Preparation method of high-efficiency compound humidity-controlling paperboard

A high-efficiency, cardboard-based technology, which is applied in special paper, paper, papermaking, etc., can solve the problems of the humidity-conditioning material’s humidity capacity and function to be improved, and the humidity capacity is not high, so as to improve the performance of moisture absorption and desorption, and the equipment is simple and easy to use. The effect of industrialization

Inactive Publication Date: 2013-03-13
ZHEJIANG SCI-TECH UNIV
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the low humidity capacity of sepiolite, the humidity capacity and humidity control function of the humidity control material still need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: a kind of preparation method of high-efficiency composite humidity-controlling cardboard is characterized in that the steps are as follows:

[0023] a, get 33 parts of sodium hydroxide by mass parts, add 100 parts of water, stir until dissolving;

[0024] b. Take 30 parts of acrylic acid monomer in parts by mass, add it to the sodium hydroxide solution obtained in step a, and stir it evenly with a strong mixer at 60°C;

[0025] c. Take 10 parts of halloysite with a particle size of 100 mesh according to the number of parts by mass, and roast it at 450° C. for 2 hours to obtain activated halloysite for subsequent use;

[0026] d. Take 0.18 parts of initiator potassium persulfate, 1 part of halloysite after activation, and 1 part of konjac glucomannan in the reactor filled with the solution obtained in step b, and react at 60 ° C by mass parts 5min;

[0027] e. Take 3.3 parts of aluminum chloride according to the number of parts by mass, add it to the abov...

Embodiment 2

[0034] Embodiment 2: a kind of preparation method of high-efficiency composite humidity-controlling cardboard is characterized in that the steps are as follows:

[0035] a, get 33 parts of sodium hydroxide by mass parts, add 110 parts of water, stir until dissolving;

[0036] b. Take 30 parts of acrylic acid monomer in parts by mass, add it to the sodium hydroxide solution obtained in step a, and stir it evenly with a strong mixer at 62.5°C;

[0037] c. Take 10 parts of halloysite with a particle size of 100 mesh according to the number of parts by mass, and roast at 450°C for 2.25 hours to obtain activated halloysite for subsequent use;

[0038] d. Take 0.18 parts by mass of initiator potassium persulfate, 3 parts of activated halloysite, and 1 part of konjac glucomannan into the reactor filled with the solution obtained in step b, and react at 62.5°C 5min;

[0039] e. Take 3.3 parts of aluminum chloride according to the number of parts by mass, add it to the above reactor,...

Embodiment 3

[0046] Embodiment 3: a kind of preparation method of high-efficiency composite humidity-controlling cardboard is characterized in that the steps are as follows:

[0047] a, get 33 parts of sodium hydroxide by mass parts, add 120 parts of water, stir until dissolving;

[0048] b. Take 30 parts of acrylic acid monomer according to the number of parts by mass, add it to the sodium hydroxide solution obtained in step a, and stir it evenly with a strong mixer at 65°C;

[0049] c. Take 10 parts of halloysite with a particle size of 100 mesh according to the number of parts by mass, and roast at 450°C for 2.5 hours to obtain activated halloysite for subsequent use;

[0050] d. Take 0.18 parts by mass of the initiator potassium persulfate, 5 parts of activated halloysite, and 1 part of konjac glucomannan into the reactor filled with the solution obtained in step b, and react at 65 ° C 5min;

[0051] e. Take 3.3 parts of aluminum chloride according to the number of parts by mass, add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of high-efficiency compound humidity-controlling paperboard, comprising the following steps: a-f, preparing humidity-controlling resin per se for later use; g, adding 0.1 part of sodium carboxymethylcellulose into 5 parts by weight of water, stirring till the sodium carboxymethylcellulose is evenly dispersed in the water, and stewing to enable the sodium carboxymethylcellulose and the water to be infiltrated and fused with each other to form into pasty glue solution for later use; h, adding 0.5 part by weight of kieselguhr, 2.5 parts by weight of L-pyrrolidone carboxylic acid-Na, 0.3 part by weight of sodium chloride and 2.7 parts by weight of anhydrous potassium carbonate into 100 parts by weight of water, and stirring to be dissolved; i, taking 4.25 parts by weight of dry paper pulp, adding the paper pulp and the pasty glue solution obtained in step g into mixed solution obtained in step h, and pulping for 2min; j, adding 1.7 parts by weight of the humidity-controlling resin obtained in step f into the mixture obtained in step i, and stirring by a stirrer; and k, papermaking, and drying under the temperate of 80-100 DEG C for 5-7h. The paperboard is very convenient to regenerate and reuse; and the preparation method is simple in production technology and equipment, and easy to industrialize.

Description

technical field [0001] The invention relates to a preparation method of a high-efficiency composite humidity-adjusting paperboard, which is mainly suitable for humidity adjustment of cultural relic preservation environments. Background technique [0002] Humidity regulation methods are mainly divided into active humidity regulation and passive humidity regulation methods. Active humidity control mainly relies on mechanical adjustment, such as dehumidifiers, humidifiers, and constant humidity air conditioners. This method often consumes a lot of energy, occupies a large area, requires personnel maintenance, and directly or indirectly causes air pollution (greenhouses) effect), heat pollution, etc.; passive humidity control materials refer to materials that do not need any artificial energy and mechanical equipment, rely on their own moisture absorption and desorption characteristics to sense the humidity changes in the surrounding environment, and reduce the higher space humi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/00D21H17/66C08L51/02C08K9/00C08K3/34C08K3/16C08F251/00C08F220/06
Inventor 姚清清彭志勤王秉
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com