Aqueous high weather-proof matt exterior wall emulsion paint and preparation method thereof

A latex paint and exterior wall technology, applied in latex paint, coating, etc., can solve the problems of weather resistance, water resistance, alkali resistance, washing resistance and other performance indicators, reduce gloss, etc., and achieve soft and refreshing paint film texture , strong adhesion, smooth surface of the paint film

Inactive Publication Date: 2013-11-27
ZHEJIANG ZHIQIANG PAINT
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] According to the statistics of relevant departments, the general water-based matt latex paint on the market mainly reduces the gloss by reducing the emulsion content and increasing the amount of powder with high oil absorption. Although the gloss is reduced, the weather resistance, water resistance, alkali resistance, Performance indicators such as washing resistance have also declined

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Made from the following raw materials in parts by weight:

[0052] TX-200 40

[0053] BS-16 0.5

[0054] celite 495 (diatomaceous earth) 2

[0055] CJ-A4 (sericite powder) 7

[0056] R902 (titanium dioxide) 20

[0057] Heavy Calcium Powder 6

[0058] 731A (dispersant) 0.4

[0059] Carbowet 13-40 (wetting agent) 0.3

[0060] DF681F (defoamer) 0.5

[0061] FT-100 (antifreeze) 0.3

[0062] Alcohol ester twelve (coalescent aid) 2

[0063] HBR250 (thickener) 0.4

[0064] RM-2020NPR (leveling agent) 0.2

[0065] BIT 20 LE (preservative) 0.2

[0066] polyphase PW40 (mold inhibitor) 0.2

[0067] water 30

[0068] The preparation steps are as follows:

[0069] 1. Premixing: Add 25 parts of water in the dispersion tank, then add the above dispersant, wetting agent, 0.2 parts by weight of defoamer, film-forming aid, propylene glycol antifreeze and cellulose thickener respectively, fully After mixing evenly, a gel-like substance will be formed to facilitate the disp...

Embodiment 2

[0075] Made from the following raw materials in parts by weight:

[0076] TX-200 31.5

[0077] BS-16 0.2

[0078] celite 495 (diatomaceous earth) 8

[0079] CJ-A4 (sericite powder) 6

[0080] R902 (titanium dioxide) 20

[0081] Heavy Calcium Powder 10

[0082] 731A (dispersant) 0.5

[0083] Carbowet 13-40 (wetting agent) 0.2

[0084] DF681F (defoamer) 0.3

[0085] FT-100 (antifreeze) 0.3

[0086] Alcohol ester twelve (film-forming aid) 1.5

[0087] HBR250 (thickener) 0.7

[0088] RM-2020NPR (leveling agent) 0.5

[0089] BIT 20 LE (preservative) 0.2

[0090] polyphase PW40 (mold inhibitor) 0.2

[0091] water 25

[0092] The preparation steps are as follows:

[0093] 1. Pre-mixing: Add 20 parts of water in the dispersion tank, then add the above dispersant, wetting agent, 0.2 parts by weight of defoamer, film-forming aid, propylene glycol antifreeze and cellulose thickener, fully After mixing evenly, a gel-like substance will be formed to facilitate the dispersio...

Embodiment 3

[0099] Made from the following raw materials in parts by weight:

[0100] TX-200 35

[0101] BS-16 0.3

[0102] celite 495 (diatomaceous earth) 6

[0103] CJ-A4 (sericite powder) 7

[0104] R902 (titanium dioxide) 21

[0105] Heavy Calcium Powder 6

[0106] 731A (dispersant) 0.7

[0107] Carbowet 13-40 (wetting agent) 0.3

[0108] DF681F (defoamer) 0.5

[0109] FT-100 (antifreeze) 0.1

[0110] Alcohol ester twelve (film-forming aid) 1.7

[0111] HBR250 (thickener) 0.6

[0112] RM-2020NPR (leveling agent) 0.4

[0113] BIT 20 LE (preservative) 0.3

[0114] polyphase PW40 (mold inhibitor) 0.1

[0115] water 24

[0116] The preparation steps are as follows:

[0117] 1. Premixing: Add 18 parts of water in the dispersion tank, then add the above dispersant, wetting agent, 0.3 parts by weight of defoamer, film-forming aid, propylene glycol antifreeze and cellulose thickener, fully After mixing evenly, a gel-like substance will be formed to facilitate the dispersion of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aqueous high weather-proof matt exterior wall emulsion paint and a preparation method thereof. The emulsion paint comprises the following components by weight: 30-40 parts of emulsion, 0.2-0.5 part of an organosilicone hydrophobic agent, 2-8 parts of diatomite, 4-7 parts of sericite powder, 20-25 parts of titanium dioxide, 6-14 parts of a calcium carbonate powder, 0.4-0.7 part of a dispersant, 0.1-0.3 part of a wetting agent, 0.3-0.6 part of a defoaming agent, 0.1-0.3 part of an antifreeze, 1.5-2 parts of a coalescing agent, 0.4-0.9 part of a thickening agent, 0.2-0.5 part of a leveling agent, 0.1-0.3 part of a preservative, 0.1-0.3 part of a mildew preventive and 20-30 parts of water. The preparation method provided by the present invention comprises steps of: pre-blending, grinding disperse, and addition of emulsion and auxiliary agent, etc. The aqueous high weather-proof matt exterior wall emulsion paint provided by the invention has advantages of soft texture, flattening and fine paint film surface, and soft matt effect.

Description

technical field [0001] The invention belongs to the field of coatings for exterior wall protection and decoration, in particular to a water-based high weather resistance matt exterior wall latex paint and a preparation method thereof. Background technique [0002] According to the statistics of relevant departments, the general water-based matt latex paint on the market mainly reduces the gloss by reducing the emulsion content and increasing the amount of powder with high oil absorption. Although the gloss is reduced, the weather resistance, water resistance, alkali resistance, Performance indicators such as washing resistance have also declined. [0003] Contents of the invention [0004] In order to solve the above technical problems, the present invention provides a water-based high weather resistance matt exterior wall latex paint and a preparation method thereof. [0005] A water-based high weather resistance matt exterior wall latex paint is characterized in that i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D7/12C09D5/02
Inventor 赖敏志卢益明金辉
Owner ZHEJIANG ZHIQIANG PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com