Macromolecular adhesive cement

A kind of polymer glue and a part of the technology, applied in the field of cement-based self-leveling mortar, can solve the problems that affect the appearance and use effect of buildings, the quality is not easy to be guaranteed, and the problems have not been effectively cured, so as to achieve good construction adaptability and construction quality. Good, the effect of shortening the construction period

Active Publication Date: 2014-12-17
浙江西塘实业有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method of multi-layer construction has low production efficiency and a large waste of materials.
The most important thing is that its quality is not easy to be guaranteed. After construction, the ground often has quality problems such as sanding, peeling, hollowing, and cracking.
Seriously affect the appearance and use effect of the building surface, and become a common quality problem of ordinary cement mortar floors, and have not been effectively cured

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Macromolecular adhesive cement
  • Macromolecular adhesive cement

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The preparation method of the quartz powder sand filler is as follows: using a dry powder mortar mixer, under the condition of cutting off air or inert gas protection, mixing 100-120 mesh quartz sand and quartz powder, adding additives, and fully mixing and stirring.

[0032] Water-based epoxy resin and water-based epoxy curing agent are prepared according to the patent (CN 100532480C A kind of water-based epoxy resin coating and its preparation method).

[0033] The self-leveling additives include retarders, coagulation accelerators, leveling agents, defoamers, and early strength agents.

[0034] The auxiliary additives used in the present invention are all general-purpose additives for coatings.

[0035] The preparation method of described polymer cement is as follows:

[0036] First disperse a part of water, additives and all pigments and fillers at a speed of 900-1200r / min for 8-30 minutes, then reduce the speed, then add a water-based epoxy curing agent, mix a...

Embodiment 1

[0040] The polymer cement of the present invention, in parts by weight: 80 parts of water-based epoxy resin, 16 parts of water-based epoxy curing agent, 120 parts of composite Portland cement, 30 parts of quartz silt filler, 10 parts of water, 35 parts of pigment and filler 0.3 parts of wetting and dispersing agent, 2 parts of self-leveling additive, 2 parts of water-based color paste.

[0041]The silica silt filler is, by weight percentage: 90% a mixture of quartz sand and quartz powder, and 10% additives. The additive is a lubricant.

[0042] The preparation method of the quartz powder sand filler is as follows: using a dry powder mortar mixer, under the condition of cutting off air or inert gas protection, mixing 100-120 mesh quartz sand and quartz powder, adding additives, and fully mixing and stirring.

[0043] Water-based epoxy resin and water-based epoxy curing agent are prepared according to the patent (CN 100532480C A kind of water-based epoxy resin coating and its p...

Embodiment 2

[0048] The polymer cement of the present invention, in parts by weight: 100 parts of water-based epoxy resin, 20 parts of water-based epoxy curing agent, 150 parts of composite Portland cement, 50 parts of quartz silt filler, 15 parts of water, 50 parts of pigment and filler 0.5 parts of wetting and dispersing agent, 6 parts of self-leveling additive, 5 parts of water-based color paste.

[0049] The quartz silt filler is: 80% mixture of quartz sand and quartz powder, 20% lubricant.

[0050] All the other preparations were as in Example 1. The product complies with DB35 / 516-2005.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a cement-based self-leveling mortar, and more particularly relates to a macromolecular adhesive cement. The macromolecular adhesive cement comprises the components in parts by weight: 80-100 parts of water-borne epoxy resin, 16-20 parts of water-borne epoxy curing agent, 120-150 parts of complex portland cement, 30-50 parts of quartz silt powder, 10-15 parts of water, 35-50 parts of pigments and fillers, 0.3-0.5 parts of wetting dispersant, 2-6 parts of self-leveling additives, and 2-5 parts of water-borne color paste. The macromolecular adhesive cement disclosed by the invention is a single-component, dry-powder-shaped and water-borne self-leveling cement-based hard / soft type waterproof adhesion-blocking and leveling material which is processed via scientific proportioning, integrates the functions of water prevention, adhesion, blockage and leveling, as well as is non-toxic and odorless, and belongs to cement-based macromolecular polymer water-borne dry-powder waterproof mortars.

Description

technical field [0001] The invention relates to a cement-based self-leveling mortar, in particular to a polymer cement. Background technique [0002] The traditional ground leveling construction method is to mix the ordinary cement mortar, then use manual paving, scraping, and plastering. Before the final setting of the mortar, it must complete three times of compaction, pulp extraction, and plastering. This multi-layer construction method has low production efficiency and a large material waste. The most important thing is that its quality is not easy to be guaranteed. After construction, the ground often has quality problems such as sanding, peeling, hollowing, and cracking. Seriously affect the look and feel and use effect of the building surface, become a common quality problem of ordinary cement mortar ground, and have not been effectively cured. As an important part of the building, the quality of the ground has attracted more and more attention. [0003] Cement-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine