A composite adhesive and magnesium oxide technology, which is applied in the direction of adhesives, non-polymer organic compound adhesives, etc., to achieve the effects of environmental protection, low cost, and strong adhesion
Inactive Publication Date: 2012-11-14
占协琼
View PDF0 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] At present, there are many types of adhesives on the market, but most of them contain harmful substances, which are easy to volatilize, which is not only not conducive to environmental protection, but also harmful to the health of operators harmful
In addition, the single-performance adhesive not only has poor performance, but also has complicated manufacturing process, high production cost, weak cohesive force, and poor leakage.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] A composite adhesive comprising the following components by weight:
[0019] Magnesium oxide 20 parts
[0021] Rosin 20 parts
[0022] Vinyl Acetate 30 parts
[0023] 10 parts polyvinyl alcohol
[0024] 30 parts of ethanol.
[0025]
Embodiment 2
[0027] A composite adhesive comprising the following components by weight:
[0028] Magnesium oxide 30 parts
[0029] Sodium sulfate 10 parts
[0030] Rosin 30 parts
[0031] Vinyl Acetate 40 parts
[0032] 20 parts polyvinyl alcohol
[0033] 50 parts of ethanol.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a composite adhesive. The adhesive comprises, by weight, 20-30 parts of magnesium oxide, 5-10 parts of sodium sulfate, 20-30 parts of rosin, 30-40 parts of vinyl acetate, 10-20 parts of polyvinyl alcohol and 30-50 parts of ethanol. The composite adhesive has the advantages of being simple in producing method, low in cost, convenient to operate during usage, non-toxic, harmless, high in adhesion, good in permeability and environment-friendly; and raw materials of the adhesive are easy to obtain.
Description
technical field [0001] The invention relates to an adhesive, in particular to a composite adhesive. Background technique [0002] There are many types of adhesives on the market, but most of them contain harmful substances, which are easy to volatilize, which is not only not conducive to environmental protection, but also harmful to the health of operators. In addition, the single-performance adhesive not only has poor performance, but also has complicated manufacturing process, high production cost, weak cohesive force and poor leakage. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a composite adhesive with strong cohesive force, good leakage, simple manufacturing process and low production cost. [0004] In order to solve the problems of the technologies described above, the technical scheme adopted in the present invention is as follows: [0005] A composite adhesive comprising the following components...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/00
Inventor 占协琼
Owner 占协琼