Shrinkable film and method for manufacturing same
A shrink film, degradable film technology, used in chemical instruments and methods, synthetic resin layered products, transportation and packaging, etc., can solve problems such as increased film opacity, aluminum delamination or separation, and reduced productivity, to achieve uniform shrinkage sexual effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0042] Example 1
[0043] 60% of polylactic acid resin was added as a raw material resin, polylactone (DAICELL Chemical Company, Celgreen), and silica having an average particle size of 2.7 μm so as to be 450 ppm in the final film, and then blended to prepare a master batch. The masterbatch was dried at 110°C for 2 hours by using a hot air dryer, melted at 200°C and extruded, and then rapidly cooled and solidified by a cooling roll at 25°C, thereby preparing an unstretched film.
[0044] The water-dispersed polyurethane coating composition is coated on one surface of the unstretched film through an in-line coating (ILC) process, so that the coating thickness after drying is 0.04 μm. The water-dispersed polyurethane coating composition contains 0.8 wt% of polyurethane resin solids (DKC, Superflex210), 0.1 wt% of a silicon-based wetting agent (Dow Corning, Q2-5212) and the balance of water.
[0045] The unstretched film coated with the water-dispersible polyurethane coating compositio...
Example Embodiment
[0047] Example 2
[0048] Except that 45 wt% of polylactone was used to prepare the masterbatch, a film was manufactured in the same manner as in Example 1, and the physical properties of the film are shown in Table 1.
Example Embodiment
[0049] Example 3
[0050] Except that 30 wt% of polylactone was used to prepare the masterbatch, the film was manufactured in the same manner as in Example 1, and the physical properties of the film are shown in Table 1.
PUM
Property | Measurement | Unit |
---|---|---|
Tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap