High-temperature resistance methyl phenyl polysiloxane resin powder coating and preparation method thereof

A technology of polysiloxane resin and methyl phenyl, which is applied in the field of high temperature resistant methyl phenyl polysiloxane resin powder coating and its preparation, can solve the problem of adhesion of various dust, dirt and even oil stains, coating machinery Unsatisfactory performance, unsatisfactory anti-sticking ability, etc., to reduce falling and cracking, improve low-temperature deformation resistance, and delay service life

Inactive Publication Date: 2013-10-02
BENGBU HONGAN PRECISION MACHINERY
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the continuous and stable growth of my country's economy and the continuous improvement of people's living standards, the powder coating business of metal components is also increasing, especially in industries such as household appliances, instruments and meters, transportation facilities, aluminum profiles, various vehicles, and daily hardware. , powder coating can provide metal with excellent anti-corrosion protection and decorative properties, but due to the unsatisfactory anti-pollution performance of existing coatings used in the above-mentioned fields, various types of dust, dirt and even oil are often attached to the coating; anti-sticking ability It is not ideal, and the coating formed by the existing powder coating is prone to blistering, cracking, peeling and other phenomena under the influence of natural conditions such as outdoor long-term exposure to the sun and rain. Therefore, the mechanical properties of the coating are not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: High temperature resistant methyl phenyl polysiloxane resin powder coating, the parts by weight (kg) of its constituent raw materials are: high temperature resistant methyl phenyl polysiloxane resin 50, tert-butyl peroxide 0.5, formazan 10 tributylketoxime silane, 1.2 silicone leveling agent, 2.8 polysiloxane, 3.5 triglycidyl isocyanurate, 100 aluminum nitride powder, 6.5 nano brick slag powder, 1-methylpentanol 1.5 and propylene glycol methyl ether acetate 28.

[0013] The preparation method of high temperature resistant methyl phenyl polysiloxane resin powder coating comprises the following steps:

[0014] (1) Preparation of high temperature resistant methylphenylpolysiloxane resin:

[0015] Formula (kg): methylphenylpolysiloxane resin 95, formaldehyde-free glue 20, antioxidant OD 2.0, triglyceride 2.0 and aminopropyltriethoxysilane 4.0;

[0016] The high temperature resistance method is as follows:

[0017] Weigh the methylphenyl polysiloxane resin b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-temperature resistance methyl phenyl polysiloxane resin powder coating and a preparation method thereof. The coating comprises following components, in parts by weight: 47 to 53 parts of methyl phenyl polysiloxane resin, 0.3 to 0.8 part of tert-butyl peroxide, 8 to 12 parts of methyltris(methylethylketoxime)silane, 1.1 to 1.3 parts of organic silicon levelling agent, 2.5 to 3.0 parts of polysiloxanes, 3.3 to 3.8 parts of triglycidyl isocyanurate, 9 to 10 parts of aluminium nitride powder, 5.5 to 7.5 parts of nano brick slag powder, 1.3 to 1.8 parts of 1-methyl amyl alcohol and 2 to 3 parts of propylene glycol methyl ether acetate. The methyl phenyl polysiloxane resin has the advantages of excellent damp-resistance, waterproofness, stainlessness, cold-resistance, ozone-resistance and weatherability. The methyl phenyl polysiloxane resin has a good high-temperature resistance performance, and the heat-resistance temperature arrives at 550 DEG C or more.

Description

technical field [0001] The invention relates to the field of powder coatings, in particular to a high-temperature-resistant methylphenyl polysiloxane resin powder coating and a preparation method thereof. Background technique [0002] With the continuous and stable growth of my country's economy and the continuous improvement of people's living standards, the powder coating business of metal components is also increasing, especially in industries such as household appliances, instruments and meters, transportation facilities, aluminum profiles, various vehicles, and daily hardware. , powder coating can provide metal with excellent anti-corrosion protection and decorative properties, but due to the unsatisfactory anti-pollution performance of existing coatings used in the above-mentioned fields, various types of dust, dirt and even oil are often attached to the coating; anti-sticking ability It is also not ideal, and the coating formed by the existing powder coating is pron...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D183/04C09D5/03C09D7/12
Inventor 张洪滨
Owner BENGBU HONGAN PRECISION MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products