Core material of vacuum insulation panel and manufacturing method thereof

A technology of a vacuum insulation panel and a manufacturing method, which is applied to fiberboards, heat exchange equipment, and pipelines through thermal insulation protection, etc. Control, reduce thermal conductivity, low cost of raw materials

Active Publication Date: 2015-10-21
CHANGZHOU SANYOU DIOR INSULATION MATERIALS MFG
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most insulation materials have high thermal conductivity, large volume, and the thickness is generally between 1cm-5cm. After being used for home appliance insulation, cold chain logistics, and building insulation, the available space for home appliances and buildings is reduced and the insulation life is short.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Core material of vacuum insulation panel and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0030] The vacuum insulation panel core material of this example, the vacuum insulation panel core material is made of glass fiber chopped strands with a diameter of 6-13um and a length of 4-20mm drawn by wire drawing and a flame with a diameter of 1.0-4.0um and a length of 1-5mm The glass fiber cotton produced by the method is mixed; the glass fiber cotton produced by the flame method accounts for 20wt%, the glass fiber chopped strands produced by the wire drawing method account for 80wt%, and the core material thickness in the finished vacuum insulation panel is 15 ±1mm, the thermal conductivity of the vacuum insulation panel is ≤0.0024W / m.k.

[0031] The above-mentioned manufacturing method of the core material of the vacuum insulation panel, the specific steps of the manufacturing method are as follows:

[0032] (1) Take the glass fiber chopped strands produced by the wire drawing method with a diameter of 6-13um and a length of 4-20mm and the glass fiber wool produced by ...

Embodiment 2

[0043] The core material of the vacuum insulation panel in this example is a mixture of glass fiber chopped strands produced by wire drawing with a diameter of 6-13um and a length of 4-20mm and glass fiber wool produced by a flame method with a diameter of 1.0-4um and a length of 1-5mm Made; the glass fiber cotton produced by the flame method accounts for 10wt%, the glass fiber chopped strands produced by the drawing method accounts for 90wt%, and the core material thickness in the finished product of the vacuum insulation panel is 15 ± 1mm. The thermal conductivity of the insulation board is ≤0.0022W / m.k.

[0044] The manufacturing method of the core material of the vacuum insulation panel of this example includes the following steps:

[0045] (1) Take the glass fiber chopped strands produced by the wire drawing method with a diameter of 6-13um and a length of 4-20mm and the glass fiber wool produced by the flame method with a diameter of 1.0-4um and a length of 1-5mm; The p...

Embodiment 3

[0054] The core material of the vacuum insulation panel in this embodiment is made of glass fiber chopped strands produced by wire drawing with a diameter of 6-13um and a length of 4-20mm and glass fiber wool produced by a flame method with a diameter of 1.0-4um and a length of 1-5mm It is made by mixing; the glass fiber wool produced by the flame method accounts for 15wt%, the glass fiber chopped strands produced by the drawing method accounts for 85wt%, and the thermal conductivity of the finished vacuum insulation panel is ≤0.0021W / m.k.

[0055] The method for manufacturing the core material of the vacuum insulation panel in this embodiment includes the following specific steps:

[0056] (1) Take the glass fiber chopped strands produced by the wire drawing method with a diameter of 6-13um and a length of 4-20mm and the glass fiber wool produced by the flame method with a diameter of 1.0-4um and a length of 1-5mm; The proportion of glass fiber cotton is 15wt%, and the propor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a vacuum insulated panel core material and a manufacturing method thereof. the core material is small in heat conductivity coefficient and low in cost and comprises 70wt% to 100wt% of short chopped glass fiber strands with diameters in a range of 6 microns to 13 microns and lengths in a range of 4 millimeters to 20 millimeters and 0wt% to 30wt% of glass fiber cotton with diameters in a range of 1.0 microns to 4 microns and lengths in a range of 1 millimeters to 5 millimeters, wherein the short chopped glass fiber strands are produced through a strand drawing method, and the glass fiber cotton is produced through a flame method flame method. According to the manufacturing method for core panels, multi-layer liquid adding and multi-layer vacuum dewatering are used, the heat conductivity coefficient of the vacuum insulated panel core material is below 0.03W / m.k, and the heat conductivity coefficient of the vacuum insulated panel is below 0.0025 W / m.k, the heat conductivity coefficient is lower than that of a glass fiber cotton core material 100% produced through the flame method, the insulating effect is good, the manufacture cost of the vacuum insulated panel core material is saved greatly simultaneously, and the quality is stable and controllable.

Description

technical field [0001] The invention relates to a core material of a vacuum insulation panel and a manufacturing method thereof, in particular to a core material of a vacuum insulation panel made of ultrafine glass fiber cotton and chopped glass fiber as raw materials, which is suitable for heat preservation of home appliances and cold chain logistics , Building insulation and other fields. Background technique [0002] At present, the core material of vacuum insulation panels generally chooses porous media, such as powdered silica, aerogel, glass fiber or microporous polyurethane, and each material has its advantages and disadvantages. Secondly, when each core board is used, desiccant or getter must be added to remove the unremoved gas and moisture in the barrier film and the core material to ensure the vacuum degree, thereby improving the service life of the vacuum insulation board. Vacuum insulation panels have been used in various fields. It meets customer requirements ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16L59/02F16L59/065D21J1/00D21H13/40
Inventor 糜玥崎
Owner CHANGZHOU SANYOU DIOR INSULATION MATERIALS MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com