A technology of polyethylene spinning and ultra-high molecular weight, which is applied in the direction of single-component polyolefin rayon, rayon manufacturing, textiles and papermaking, etc. problem, to achieve low cost, high quality, bright and uniform color effect

Active Publication Date: 2013-01-16
宁波大盛新材料有限公司
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] According to the above-mentioned existing technical data, color masterbatches similar to polyethylene are only used in the coloring of polyethylene plastic products and in the fields of polypropylene, polyamide, and polyester PET spinning, and cannot be used for ultra-high molecular weight polyethylene spinning colored fibers. masterbatch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The invention is a method for preparing a special color masterbatch for ultra-high molecular weight polyethylene spinning, which is specifically implemented by the following four steps:

[0023] step 1

[0024] Choose the molecular weight (×10 4 ) 50-1.5 million, particle size is 40-60 mesh polyethylene resin, with 66-84% by weight of high-molecular-weight polyethylene resin as the main body, plus 10-20% organic pigment toner (the color can be adjusted according to the needs of organic Pigment toner), 1-3% antioxidant, 1-5% light stabilizer, 2-6% mineral oil, mixed at room temperature for 20-40 minutes by a mixer to prepare colored resin mixture.

[0025] step 2

[0026] Melt and extrude the colored resin mixture prepared in step 1 with a vented twin-screw extruder to extrude multiple strands of Φ4-5mm; the extruded colored strands are cooled and solidified by a water tank, and then cut off by a pelletizer It is a colored masterbatch with a length of 5mm. The screw ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of special color master batch for ultrahigh-molecular-weight polyethylene spinning. The preparation method is implemented through the following four steps of: 1) selecting high-molecular-weight polyethylene resin as main materials, then adding organic pigment powder, antioxidant, light stabilizer and mineral oil, and mixing by using a mixing machine to prepare colored resin mixture; 2) extruding in a fused state by using an exhaust-type double-screw extruder to obtain a plurality of lines; cooling and solidifying the extruded colored lines through a water trough, and cutting the lines into colored master batch grains by using a grain cutting machine; 3) fully drying the colored master batch grains by using a dryer; and 4) grinding the colored master batch grains into even powder to obtain the special color master batch with uniform grain size for ultrahigh-molecular-weight polyethylene spinning. The preparation method of special color master batch for ultrahigh-molecular-weight polyethylene spinning has the advantages that the demands for various colors needed for ultrahigh-molecular-weight polyethylene spinning are met, the production technology is simple, the cost is low and the preparation method is the best technique for preparing various colored fibers at present.

Description

technical field [0001] The invention relates to a method for preparing raw materials in the textile industry, in particular to a method for preparing a special color masterbatch for ultra-high molecular weight polyethylene spinning. Background technique [0002] Ultra-high molecular weight polyethylene fiber is one of the high-tech fibers in the world today. Its molecular weight is extremely high, reaching more than 2 million (×10 4 ); the fiber has high molecular density, no functional groups, smooth surface, and cannot be dyed, so the ultra-high molecular weight polyethylene fibers produced at home and abroad are all white, and its fibers are limited in special industrial textiles and marine engineering ropes and fishing nets. Wide range of applications in the field, such as the production of colored ultra-high molecular weight polyethylene fibers, must be mixed with high molecular weight polyethylene color masterbatch and ultra-high molecular weight polyethylene resin to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06D01F6/46D01F1/10B29C47/92B29C48/92
CPCB29C48/0022B29C48/04B29C48/40B29C48/92B29C2948/92704B29C2948/92895
Inventor 陈成泗许史安达巍峰王华海颜巧喜陆展飞陈华君
Owner 宁波大盛新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap