a rust removal paste

A technology of rust removal slurry and aluminum oxide polishing powder, which is applied in the field of metal surface polishing slurry, can solve the problem of losing metallic luster on the surface, and achieve the effect of preventing re-rusting

Active Publication Date: 2016-01-20
江苏意迪驱动设备有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Iron devices will inevitably be oxidized to a certain extent during long-term contact with the air, especially in a humid environment, causing a layer of rust on the surface of the device. Although the existing rust removal treatment agent can remove the rust on the surface, the rust removal If the finished iron is not treated with anti-corrosion treatment, it will soon be oxidized on the surface and lose its metallic luster, and even regenerate rust.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A kind of derusting slurry, consisting of 1 kg of alumina polishing powder (α-Al with a particle size of 4-15 μm 2 o 3 ), 0.3 kg of octadecyltriethoxysilane (CAS: 7399-00-0), 0.2 kg of stearic acid, 0.1 kg of glycerol, 0.01 kg of phosphoric acid, 0.01 kg of manganese dioxide, 0.01 kilogram of sodium lauryl sulfonate and 8.37 kilograms of water are obtained after grinding and mixing.

Embodiment 2

[0013] A kind of derusting slurry, consisting of 2 kg of alumina polishing powder (α-Al with a particle size of 10-25 μm 2 o 3 ), 0.2 kg of octadecyltriethoxysilane, 0.3 kg of stearic acid, 0.1 kg of glycerin, 0.1 kg of phosphoric acid, 0.1 kg of manganese dioxide, 0.05 kg of dodecylsulfonic acid Sodium and 7.15 kg of water, obtained after grinding and mixing.

Embodiment 3

[0015] A kind of derusting slurry, consisting of 3 kg of alumina polishing powder (α-Al with a particle size of 25-50 μm 2 o 3 ), 0.1 kg of octadecyltriethoxysilane, 0.01 kg of stearic acid, 0.2 kg of glycerin, 0.05 kg of phosphoric acid, 0.05 kg of manganese dioxide, 0.03 kg of nonylphenol polyoxyethylene Ether NP-10 and 6.56 kg of water were obtained after grinding and mixing uniformly.

[0016] Use of the derusting slurry: use a polishing cloth to dip the slurry, and polish the surface of the iron utensil until the utensil shows a metallic luster, then leave it for 10-20 minutes, and finally rinse with water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to derusting slurry which contains 10-30wt% of aluminum oxide polishing powder, 1-3wt% of octadecyl triethoxy silane, 0.1-3wt% of stearic acid, 1-2wt% of glycerol, 0.1-1wt% of phosphoric acid, 0.1-1wt% of manganese dioxide, 0.1-0.5wt% of surfactant and the balance of water. According to the invention, the derusting slurry can remove iron rust on surfaces of iron devices, and can simultaneously form a protective film, thereby preventing the iron devices from rusting again.

Description

technical field [0001] The invention relates to a slurry for metal surface polishing. Background technique [0002] Iron devices will inevitably be oxidized to a certain extent during long-term contact with air, especially in humid environments, which will cause a layer of rust on the surface of the device. Although the existing rust removal treatment agent can remove the rust on the surface, the rust removal If the finished iron is not treated with anti-corrosion treatment, the surface will soon be oxidized again and lose its metallic luster, and even rust will regenerate. Contents of the invention [0003] The object of the present invention is to provide a rust removal slurry. [0004] In order to achieve the above object, the present invention provides the following technical solutions: [0005] A rust removal slurry, containing 10-30wt% alumina polishing powder, 1-3wt% octadecyltriethoxysilane, 0.1-3wt% stearic acid, 1-2wt% glycerin , 0.1-1wt% phosphoric acid, 0.1-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23F3/00
Inventor 杨龙兴
Owner 江苏意迪驱动设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products