Steel plate for structure with excellent marine atmospheric corrosion resistance and production method thereof

A marine atmosphere and production method technology, applied in the field of metallurgy, to achieve the effect of excellent corrosion resistance and excellent resistance

Active Publication Date: 2013-07-10
NANJING IRON & STEEL CO LTD
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no structural steel plate that meets the requirements for resisting marine atmospheric corrosion. Therefore, the application prospects of structural steel plates for resisting marine atmospheric corrosion in coastal areas are relatively promising.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The corrosion-resistant steel plate for marine and atmospheric environments in this embodiment includes the following components by weight percentage: C: 0.04%, Si: 0.20%, Mn: 1.30%, P: 0.080%, S: 0.0020%, Ni: 3.20%, Mo: 0.10%, Cu: 0.35%, Nb: 0.060%, Ca: 0.0010%, Alt: 0.021%, N: 0.0045%, and the rest are iron and unavoidable impurities.

[0013] The production method of the corrosion-resistant steel plate for marine and atmospheric environments in this embodiment includes a controlled rolling and controlled cooling process. The production is carried out by using the steel coil rolling mill production line or the medium and heavy plate production line, including the converter or electric furnace smelting process, the refining process outside the furnace, the vacuum treatment process, the continuous casting process, the controlled rolling process and the controlled cooling process; the heating temperature of the continuous casting slab before rolling is 1200 ℃; in the con...

Embodiment 2

[0015] The corrosion-resistant steel plate for marine and atmospheric environments in this embodiment includes the following components by weight percentage: C: 0.06%, Si: 0.25%, Mn: 1.10%, P: 0.010%, S: 0.0060%, Ni: 0.08%, Mo : 0.20%, Cu: 0.15%, Cr: 5.50%, Nb: 0.007%, RE: 0.030%, Ca: 0.0015%, Alt: 0.043%, N: 0.0035%, and the rest are iron and unavoidable impurities;

[0016] The production process of corrosion-resistant steel plates for marine and atmospheric environments in this embodiment is produced using a steel plate production line or a steel plate production line, including a converter or electric furnace smelting process, an out-of-furnace refining process, a vacuum treatment process, a continuous casting process, and a controlled rolling process. Manufacturing process and controlled cooling process; continuous casting slab heating temperature before rolling: 1180°C; in the controlled rolling process, the finishing temperature of rough rolling: 1070°C, and the starting...

Embodiment 3

[0018] The corrosion-resistant steel plate for the marine and atmospheric environment of this embodiment comprises the following components by weight percentage:

[0019] C: 0.08%, Si: 0.40%, Mn: 0.60%, P: 0.030%, S: 0.010%, Ni: 0.75%, Cu: 1.20%, Mo: 0.50%, Cr: 0.55%, Nb: 0.020%, Ti: 0.080%, V: 0.020%, Sb: 0.10%, Ca: 0.0030%, Alt: 0.031%, N: 0.0065%, and the rest are iron and unavoidable impurities;

[0020] The production process of corrosion-resistant steel plates for marine and atmospheric environments in this embodiment is produced using a steel plate production line or a steel plate production line, including a converter or electric furnace smelting process, an out-of-furnace refining process, a vacuum treatment process, a continuous casting process, and a controlled rolling process. Manufacturing process and controlled cooling process; continuous casting slab heating temperature before rolling: 1150°C; in the controlled rolling process, the finishing temperature of rough...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a steel plate for structure with excellent marine atmospheric corrosion resistance and a production method thereof. The steel plate comprises the chemical ingredients by weight percent: 0.001-0.08% of C, 0.10-0.50% of Si, 0.50-1.60% of Mn, 0.080% or less of P, 0.025% or less of S, 0.01-3.50% of Ni, 0.01-0.50% of Mo, 0.01-1.20% of Cu, 0.001-0.060% of Nb, 0.0005-0.0040% of Ca, 0.010-0.080% of Al, 0.0080% or less of N, the balance of Fe and inevitable impurities. A controlled rolling and cooling process is adopted; the heating temperature of a continuous casting billet before rolling is 1100-1250 DEG C; the roughing end temperature is 990-1080 DEG C; the finishing rolling temperature is 850-970 DEG C; laminar cooling is adopted after rolling; the final rolling temperature is 250-750 DEG C; and the cooling speed is 5-40 DEG C / s. The situation that a steel ball has excellent resistance to the marine-atmosphere environment by low carbon and alloy ingredient is ensured.

Description

technical field [0001] The invention belongs to the field of metallurgy and relates to a corrosion-resistant steel for marine and atmospheric environments, in particular to a structural steel plate with excellent resistance to marine and atmospheric corrosion and a production method thereof. Background technique [0002] With the development of my country's socialist construction, the demand for steel in marine and coastal areas will increase. The "National "Twelfth Five-Year" Marine Science and Technology Development Plan" proposes that during the "Twelfth Five-Year Plan" period, the contribution rate of marine science and technology to the marine economy will increase from 54.5% during the "Eleventh Five-Year Plan" period to 60%. The development of technology will inevitably increase the steel used in ocean and coastal areas. In the coastal area, due to the high salt content in the ocean atmosphere, the rust layer of ordinary weathering steel will peel off, and the weathe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/16C22C38/48C22C38/50C22C38/58C22C38/60C21D8/02
Inventor 尹雨群王军赵晋斌
Owner NANJING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com