Making process of artificial crystal diamond adhesive powder

A technology of man-made crystal and manufacturing process, applied in clothing, applications, jewelry, etc., can solve the problem of not seeing rhinestone rubber powder, etc., and achieve the effect of fast melting speed and low temperature

Active Publication Date: 2014-11-19
潘晓
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no literature about rhinestone rubber powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Making process of artificial crystal diamond adhesive powder
  • Making process of artificial crystal diamond adhesive powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] like figure 1 Shown, artificial crystal diamond adhesive powder manufacturing process, comprises the following steps successively:

[0022] 1) Accurately weigh 3 parts by mass of shellac, 5 parts by mass of rosin, 10 parts by mass of Shuangfei powder or lime powder, and mix them evenly;

[0023] 2) Add the uniformly mixed mixture into the constant temperature stirring tank and raise the temperature to 160°C to melt the mixture;

[0024] 3) Stir at a constant temperature of 160°C and at a low speed of 50 rpm for 1 hour;

[0025] 4) Open the discharge port of the constant temperature stirring tank, let the melted mixture flow into the rubber powder tray; and let the mixture cool in the rubber powder tray to become a flake-like mixture;

[0026] 5) Put the obtained flaky mixture into a ball mill for powdering, and pass cooling water during the powdering process to prevent the rubber powder from heating up, melting and agglomerating during the powdering process; that is, ...

Embodiment 2

[0028] like figure 1 Shown, artificial crystal diamond adhesive powder manufacturing process, comprises the following steps successively:

[0029] 1) Accurately weigh 4 parts by mass of shellac, 4 parts by mass of rosin, and 6 parts by mass of Shuangfei powder, and mix them evenly;

[0030] 2) Add the evenly mixed mixture into the constant temperature stirring tank and raise the temperature to 150°C to melt the mixture;

[0031] 3) Stir at a constant temperature of 150°C and at a low speed of 70 rpm for 2 hours;

[0032] 4) Open the discharge port of the constant temperature stirring tank, let the melted mixture flow into the rubber powder tray; and let the mixture cool in the rubber powder tray to become a flake-like mixture;

[0033] 5) Put the obtained flaky mixture into a ball mill for powdering, and pass cooling water during the powdering process to prevent the rubber powder from heating up, melting and agglomerating during the powdering process; that is, the artificial...

Embodiment 3

[0035] like figure 1 Shown, artificial crystal diamond adhesive powder manufacturing process, comprises the following steps successively:

[0036] 1) Accurately weigh 5 parts by mass of shellac, 3 parts by mass of rosin, 10 parts by mass of Shuangfei powder or lime powder, and mix them evenly;

[0037] 2) Add the uniformly mixed mixture into the constant temperature stirring tank and raise the temperature to 180°C to melt the mixture;

[0038] 3) Stir at a constant temperature of 180°C and at a low speed of 80 rpm for 0.5 hours

[0039] 4) Open the discharge port of the constant temperature stirring tank, let the melted mixture flow into the rubber powder tray; and let the mixture cool in the rubber powder tray to become a flake-like mixture;

[0040] 5) Put the obtained flaky mixture into a ball mill for powdering, and pass cooling water during the powdering process to prevent the rubber powder from heating up, melting and agglomerating during the powdering process; that is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a making process of artificial crystal diamond adhesive powder, which sequentially comprises the following steps of (1) weighting raw materials including 3-5 parts of orange lac, 3-5 parts of rosin and 4-10 parts of heavy calcium carbonate or lime powder, and uniformly mixing the raw materials; (2) increasing the temperature of the mixed materials to 150-200 DEG C to melt the mixed materials; (3) stirring the mixed materials melted in the step (2) at the speed of 40-100r / min and the temperature of 120-160 DEG C for 0.5-4h; (4) enabling the mixed materials to flow into an adhesive powder tray and cooling the mixed materials in the adhesive powder tray to form sheet-like adhesive powder; and (5) grinding or smashing the sheet-like adhesive powder obtained in the step (4) into powder to obtain the artificial crystal diamond adhesive powder. The artificial crystal diamond adhesive powder prepared by the invention has various performances required by mechanical production and is high in melting speed, low in melting temperature and strong in adhesive force after being cooled; and a water drill can not fall off easily.

Description

technical field [0001] The invention belongs to the field of production and processing of artificial crystal diamonds, in particular, the invention relates to a manufacturing process of artificial crystal diamond adhesive powder. Background technique [0002] The traditional method of man-made crystal diamond (rhinestone) processing is to use manual clamping blanks for grinding and polishing. Because of low efficiency and uneven quality, it has been replaced by mechanized processing. The feeding process of the rhinestone blank is to eject the feeding mold from the cylinder—heat the feeding fixture—glue the rubber powder on the fixture—join the feeding mold and take the material. Due to the mechanized production, the melting speed of the rubber powder and the melting temperature of the rubber powder , Adhesion after cooling, hardness after cooling and other properties directly affect the efficiency of mechanized production and the quality of grinding and polishing of rhinesto...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A44C27/00
Inventor 张序虎张甜甜
Owner 潘晓
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com