Copper phosphorus brazing alloy with hafnium zirconium cobalt

A technology of copper-phosphorus solder and zirconium-cobalt, which is applied in the direction of welding/cutting media/materials, welding media, metal processing equipment, etc., to achieve good fluidity, low melting temperature range, and reduce technical difficulty

Active Publication Date: 2014-01-01
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is not limited to the novel copper-phosphorus brazing filler metals disclosed in these documents. "Instructions"), more specifically, do not belong to "copper-phosphorus solder with P element content

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A new type of copper-phosphorus solder containing hafnium, zirconium and cobalt, the composition of which is: P8.0%, Sn4.5%, Co0.05%, Hf0.2%, Zr0.2%, and the balance is Cu .

[0030] The solidus temperature of the "new copper-phosphorus solder containing hafnium, zirconium and cobalt" obtained from the above composition ratio is 585°C ± 10°C, and the liquidus temperature is 645°C ± 10°C (all considering the measurement error). Use the flame brazing method, cooperate with FB102 flux, and see the data in the brackets for the brazing joint strength when the brazing base material is the following combination: red copper-H62 brass (σ b =215±25MPa, τ=205±30MPa), red copper-HPb62-3 lead brass (σ b =220±25MPa, τ=210±30MPa), red copper-HPb59-3 lead brass (σ b =220±25MPa, τ=210±30MPa).

Embodiment 2

[0032] A new type of copper-phosphorus solder containing hafnium, zirconium and cobalt, the composition of which is: P5.0%, Sn10.0%, Co0.35%, Hf0.01%, Zr0.01%, and the balance is Cu .

[0033] The solidus temperature of the "new copper-phosphorus solder containing hafnium, zirconium and cobalt" obtained from the above composition ratio is 585°C ± 10°C, and the liquidus temperature is 645°C ± 10°C (both taking into account the measurement error). Use the flame brazing method, cooperate with FB102 flux, and see the data in the brackets for the brazing joint strength when the brazing base material is the following combination: red copper-H62 brass (σ b =215±25MPa, τ=205±30MPa), red copper-HPb62-3 lead brass (σ b =220±25MPa, τ=210±30MPa), red copper-HPb59-3 lead brass (σ b =220±25MPa, τ=210±30MPa).

Embodiment 3

[0035] A new type of copper-phosphorus solder containing hafnium, zirconium and cobalt, the composition of which is: P7.6%, Sn7.0%, Co0.15%, Hf0.05%, Zr0.05, and the balance is Cu.

[0036] The solidus temperature of the "new copper-phosphorus solder containing hafnium, zirconium and cobalt" obtained from the above composition ratio is 585°C ± 10°C, and the liquidus temperature is 645°C ± 10°C (both taking into account the measurement error). Use the flame brazing method, cooperate with FB102 flux, and see the data in the brackets for the brazing joint strength when the brazing base material is the following combination: red copper-H62 brass (σ b =215±25MPa, τ=205±30MPa), red copper-HPb62-3 lead brass (σ b =220±25MPa, τ=210±30MPa), red copper-HPb59-3 lead brass (σ b =220±25MPa, τ=210±30MPa).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed is a copper phosphorus brazing alloy with hafnium zirconium cobalt, and belongs to the technical field of soldering material of metal materials. The chemical ingredients includes, by weight: 5.0% to 8.0% of P, 4.5% to 10.0% of Sn, 0.05% to 0.35% of Co, 0.01% to 0.2% of Hf, 0.01% to 0.2% of Zr, and the balance being Cu. The adding proportion of the Hf element and the Zr element is Hf : Zr =1:1. According to the copper phosphorus brazing alloy, obtained according to the above proportion with the hafnium zirconium cobalt, the solidus line temperature ranges from 575 to 595 DEG C, and the liquidus line temperature ranges from 635 to 655 DEG C (measuring errors are considered both). The copper phosphorus brazing alloy with the hafnium zirconium cobalt has the advantages of 'high phosphorus, high tin, high plasticity and low melting point', the copper phosphorus brazing alloy can be processed into fine wires with the diameter of 0.5 to 1.2mm, and the requirements of soldering when HPb62-3 lead brass and HPb59-3 lead brass are adopted to produce products in the household appliance industry and the hardware industry can be met.

Description

technical field [0001] The invention belongs to the technical field of brazing materials of metal materials, and in particular relates to a copper-phosphorus brazing material containing hafnium, zirconium and cobalt. Background technique [0002] The BCu86SnPNi solder used in the existing technology (GB / T6418-2008 "Copper-based solder"), because the P element range (mass fraction, the same below) in its chemical composition is 4.8% to 5.8%, the highest is only 5.8% , and the melting temperature range is solidus 620 ° C, liquidus 670 ° C; and BCu86SnP solder, the P element range in the chemical composition is 6.4% to 7.2%, the highest still only reaches 7.2%, and the melting temperature range is solid phase Line 650 ℃, liquidus 700 ℃, still can not meet the RoHS directive "exempt" lead brazing needs of less than or equal to 4% lead brass. Due to the implementation of the RoHS directive, in order to reduce manufacturing costs, domestic and foreign companies have adopted lead ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/30
CPCB23K35/302
Inventor 薛鹏薛松柏沈以赴龙伟民马佳
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap