Honeycomb structure polyester modified fiber pure/blended yarns and production technology thereof

A technology of polyester modification and honeycomb structure, which is applied in the direction of yarn, textiles and paper making, can solve the problems affecting the popularization and application of textile products, and achieve the effect of high moisture absorption rate and good combustion resistance

Inactive Publication Date: 2013-11-06
RUGAO CITY DINGYAN TEXTILE
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at present, there is no special process and process conditions for yarns and yarn spinning of fibers with different properties (honeycomb structure polyester modified fiber pure spinning or blended yarn), which affects the use of honeycomb structure polyester modification. Popularization and application of textile products made of natural fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1 : produce 60 S Honeycomb Structure Polyester Modified Fiber Pure Spinning Yarn

[0024] 1. Raw material: honeycomb structure polyester modified fiber: 1.33dtxe×38mm;

[0025] 2. Process flow:

[0026] Raw material processing→blowing→carding→drawing→roving→spinning→winding.

[0027] 3. Specific process:

[0028] Processing of raw materials: raw materials are placed in loose bags for 9 hours in an environment with a relative humidity of 75%;

[0029] Blowing process: short process and combing needle beater are adopted, mainly for soft loosening and carding, the speed of the roll machine beater is controlled at 700r / min, the blowing temperature: 28°C, and the relative humidity: 75%.

[0030] Carding process: Carding licker-in speed 700r / min, 2520 series cylinder card clothing, MCH36 flat card clothing, neps controlled at 1.8 grains / g, 5-point gauge between cylinder and flat: 0.35, 0.32, 0.32, 0.30, 0.32mm.

[0031] Drawing process: a total of two drawing (...

Embodiment 2

[0035] Example 2 , production 38 S Honeycomb structure polyester modified fiber 55%, wool 25%, cashmere 15% blended yarn

[0036] 1. Raw material: honeycomb structure polyester modified fiber: 1.33dtxe×38mm; wool: 66 S Combed noil; cashmere.

[0037] 2. Process route:

[0038] Honeycomb structure polyester modified fiber / wool / cashmere→grabbing cotton→mixing cotton opening→multi-compartment blending→rolling→carding→first sliver→second drawing→roving→spinning→winding.

[0039] 3. Process parameters:

Embodiment 3

[0042] Embodiment 3, Production 60 S Honeycomb structure polyester modified fiber 65% and soft silk fiber 15% spun silk 20% blended yarn

[0043] 1. Raw material: honeycomb structure polyester modified fiber: 1.33dtxe×38mm; soft silk fiber; No. 3 silk strip.

[0044] 2. Process route:

[0045] Honeycomb structure polyester modified fiber / soft silk fiber→Cotton plucking machine→Mixed opener→Multi-compartment blending machine→Roller→Carding machine→Honeycomb structure polyester modified fiber and soft silk fiber blended raw sliver / Silk sliver mixing head draw frame→second draw frame→three draw frame→roving frame→spinning frame→winder.

[0046] 3. Process parameters:

[0047] Honeycomb structure polyester modified fiber and soft silk fiber are mixed in the cotton box, and then honeycomb structure polyester modified fiber and soft silk fiber are blended into raw sliver and silk sliver by three-way mixing process; roving basis weight 3.9g / 10m, twist coefficient 88; Spinning ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

According to the invention, honeycomb structure polyester modified fibers can be obtained through copolymerization of low molecular weight PET (polyethylene terephthalates), monomers containing sulfuric acid groups, amino groups and amide groups, and an antistatic agent. The invention further comprises honeycomb structure polyester modified fiber pure / blended yarns and production technology thereof, wherein the blending weight ratio of honeycomb structure polyester modified fibers and other fibers is (40%-75%) to (25%-35%). The invention has the benefits as follows: the obtained honeycomb structure polyester modified fibers have high moisture absorption rate, high antistatic property, high anti-staining performance, high anti-pilling property and excellent flame resistance; on the premise of thorough comprehension of optimal optimum technology parameters, the honeycomb structure polyester modified fibers can be produced by adopting normal equipment of a cotton spinning mill; the produced honeycomb structure polyester modified fiber pure / blended yarns and back-end fabric products thereof can be used for development of high quality clothes and relevant products; pure spinning and blended spinning are different in style and have different characteristics.

Description

technical field [0001] The patent of the invention relates to the spinning process in textile engineering, specifically a pure spinning and blended yarn of polyester modified fiber with honeycomb structure and its production process. Background technique [0002] Ordinary polyester fiber has poor hygroscopicity, the moisture regain rate is 0.4-0.5% under standard conditions, and the moisture regain rate is 0.6-0.8% when the relative humidity is 100%, so the fiber performance does not change much under dry and wet conditions; Since the fiber has no hydrophilic groups and the molecules are tightly packed, it is difficult for the dye molecules to enter the interior and cannot be dyed by general methods; at the same time, the polyester fiber has high strength and good elastic recovery performance. The above-mentioned performance characteristics lead to poor wearing performance and dyeing performance of ordinary polyester fibers, and they are stiff and airy when used as underwear...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/02D02G3/04
Inventor 陈坚朱张林
Owner RUGAO CITY DINGYAN TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com