Processing technique of noctilucent glazing floors

A processing technology, the technology of luminous glaze, applied in the field of floor processing, can solve the problems that cannot be practically used in mass production, the crystal structure loses the efficiency of luminescence, and the uneven luminous area, so as to improve the aesthetics and texture, and have a strong three-dimensional effect , good color rendering effect

Active Publication Date: 2013-04-24
如东文园投资开发有限公司
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because ordinary luminous powder has certain radioactivity, it is not suitable for general application in the living environment, so it cannot be used in a large area. At the same time, because the luminous material is coated on the surface of the floor, its crystal structure will be destroyed due to long-term external collision or friction, and its luminous efficiency will be lost.
The actual application effect is poor, the luminous area is uneven, and it is prone to partial or complete non-luminous phenomenon. The surface of the floor will also appear stains due to the oxidation of the luminous powder, which will affect the appearance of the floor.
Due to poor practicability, we have never seen luminous flooring in actual production or life. We can only stay in theory and cannot be used in actual mass production and generally used in the living environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] A luminous glazed floor processing technology, characterized in that: comprising the following steps:

[0062] (1) Making floor slabs;

[0063] (2) Apply a luminous primer to the floor slab prepared in step (1) to obtain a floor slab one;

[0064] (3) Apply elastic primer, wear-resistant primer and hardened primer to floor slab 1 obtained in step (2) to obtain floor slab 2;

[0065] (4) Apply 2-5 coats of glaze paint to the second floor slab prepared in step (3) to obtain a luminous glazed floor.

[0066] After each painting process, drying treatment is required, and sanding treatment is required after part of the drying treatment process. The detailed steps are as follows:

[0067] Floor slab-light primer-luminous primer-infrared drying-sanding-elastic primer-infrared drying-sanding-wear-resistant primer-infrared drying-hardening primer-infrared drying-sanding Light-wear-resistant primer-infrared drying-sanding-infrared drying-sanding-glaze paint-infrared drying-sa...

Embodiment 2

[0075] The difference from the above-mentioned embodiment lies in the ratio of each component, this embodiment uses multi-layer solid wood composite floor slabs.

[0076] The detailed steps are as follows:

[0077] Floor slab-luminous primer-infrared drying-sanding-elastic primer-infrared drying-sanding-wear-resistant primer-infrared drying-hardening primer-infrared drying-sanding-wear-resistant bottom Paint-infrared drying-sanding-infrared drying-sanding-glaze paint-infrared drying-glaze paint-infrared drying-glaze paint.

[0078] The luminous primer contains 30% luminous powder by weight; the thickness of the luminous primer is 200um; the particle size of the luminous powder is 1200 mesh. The anti-settling agent selected in this embodiment is a high-viscosity resin.

[0079] The parts by weight of the glaze paint components are: 13 parts of neoprene rubber, 5 parts of red lead, 2.0 parts of toluene, 2 parts of fumed silica, 1.3 parts of ethyl acetate, 1 part of sulfur, 50 ...

Embodiment 3

[0083] The difference from the above embodiment is that the floor slab in this embodiment is a solid wood antique floor slab, and the step (1) includes making wood texture grooves on the floor slab, and only sanding the wood texture when sanding the primer. The raised part of the grain is primed, and the primer of the groove of the wood grain is retained. The prepared floor glows at night in the groove of the wood grain, highlighting the wood grain of the whole floor in the form of light, which is very beautiful.

[0084] The detailed steps are as follows:

[0085]Floor slab-light primer-luminous primer-infrared drying-sanding-elastic primer-infrared drying-sanding-wear-resistant primer-infrared drying-hardening primer-infrared drying-sanding Light-wear-resistant primer-infrared drying-sanding-infrared drying-sanding-glaze paint-infrared drying-sanding-glaze paint-infrared drying-glaze paint-infrared drying-glaze Lacquer-infrared drying-sanding-glaze finish.

[0086] The lum...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of floor processing, in particular to a processing technique of noctilucent glazing floors. The processing technique is good in decoration and comprises the following steps of (1) processing a floor slab; (2) coating noctilucent primer on the floor slab processed in the step (1) to obtain a first floor slab; (3) coating elastic primer, wear-resisting primer and hardening primer on the first floor slab processed in the step (2) to obtain a second floor slab; and (4) coating glazing paint on the second floor slab processed in the step (3) to obtain the noctilucent glazing floors. The glazing paint is coated outside the noctilucent primer of the processed floors to enable the floors to give out full and soft light at night, simultaneously friction losses or oxidation of the noctilucent primer can be well avoided, weather resistance of the noctilucent primer is strengthened, and lighting service life of the noctilucent primer is prolonged. The glazing paint is applied to the surface of the floors, glossiness, abrasive resistance and fire resistance of the floors are strengthened, flame retardant efficiency of the floors is good, strength is high, and deformation caused by external temperature and humidity is not easy to cause.

Description

technical field [0001] The invention belongs to the field of floor processing, and in particular relates to a process for processing luminous glazed floors with better decorative properties. Background technique [0002] At present, the floors sold on the market are generally decorated with wooden textures on the surface, and the decorative effect is relatively simple. In order to improve the decorativeness of the floors, some existing manufacturers add luminous components to the floor coatings. For example, the application publication number is "CN 102011479 A "Treatment process for coating luminous materials on wooden floors", including groove-and-groove processing on the formed floor; polishing on the end surface of the floor, and sandblasting on the polished end surface; evenly coating the white bottom layer on the end surface of the floor , drying and curing the white bottom layer; sanding the white bottom layer on the end surface of the floor by using a sander or manua...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F15/02E04F15/10B32B33/00B32B37/02C09D111/00C09D7/12C09K11/84
Inventor 姚金根何家忠刘文山杨杰
Owner 如东文园投资开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products