High-strength rubber track for excavating machines and manufacturing method thereof

A rubber crawler, high-strength technology, applied in the field of high-strength rubber crawler for excavators and its manufacturing, can solve the problems of low running noise and large adhesion, and achieve high tear resistance, high tensile strength, and excellent appearance. Effect

Inactive Publication Date: 2012-12-19
QINGDAO TKS SEALING IND
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The rubber track is composed of rubber body, transmission parts, steel cord and canvas (or nylon), etc. It has the characteristics of high adhesion, low operating noise, small vibration, small damage to the soil layer and low ground pressure. It is widely used in combine harvesters, and the normal service life of rubber tracks is about 1000h (hours). However, most of the current rubber tracks have the problem of being difficult to maintain excellent performance and appearance in a relatively harsh environment. For this reason, a The rubber track that can solve the above problems, in order to meet the needs of the actual situation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] A high-strength rubber crawler track for an excavator, the content ratio of each raw material component is as follows in parts by weight:

[0077] 100 parts of 1# natural rubber,

[0078] 3 parts zinc oxide,

[0079] 1.5 parts of stearic acid,

[0080] Anti-aging agent 4010NA 1 part,

[0081] Anti-aging agent RD 1 part,

[0082] Carbon black N330 40 parts,

[0083] 8 parts of white carbon black,

[0084] Si-69 2 parts,

[0085] 3 parts aromatic oil,

[0086] S (sulfur) 2 parts,

[0087] Accelerator Cz 1.2 parts,

[0088] Anti-scorch agent Pvi 0.5 part;

[0089] And it is prepared by the following steps:

[0090] Adjust the roller distance of the double-roll mill to 0.5mm, plasticize the natural rubber, and pack it into a triangle bag ten times; then adjust the roller distance to 1mm, and add zinc oxide, stearic acid, anti-aging agent 4010NA, and anti-aging agent twice RD, carbon black N330, white carbon black, Si-69 and aromatic oil; after mixing the above ra...

Embodiment 2

[0092] A kind of excavator high-strength rubber crawler track, with embodiment 1, difference is, its each raw material component content proportioning is by weight:

[0093] 100 parts of 1# natural rubber,

[0094] Zinc oxide 6 parts,

[0095] 2.5 parts of stearic acid,

[0096] Antiaging agent 4010NA 2 parts,

[0097] Anti-aging agent RD 2 parts,

[0098] Carbon black N330 60 parts,

[0099] 12 parts of white carbon black,

[0100] Si-69 6 parts,

[0101] 6 parts aromatic oil,

[0102] S (sulfur) 2.8 parts,

[0103] Accelerator Cz 1.8 parts,

[0104] Anti-scorch agent Pvi 0.8 parts.

Embodiment 3

[0106] A kind of excavator high-strength rubber crawler track, with embodiment 1, difference is, its each raw material component content proportioning is by weight:

[0107] 100 parts of 1# natural rubber,

[0108] Zinc oxide 4.5 parts,

[0109] 2 parts stearic acid,

[0110] Antiaging agent 4010NA 1.5 parts,

[0111] Anti-aging agent RD 1.5 parts,

[0112] Carbon black N330 50 parts,

[0113] White carbon black 10 parts,

[0114] Si-69 4 parts,

[0115] Aromatic oil 4.5 parts,

[0116] S (sulfur) 2.4 parts,

[0117] Accelerator Cz 1.5 parts,

[0118] Anti-scorch agent Pvi 0.65 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strength at breakaaaaaaaaaa
tensile strength at breakaaaaaaaaaa
tensile strength at breakaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of rubber tracks and preparation thereof, specifically relating to a high-strength rubber track for excavating machines and a manufacturing method thereof. The high-strength rubber track contains the following raw materials by weight part: 100 parts of natural rubber, 3-6 parts of zinc oxide, 1.5-2.5 parts of stearic acid, 1-2 parts of an anti-aging agent 4010 NA, 1-2 parts of an anti-aging agent RD, 40-60 parts of carbon black N330, 8-12 parts of white carbon black, 2-6 parts of Si-69, 3-6 parts of aromatic oil, 2-2.8 parts of S, 1.2-1.8 parts of accelerant Cz 1.2-1.8, and 0.5-0.8 part of scorch retarder Pvi. The high-strength rubber track prolongs service life thereof, and has the advantages of excellent appearance, low hardness, high tear resistance, high tensile strength, excellent ageing resistance and ozone resistance. The high-strength rubber track has lower dynamic heating performance, so the high-strength rubber track can keep excellent performance and appearance under the more bad service environment; the technology is simple; and raw material ratio is reasonable.

Description

technical field [0001] The invention belongs to the technical field of rubber crawler and its preparation, and in particular relates to a high-strength rubber crawler for an excavator and a manufacturing method thereof. Background technique [0002] The rubber track is composed of rubber body, transmission parts, steel cord and canvas (or nylon), etc. It has the characteristics of high adhesion, low operating noise, small vibration, small damage to the soil layer and low ground pressure. It is widely used in combine harvesters, and the normal service life of rubber tracks is about 1000h (hours). However, most of the current rubber tracks have the problem of being difficult to maintain excellent performance and appearance in a relatively harsh environment. For this reason, a The rubber track that can solve the above problems can meet the needs of the actual situation. Contents of the invention [0003] The invention provides a high-strength rubber track for an excavator an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08K13/02C08K3/22C08K5/09C08K3/04C08K3/36C08K3/06B29B7/56
Inventor 刘建强
Owner QINGDAO TKS SEALING IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap