics.

Description

technical field [0001] The invention relates to the technical field of functional fibers, in particular to a production method of high-performance conductive fibers. Background technique [0002] With the rapid development of the textile industry, textiles have also ushered in a new era of rapid changes, so the corresponding conductive fibers for textiles are also coming out, because conductive fibers not only maintain the flexibility of ordinary fibers, but also have the characteristics of electrical conductivity, electric heating, shielding, Functions such as absorbing electromagnetic waves are widely used in textiles, from early antistatic radiation protection, electromagnetic shielding, conductive work clothes to current conductive textiles such as heating and health care clothing. Therefore, the development and application of conductive fibers are getting more and more attention. Looking at the relevant domestic research, the existing conductive textiles are mostly wove...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/06D01F8/12D01F1/09D01D1/04D01D5/34
Inventor 陆建益王礼胜
Owner 绍兴优伯纤维科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products