Formula and preparation method of snow tire

A snow tire and formula technology, applied in special tires, tire parts, transportation and packaging, etc., can solve the problem of low glass transition temperature of rubber, and achieve low glass transition temperature of rubber, good elasticity and good grip. Effect

Active Publication Date: 2013-12-18
KENDA RUBBER CHINA
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the above-mentioned technical problems, the object of the present invention is to provide a snow tire formula and a preparation method thereof. The tread rubber has low hardness, good elasticity, low glass transition temperature of rubber, and can still maintain softness at lower ambient temperatures. High wear resistance, good grip on ice and snow roads, effectively avoid skidding on ice and snow roads, thereby avoiding car accidents and improving driving safety; at the same time, the physical and mechanical properties are basically the same as ordinary tires, retaining the tires in wet and dry conditions. Advantages in terms of grip

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] A preparation method of snow tire formula, described snow tire formula is as above-mentioned a kind of snow tire formula, and its synthetic steps are as follows:

[0034] (1). Put in natural rubber, solution polystyrene butadiene rubber, peptizer A-8, chemical anti-aging agent 6PPD, physical anti-aging agent microcrystalline wax, active agent ZNO, active agent SA, polyethylene glycol PEG, and mix 30-40 seconds, mixing temperature 80-100 ℃, pressure 0.56-0.64Mpa;

[0035] (2). Put in 2 / 3 highly dispersed white carbon black and coupling agent SI69 and mix for 30-40 seconds, the mixing temperature is 90-110°C, and the pressure is 0.56-0.64Mpa;

[0036] (3). Put in another 1 / 3 highly dispersed silica and high wear-resistant carbon black N234 and mix for 40-50 seconds, the mixing temperature is 100-125°C, and the pressure is 0.51-0.59Mpa;

[0037] (4). Put in the operating oil to adjust the mixing conditions, mixing for 150-200 seconds, mixing temperature 120-145 ℃, pressur...

Embodiment 1

[0045] Raw material components: 20 parts of natural rubber, 80 parts of solution-polymerized styrene-butadiene rubber, 40 parts of high wear-resistant carbon black, 30 parts of high-dispersion silica, 8 parts of coupling agent SI69, 1 part of peptizer A-8, 3 1 part of anti-aging agent (2 parts of 6PPD, 1 part of microcrystalline wax), 8 parts of active agent (3 parts of ZNO, 2 parts of SA, 3 parts of PEG), 3 parts of vulcanizing agent S-325, 2 parts of accelerator (1.5 parts of CZ, 0.5 parts of CTP) and 10 parts of process oil.

[0046] The preparation process is carried out in an internal mixer:

[0047] (1). Put in natural rubber, solution polystyrene butadiene rubber, peptizer A-8, chemical anti-aging agent 6PPD, physical anti-aging agent microcrystalline wax, active agent ZNO, active agent SA, polyethylene glycol PEG, and mix 30-40 seconds, mixing temperature 80-100 ℃, pressure 0.56-0.64Mpa;

[0048] (2). Put in 2 / 3 highly dispersed white carbon black and coupling agent ...

Embodiment 2

[0057] Snow tire formula includes the following components, natural rubber 10%, solution polystyrene butadiene rubber 30%, high wear-resistant carbon black N234 20%, high-dispersion white carbon black 16%, peptizer A-8 0.5%, chemical anti-aging Agent 6PPD 1.5%, physical antioxidant microcrystalline wax 1.5%, active agent ZNO 3%, active agent SA 3%, polyethylene glycol PEG 1.5%, vulcanizing agent S-325 3%, accelerator CZ 1.5%, special accelerator Agent CTP 0.5% and coupling agent SI69 8%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tgaaaaaaaaaa
Login to View More

Abstract

The invention discloses a formula of a snow tire. The formula of the snow tire comprises the following components: 5-15% of natural rubber, 20-40% of solution polymerized styrene butadiene rubber, 15-30% of high abrasion proof carbon black N234, 10-20% of high dispersion white carbon black, 0.5-1% of a peptizer A-8, 0.5-1.5% of a chemical antioxidant 6PPD, 0.5-1.5% of a physical antioxidant microcrystalline wax, 1-3% of an active agent ZNO, 1-3% of an active agent SA, 0.5-1.5% of polyethylene glycol (PEG), 1-3% of a vulcanizing agent S-325, 0.5-1.5% of an accelerant CZ, 0.1-0.5% of a special agent CTP and 4-8% of a coupling agent SI69. The technical scheme provided by the invention has the beneficial effects of low hardness and good elasticity of tire surface glue, low vitrification point of rubber, high wear resistance, good road holding performance on ice and snow covered pavement; therefore, the snow tire can effectively avoid skidding on ice and snow covered pavement, and enhance road safety.

Description

technical field [0001] The invention relates to a tire tread formula and a preparation method thereof, in particular to a snow tire formula and a preparation method thereof. Background technique [0002] Ordinary tires come to winter, especially under the conditions of perennial ice and snow weather in the north, as the temperature decreases, the hardness of the tread rubber increases and the elasticity decreases. The stability is greatly reduced, the grip is reduced to the minimum, and it will slip on ice and snow roads, leading to car accidents. Contents of the invention [0003] In order to solve the above-mentioned technical problems, the object of the present invention is to provide a snow tire formula and a preparation method thereof. The tread rubber has low hardness, good elasticity, low glass transition temperature of rubber, and can still maintain softness at lower ambient temperatures. High wear resistance, good grip on ice and snow roads, effectively avoid ski...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/06C08L7/00C08K13/02C08K3/04C08K3/36B29B7/00B29C47/00B60C1/00
Inventor 杨银明王该再叶荣贞
Owner KENDA RUBBER CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com