Tobacco film preparing method for heated non-combustion tobacco products

A technology for heating non-combustion tobacco products, applied in the field of tobacco, which can solve the problems of unsatisfactory smoke release performance and sensory quality of smoke, and achieve the effect of enhancing smoke release performance, good sensory quality, and good flame retardancy

Active Publication Date: 2013-12-25
ZHENGZHOU TOBACCO RES INST OF CNTC
View PDF13 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the reason why heat-not-burn tobacco products have not been widely accepted is mainly because the smoke release pe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0013] Example 1

[0014] Take 1 part of flue-cured tobacco shreds into the extraction container, then add 15 parts of 40% ethanol aqueous solution, soak at 30 ℃ for 48 hours, and filter under reduced pressure to obtain the tobacco extract. After the extract is evaporated to remove ethanol under reduced pressure, it is freeze-dried to obtain a flue-cured tobacco-type solid tobacco extract.

Example Embodiment

[0015] Example 2

[0016] Take 3 parts of flue-cured tobacco, 1 part of burley tobacco and 1 part of oriental tobacco and mix them into the extraction vessel, then add 50 parts of 60% ethanol aqueous solution, soak at 40 ℃ for 24 hours, and filter under reduced pressure to obtain tobacco extract liquid. After evaporating the extract under reduced pressure to remove ethanol, it is spray-dried to obtain a mixed solid tobacco extract.

Example Embodiment

[0017] Example 3

[0018] 100 parts of starch polysaccharide, 30 parts of flue-cured tobacco solid tobacco extract, 15 parts of glycerol, 15 parts of Mg(OH) 2 Add deionized water, fully disperse and dissolve, gelatinize at 80 ℃ for 1 h, then degas under reduced pressure for 20 min to obtain a film-forming liquid. Using the casting method, spread the film-forming liquid on a glass template to form a film, and dry it at 35 ℃ for 48 h before releasing the film. After the prepared film is equilibrated in an environment with a temperature of 22 ℃ and a relative humidity of 60% for 48 hours, a tobacco film suitable for heating non-combustion tobacco products is obtained. The tobacco film has good smoke release performance in the heating and non-combustion state, and the released smoke presents obvious flue-cured tobacco style characteristics, and has good satisfaction and comfort.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A tobacco film preparing method for heated non-combustion tobacco products is characterized by sequentially comprising the following steps of (1) preparing a tobacco extract: performing digestion on tobacco raw materials with an ethanol solution, obtaining a tobacco extracting solution by separating and obtaining a solid tobacco extract by decompressing, evaporating and drying; (2) preparing a tobacco film: proportionally adding a filming material, the solid tobacco extract, polyhydric alcohols, and metal hydroxides into deionized water, performing gelatinization reaction, degassing under a decompressing condition to obtain a filming solution, unfolding the filming solution on a template, and balancing to obtain the tobacco film suitable for the heated non-combustion tobacco products. The tobacco film prepared by the method can effectively release smoke under a heated non-combustion state, and the released smoke has good sense quality, the smoke releasing quality performance of the tobacco raw material under the heated non-combustion state can be enhanced, the smoke concentration is improved and a good flame retarding action is realized due to the addition of the metal hydroxides.

Description

technical field [0001] The invention belongs to the technical field of tobacco, and in particular relates to a method for preparing a tobacco film suitable for heating non-combustion tobacco products. Background technique [0002] Heat-not-burn tobacco products originated in the 1980s and have a history of nearly 30 years since the products were launched. After continuous technological innovation and product promotion, it has become one of the important types of new tobacco products. The smoke produced by this type of product is closer to that of traditional cigarettes, and the sidestream smoke and some harmful components are significantly reduced, making it have a certain market potential. Therefore, related technologies have become a research hotspot for foreign tobacco companies. In recent years, with the continuous increase of tobacco control efforts, foreign tobacco companies have continuously increased research and development efforts on heat-not-burn tobacco products...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A24B3/14
Inventor 曾世通孙世豪李鹏张建勋卢斌斌张启东柴国壁宗永立刘俊辉
Owner ZHENGZHOU TOBACCO RES INST OF CNTC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap