A kind of high tenacity sound insulation composite material and preparation method thereof

A technology of composite materials and sound insulation materials, applied in the direction of coating, etc., can solve the problems of poor environmental protection and unsatisfactory sound insulation performance, and achieve the effects of convenient coloring, excellent mechanical properties, and good sound insulation performance

Active Publication Date: 2016-01-27
HEFEI GENIUS NEW MATERIALS
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] There are many types of sound insulation materials, such as solid bricks, reinforced concrete walls, wood boards, gypsum boards, iron boards, sound insulation felts, fiberboards, etc., but these sound insulation materials usually have disadvantages such as poor environmental protection or unsatisfactory sound insulation performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high tenacity sound insulation composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 46 parts by weight of polypropylene, 3 parts by weight of ethylene-acrylate-glycidyl methacrylate terpolymer, 0.4 parts by weight of polypropylene wax as a lubricant, 10100.2 parts by weight of antioxidant, and 1680.4 parts by weight of antioxidant in 180 Plasticized and melted at -200°C to obtain a polypropylene resin melt; the continuous polyethylene terephthalate fiber is drawn out from the creel, the tension is adjusted by the tension roller, and the melt is introduced into the impregnated die, and passed through the polypropylene resin. Acrylic resin melt impregnation, realize the dispersion and infiltration of fibers in the die head, control the fiber content to 50 parts by weight through the fiber outlet of the die head, after the organic fibers are completely infiltrated and cooled and solidified, cut into 10mm length by pelletizer The particles were obtained to obtain polyethylene terephthalate fiber toughened polypropylene composites.

[0039] 54.7 parts by we...

Embodiment 2

[0042] 67.4 parts by weight of polypropylene, 2 parts by weight of styrene-ethylene / butylene-styrene block copolymer, 10100.2 parts by weight of antioxidant, and 1680.4 parts by weight of antioxidant are plasticized and melted at a temperature of 180-220 ° C, The polypropylene resin melt is obtained; the continuous polyphenylene sulfide fiber is drawn out from the creel, the tension is adjusted by the tension roller, and the melt is impregnated into the die, and the polypropylene resin melt is impregnated to realize the dispersion of the fiber in the die. Infiltration, through the fiber outlet of the die head, the content of the fiber is controlled to 30 parts by weight. After the organic fiber is completely infiltrated and cooled and solidified, it is cut into particles with a length of 12mm by a pelletizer to obtain a polyphenylene sulfide fiber toughened polypropylene composite material. .

[0043] 59.7 parts by weight of polypropylene resin, 40 parts by weight of talcum po...

Embodiment 3

[0046] 57.2 parts by weight of polypropylene, 2 parts by weight of maleic anhydride grafted polypropylene, 0.2 parts by weight of lubricant calcium stearate, 10980.2 parts by weight of antioxidant, and 1680.4 parts by weight of antioxidant were molded at a temperature of 180-200 ° C. melted to obtain a polypropylene resin melt; the continuous nylon 66 fiber is drawn out from the creel, the tension is adjusted by a tension roller, and the melt is impregnated into the die head, and the polypropylene resin melt is impregnated to realize the dispersion of the fiber in the die head and infiltration, the content of the fiber controlled by the fiber outlet of the die head is 40 parts by weight, after the organic fiber is completely infiltrated and cooled and solidified, it is cut into particles with a length of 11 mm by a pelletizer to obtain a nylon 66 fiber toughened polypropylene composite material.

[0047] 49.7 parts by weight of polypropylene resin, 50 parts by weight of barium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
impact strengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a high toughness sound insulation composite material, which is prepared from the following components, by weight, 30-50 parts of an organic fiber toughened polypropylene composite material, and 50-70 parts of a sound insulation material masterbatch, wherein the organic fiber toughened polypropylene composite material comprises the following components, by weight, 46-67.4 parts of polypropylene, 30-50 parts of organic fibers, 2-3 parts of a compatibilizing agent, and 0.6 part of an antioxidant, and the sound insulation material masterbatch comprises the following components, by weight, 49.7-59.7 parts of polypropylene, 40-50 parts of a sound insulation filling material, and 0.3 part of an antioxidant. The invention further discloses a high toughness sound insulation composite material preparation method. The high toughness sound insulation composite material has characteristics of good sound insulation, excellent mechanical property, convenient processing molding, high product shape design freedom degree, excellent elasticity, chemical corrosion resistance and the like.

Description

technical field [0001] The invention relates to the technical field of polymer composite materials, in particular to a high-toughness sound-insulating composite material and a preparation method thereof. Background technique [0002] At present, noise has become a major environmental pollution, and people pay more and more attention to the problem of acoustic environment. Selecting appropriate materials for sound absorption and sound insulation is one of the most commonly used and basic technical measures in noise control engineering. The difference between material sound absorption and material sound insulation is that material sound absorption focuses on the size of the reflected sound energy on one side of the sound source, and the goal is to reduce the reflected sound energy; material sound insulation focuses on the size of the transmitted sound energy on the other side of the incident sound source, and the goal is The transmitted sound energy is smaller. [0003] Soun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08K13/02C08J5/04C08J3/22B29B15/14B29B9/06
Inventor 肖玲玲孙利明
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap