Low-density high-strength ceramsite proppant prepared from flint clay as raw material and preparation method thereof
A technology of high-strength ceramsite and proppant, which is applied to clay products, earth square drilling, and other household appliances. It can solve the problems of low plasticity and difficulty in dispersing, and achieve low breakage rate, low production energy consumption, and simple preparation method. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0038] Example 1
[0039] The chemical composition and mass percentage of scorched gems are as follows:
[0040] Al 2 O 3 :46%, SiO 2 : 51%, Fe 2 O 3 : 1%, TiO 2 : 1%, CaO: 0.4%, MgO: 0.4%, K 2 O: 0.1%, Na 2 O: 0.1% and loss on ignition.
[0041] The preparation method of the low-density and high-strength ceramsite proppant using scorched gemstone as raw material is as follows:
[0042] (1) Carry out the calcination treatment of raw coke gemstone ore at a calcination temperature of 1000°C for 2.5 hours;
[0043] (2) Grind the calcined raw materials to 120 mesh;
[0044] (3) Add water and stir wet-grind the ground raw materials into a slurry to make the solid content of the slurry 70%. Take samples every 10 minutes to check the particle size with a laser particle size analyzer. The particle size reaches 800 mesh;
[0045] (4) Spray-dry the mud up to the particle size with a spray drying tower to a moisture content of less than 6%;
[0046] (5) Add the spray-dried powder to 24% water of the ...
Example Embodiment
[0049] Example 2
[0050] The chemical composition and mass percentage of scorched gems are as follows:
[0051] Al 2 O 3 : 43%, SiO 2 : 52%, Fe 2 O 3 :1.5%, TiO 2 : 2.5%, CaO: 0.2%, MgO: 0.5%, K 2 O: 0.2%, Na 2 O: 0.1% and loss on ignition.
[0052] The preparation method of the low-density and high-strength ceramsite proppant using scorched gemstone as raw material is as follows:
[0053] (1) The raw coke gemstone ore is calcined, the calcining temperature is 1200℃, and the calcining is 3 hours;
[0054] (2) Grind the calcined raw materials to 300 mesh;
[0055] (3) Add water to the ground raw materials and wet-grind them into a slurry with agitation. The solid content of the slurry is 68%. The particle size is measured with a laser particle size analyzer every 10 minutes, and the particle size reaches 500 meshes;
[0056] (4) Spray-dry the mud up to the particle size with a spray drying tower to a moisture content of less than 6%;
[0057] (5) Add the spray-dried powder to 20% water of ...
Example Embodiment
[0060] Example 3
[0061] The chemical composition and mass percentage of scorched gems are as follows:
[0062] Al 2 O 3 :41%, SiO 2 : 54%, Fe 2 O 3 : 2.5%, TiO 2 : 1.5%, CaO: 0.2%, MgO: 0.3%, K 2 O: 0.3%, Na 2 O: 0.2% and loss on ignition.
[0063] The preparation method of the low-density and high-strength ceramsite proppant using scorched gemstone as raw material is as follows:
[0064] (1) The raw coke gemstone ore is calcined at 800°C for 4 hours;
[0065] (2) Grind the calcined raw materials to 200 mesh;
[0066] (3) Add water to the ground raw materials and grind them into a slurry according to the solid content of 69% by stirring and grinding. The particle size is measured with a laser particle size analyzer every 10 minutes, and the particle size reaches 1500 mesh;
[0067] (4) Spray-dry the mud up to the particle size with a spray drying tower to a moisture content of less than 6%;
[0068] (5) Add the spray-dried powder to 15% water of the granulated powder mass, and use a gran...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap