Rayon three-dimensional lattice shell fabric and production process thereof

A three-dimensional, fabric technology, applied in fabrics, textiles, textiles and papermaking, etc., can solve problems such as unstable product quality

Inactive Publication Date: 2013-06-05
JIANGSU DESHUN TEXTILES
View PDF5 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] As a traditional textile raw material, viscose fiber has mature production technology and product quality, but in the process of blending it with chemical fiber to make new fabrics, due to the huge difference in physical and chemical properties between the two, the product quality is often unstable. , especially when customers demand some unique fabric textures, new technical problems will arise

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rayon three-dimensional lattice shell fabric and production process thereof
  • Rayon three-dimensional lattice shell fabric and production process thereof
  • Rayon three-dimensional lattice shell fabric and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] like figure 1 As shown, the production process of rayon three-dimensional lattice fabric includes the following steps:

[0049] 1. Warp silk processing:

[0050] (1) Warping:

[0051] The warp warping head weight is 1496+1493*8, the creel monofilament tension is 8g, the crimping monofilament tension is 8g, and the total crimping tension is 17-18kg;

[0052] (2) Sizing:

[0053] The warp filaments after warping are uniformly sized by the sizing machine and wound into a sizing shaft, the sizing temperature is set to 40 °C, and the speed of the sizing machine is 300 r / min; It consists of two ovens. The temperature of the first oven is 135°C, and the temperature of the second oven is 140°C. Finally, after the drying cylinder of the pulp car, the drying cylinder consists of five units. The temperature of the cylinder is 125°C, 120℃, 115℃, 110℃, 110℃;

[0054] (3) Parallel axis:

[0055] The warp yarns after the sizing are loaded into the doubling machine and combine...

Embodiment 2

[0068] like figure 1 As shown, the production process of rayon three-dimensional lattice fabric includes the following steps:

[0069] 1. Warp silk processing:

[0070] (1) Warping:

[0071]The warp warping head weight is 1496+1493*8, the monofilament tension on the creel is 10g, the crimping monofilament tension is 11g, and the total crimping tension is 17.5kg;

[0072] (2) Sizing:

[0073] The warp filaments after warping are uniformly sized by the sizing machine and wound into a sizing shaft, the sizing temperature is set to 45 °C, and the speed of the sizing machine is 330 r / min; It consists of two ovens, the temperature of the first oven is 140°C, and the temperature of the second oven is 145°C; finally, after the drying cylinder of the pulp car, the drying cylinder consists of five units, and the temperature of the cylinder is 130°C, 125℃, 120℃, 115℃, 115℃;

[0074] (3) Parallel axis:

[0075] The warp yarns after the sizing are loaded into the paralleling machin...

Embodiment 3

[0088] like figure 1 As shown, the production process of rayon three-dimensional lattice fabric includes the following steps:

[0089] 1. Warp silk processing:

[0090] (1) Warping:

[0091] The warp warping head weight is 1496+1493*8, the creel monofilament tension is 11g, the crimping monofilament tension is 15g, and the total crimping tension is 18kg;

[0092] (2) Sizing:

[0093] The warp filaments after warping are uniformly sized by the sizing machine and wound into a sizing shaft, the sizing temperature is set to 50 °C, and the speed of the sizing machine is 360 r / min; It consists of two ovens, the temperature of the first oven is 145°C, and the temperature of the second oven is 150°C; finally, the drying cylinder is composed of five units through the drying cylinder of the pulp cart, and the temperature of the cylinder is 135°C, 130℃, 125℃, 120℃, 120℃;

[0094] (3) Parallel axis:

[0095] The warp yarns after sizing are loaded into the paralleling machine and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rayon three-dimensional lattice shell fabric and a production process thereof. The shell fabric comprises organzine and tram. The organzine is dacron black silk. The tram comprises first tram and second tram. The first tram is superfine denier fiber and the second tram is lustrous dacron filament. The rayon three-dimensional lattice shell fabric production process comprises organzine processing, tram processing and weaving, wherein organzine process steps comprises beam warping, starching, warp rebeaming and drafting scrabbling reed; and tram process steps comprises spooling, two-for-one twisting and rewinding. The process combines a specific fabric style and a novel type fiber advantage, product property is optimized, and stability of the product quality is improved. Products which are produced by the process are smooth, light in weight, exquisite in handle, good in air permeability, good in drapability and capable of being used as high-grade garment materials.

Description

technical field [0001] The invention relates to the field of textile fabric production, in particular to a rayon three-dimensional lattice fabric and a production process thereof. Background technique [0002] At present, the apparel fabric market is dominated by polyester chemical fiber woven fabrics. Due to the prominent environmental impact of viscose fiber wet spinning, its worldwide output and market have become smaller and smaller. However, due to its extremely low water absorption, polyester chemical fiber cannot simply imitate the smooth feel and cool body touch brought by the high water absorption rate of viscose fiber fabrics. [0003] Viscose fiber has good hygroscopicity, and the fabric woven by viscose fiber is cool and breathable, and has the function of moisture absorption and perspiration. The polyester-viscose composite fabric made of viscose fiber as weft yarn and polyester blended with polyester is a new type of fiber with the hand feeling characteristics...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D03D13/00D03D15/225D03D15/283D03D15/33D03D15/54D03D15/547
Inventor 沈小春吴国良郭建洋李俊王国和吴保虎刘彬宋启雨
Owner JIANGSU DESHUN TEXTILES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More