Color glass-reinforced plastic profile material made from novel reclaimed material

A technology of recycled materials and plastic steel, applied in the field of material processing, can solve the problems of environmental impact, white pollution, improper recycling of plastic steel profiles, etc., and achieve the effect of good toughness, smooth surface and saving raw materials

Inactive Publication Date: 2012-11-21
SHUCHENG ANTAI PLASTIC PROD
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, a large number of discarded plastic-steel profiles or improper recycling of unqualified plastic-steel profiles can easily cause white pollution and affect the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Color glass-reinforced plastic profile material made from novel reclaimed material
  • Color glass-reinforced plastic profile material made from novel reclaimed material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The new recycled material colored plastic steel profile is made of the following raw materials in parts by weight: recycled PVC 100, modified nano-calcium carbonate 25, calcium zinc stabilizer 1.5, stearic acid 1.5, dioctyl 0.7, plasticizer 0.5, chlorinated polyvinyl chloride Ethylene 3, ABS high rubber powder 2, polyethylene wax 0.2, paraffin wax 0.6, acrylate impact modifier ACR 2, MBS 3, iron oxide red 2, carbon black 0.02, pigment 0.15. Described plasticizer is epoxy fatty acid methyl ester. The modified nano-calcium carbonate is prepared by the following method: Calcium carbonate is burnt at 600-700°C for 4-5 hours, then ground into nano-powder, and mixed with bis(dioctyloxypyrophosphate) equivalent to 1% of the powder weight base) ethylene titanate, 2% propylene glycol sebacate, stirred evenly, dried, and crushed into powder.

[0026] The manufacturing process of the new colored plastic-steel profiles made of recycled materials includes the following steps:

[0...

Embodiment 2

[0032] The new colored plastic steel profile made of recycled materials is made of the following raw materials in parts by weight: recycled PVC 105, modified nano calcium carbonate 27, calcium zinc stabilizer 1.6, stearic acid 2, dioctyl 0.8, plasticizer 0.8, chlorinated polyvinyl chloride Ethylene 4, ABS high rubber powder 4, polyethylene wax 0.3, paraffin wax 0.7, acrylate impact modifier ACR 3, MBS 4, iron oxide red 3, carbon black 0.03, pigment 0.16. Described plasticizer is n-butyl methacrylate. The modified nano-calcium carbonate is prepared by the following method: Calcium carbonate is burnt at 600-700°C for 4-5 hours, then ground into nano-powder, and mixed with bis(dioctyloxypyrophosphate) equivalent to 1% of the powder weight base) ethylene titanate, 2% propylene glycol sebacate, stirred evenly, dried, and crushed into powder.

[0033] The manufacturing process of the novel recycled material colored plastic-steel profile is the same as in Example 1.

Embodiment 3

[0035] The new recycled material colored plastic-steel profile is made of the following raw materials in parts by weight: recycled PVC 110, modified nano calcium carbonate 28, calcium zinc stabilizer 1.8, stearic acid 2.5, dioctyl 0.8, plasticizer 0.9, chlorinated polyvinyl chloride Ethylene 4, ABS high rubber powder 5, polyethylene wax 0.4, paraffin wax 0.7, acrylate impact modifier ACR 4, MBS 4, iron oxide red 4, carbon black 0.03, pigment 0.18. Described plasticizer is glycerol triglyceride. The modified nano-calcium carbonate is prepared by the following method: Calcium carbonate is burnt at 600-700°C for 4-5 hours, then ground into nano-powder, and mixed with bis(dioctyloxypyrophosphate) equivalent to 1% of the powder weight base) ethylene titanate, 2% propylene glycol sebacate, stirred evenly, dried, and crushed into powder.

[0036] The manufacturing process of the novel recycled material colored plastic-steel profile is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a color glass-reinforced plastic profile material made from a novel reclaimed material. The color glass-reinforced plastic profile material is made from raw materials, such as recycled PVC (polyvinyl chloride), modified nano calcium carbonate, a calcium zinc stabilizer, stearic acid, di-n-octyl phthalate, plasticizer, chlorinated polyethylene, ABS (acrylonitrile-butadiene-styrene) high rubber powder, polyethylene wax, paraffin, acrylate impact modifier ACR, MBS (methyl methacrylate), iron oxide red, carbon black and a pigment. According to the color glass-reinforced plastic profile material, the calcium zinc stabilizer substitutes a lead salt stabilizer, so that the color glass-reinforced plastic profile material is safer and harmless and does not affect the health of human bodies. A waste glass-reinforced plastic profile material or an unqualified glass-reinforced plastic profile material is effectively utilized, so that the reutilization of the glass-reinforced plastic profile material is realized, a large number of raw materials are also saved in a production process, white pollution is reduced, our natural environment is more protected, and the policy requirements of energy conservation and environment friendliness are met. The profile material made from the recycled PVC has all the characteristics of the profile material made from the raw materials as well as the characteristics of smoother surface, better density, better toughness and the like.

Description

technical field [0001] The invention relates to a novel colored plastic-steel profile made of recycled materials, which belongs to the technical field of material processing. Background technique [0002] Plastic steel profiles are referred to as plastic steel, and the main chemical composition is PVC, so they are also called PVC profiles. It is a new type of building material that is widely used. This material has excellent performance, convenient processing and wide application. Due to its physical properties such as rigidity, elasticity, corrosion resistance, and excellent aging resistance, it is usually used as copper, zinc, aluminum, etc. Good substitute for non-ferrous metals. In housing construction, it is mainly used for push-pull, casement doors and windows, guardrails, pipes and ceiling materials. Plastic steel profiles are made of PVC resin as the main raw material, plus a certain proportion of stabilizers, colorants, fillers, ultraviolet absorbers, etc., and ex...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/28C08L55/02C08L23/06C08L91/06C08L51/00C08K13/06C08K9/04C08K3/26C08K5/04C08K5/09C08K5/10C08K3/22C08K3/04B29C47/92B29C48/92
CPCB29B7/46B29B7/72B29B7/7461B29B9/06B29B9/12B29C48/04B29C48/40B29C48/92B29C2948/92704B29C2948/92895B29C2948/92904
Inventor 袁孝菊
Owner SHUCHENG ANTAI PLASTIC PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap