Nano modified one-component polyurethane waterproofing paint and preparation method thereof

A polyurethane waterproof and nano-modified technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of unstable quality and poor overall performance of polyurethane waterproof coatings, and achieve the effect of improving mechanical properties and improving weather resistance.

Active Publication Date: 2015-07-01
GUANGXI NANNING QISHUN CHEM
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, compared with developed countries, the overall performance of polyurethane waterproof coatings in my country is poor, and the quality is also unstable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 60 parts of trihydroxypolyoxypropylene ether, 60 parts of dihydroxypolyoxypropylene ether; 60 parts of TDI; 10 parts of phosphoric acid; nanometer CaCO 3 10 parts; Nano TiO 2 10 parts; 10 parts of nano-ZnO; 1 part of cetyltrimethylammonium bromide; 2 parts of defoamer; 3 parts of dibutyltin dilaurate.

Embodiment 2

[0019] 70 parts of trihydroxypolyoxypropylene ether, 70 parts of dihydroxypolyoxypropylene ether; 70 parts of TDI; 20 parts of phosphoric acid; nano-CaCO 3 20 parts; Nano TiO 2 20 parts; 20 parts of nano-ZnO; 5 parts of cetyltrimethylammonium bromide; 4 parts of defoamer; 8 parts of dibutyltin dilaurate.

Embodiment 3

[0021] 65 parts of trihydroxypolyoxypropylene ether, 65 parts of dihydroxypolyoxypropylene ether; 60 parts of TDI; 12 parts of phosphoric acid; nano-CaCO 3 14 parts; Nano TiO 2 14 parts; 14 parts of nano-ZnO; 2 parts of cetyltrimethylammonium bromide; 3 parts of defoamer; 5 parts of dibutyltin dilaurate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano modified one-component polyurethane waterproofing paint and a preparation method thereof. The paint comprises the following ingredients in parts by weight: 120-150 parts of polyether polyol, 60-70 parts of TDI (toluene di-isocyanate), 10-20 parts of phosphoric acid, 10-20 parts of nano CaCO3, 10-20 parts of nano TiO2, 10-20 parts of nano ZnO, 1-5 parts of hexadecyl trimethyl ammonium bromide, 2-4 parts of a de-foaming agent, and 3-8 parts of dibutyltin dilaurate. By adding the nano materials to modify the waterproofing paint, the weather resistance and the acid resistance of the waterproofing paint are effectively improved, and meanwhile, the other mechanical properties of the film are also greatly improved correspondingly.

Description

technical field [0001] The invention relates to a waterproof coating, in particular to a nano-material modified one-component polyurethane waterproof coating and a preparation method thereof. Background technique [0002] Building waterproof coatings are mainly made of synthetic polymer materials, asphalt, polymer modified asphalt, inorganic materials, etc., mixed with appropriate amount of additives, modified materials, filler materials, etc. Compared with waterproof coiled materials, waterproof coatings are simple and convenient to construct, suitable for any shape of base surface, and can form a dense and seamless coating film. Therefore, waterproof coatings have been widely used in various waterproof projects and have achieved rapid development. develop. At present, waterproof coatings in industrially developed countries such as the United States, Britain, Japan, France, and Germany all occupy a considerable share in building waterproof materials. While actively develo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/08C09D7/12C09D5/00
Inventor 汪洋
Owner GUANGXI NANNING QISHUN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products