Anti-mildew formaldehyde-removing coating

A coating and formaldehyde technology, applied in the field of anti-mildew and formaldehyde-removing coatings, can solve the problems of short duration and poor anti-mildew ability, and achieve the effect of prolonging the service life, improving the sterilization and antibacterial ability, and maintaining the sterilization and anti-mildew effect.

Active Publication Date: 2014-01-29
苏州市东挺河智能科技发展有限公司
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem of poor anti-mildew ability and short duration of decoration coatings in the prior art, one of the purposes of the present invention is to provide an anti-mildew and formaldehyde-removing coating, which can effectively resist mildew and has a long-lasting effect. At the same time, the coating also has the effect of removing formaldehyde

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A mildew-resistant and formaldehyde-removing coating, the composition ratio (by weight) of the coating is as follows: 100 parts of polystyrene-acrylic acid copolymer, 26 parts of talcum powder less than 100 microns, 8 parts of wetting agent, and 6 parts of titanium dioxide , 10 parts of anti-mildew fungicide, 3 parts of bamboo charcoal, 40 parts of water, the anti-mold fungicide is nano-TiO 2 , Nano ZnO and ZrO 2 mixture of nano-TiO 2 , The particle size of nano-ZnO is 30-50 nanometers, ZrO 2 The particle size is -400 mesh, and the ratio of the three is TiO 2 :ZnO:ZrO 2 =1:1:0.5.

[0021] After testing: mildew resistance grade 0, antibacterial rate 98%, formaldehyde removal rate 97%.

Embodiment 2

[0023] A mildew-resistant and formaldehyde-removing coating, the composition ratio (by weight) of the coating is as follows: 100 parts of polyacrylic acid copolymer, 30 parts of talcum powder less than 100 microns, 3 parts of dispersant powder, 4 parts of wetting agent, 10 parts of ultramarine blue 8 parts, 8 parts of antimold bactericide, 5 parts of diatomaceous earth, 50 parts of water, described antimold bactericide is nano-TiO 2 , Nano ZnO and ZrO 2 mixture of nano-TiO 2 , The particle size of nano-ZnO is 30-50 nanometers, ZrO 2 The particle size is -400 mesh, and the ratio of the three is TiO 2 :ZnO:ZrO 2 =2:1:0.5.

[0024] After testing: mildew resistance level 0, antibacterial rate 98.5%, formaldehyde removal rate 97.5%.

Embodiment 3

[0026] A mildew-resistant and formaldehyde-removing coating, the composition ratio (by weight) of the coating is as follows: 100 parts of polyvinyl acetate-acrylic acid copolymer, 28 parts of talcum powder less than 100 microns, 2 parts of dispersant, 2 parts of wetting agent , 2 parts of defoamer, 2 parts of thickener, 8 parts of titanium dioxide, 9 parts of anti-mildew bactericide, 2 parts of activated carbon, 1 part of diatomaceous earth, 1 part of perlite, 45 parts of water, the anti-mold bactericide Nano TiO 2 , Nano ZnO and ZrO 2 mixture of nano-TiO 2 , The particle size of nano-ZnO is 30-50 nanometers, ZrO 2 The particle size is -400 mesh, and the ratio of the three is TiO 2 :ZnO:ZrO 2 =1.5:1:0.5.

[0027] After testing: mildew resistance grade 0, antibacterial rate 98.6%, formaldehyde removal rate 97.3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-mildew formaldehyde-removing coating. The coating contains the following components in part by weight: 100 parts of polystyrene-acrylic copolymer or polyacrylic acid copolymer or polyvinyl acetate-acrylic copolymer, 26-30 parts of talcum powder, 5-8 parts of additive, 6-10 parts of pigment, 8-10 parts of anti-mildew bactericide, 3-5 parts of adsorbent and 40-50 parts of water, wherein the anti-mildew bactericide is the mixture of nanometer TiO2, nanometer ZnO and ZrO2, the granularity of nanometer TiO2 and nanometer ZnO is 30-50 nanometers, the granularity of ZrO2 is minus 400 meshes, and the ratio of nanometer TiO2, nanometer ZnO to ZrO2 is (1-2):1:0.5. The anti-mildew formaldehyde-removing coating is capable of effectively resisting mildewing and long in effect, and the coating also has a formaldehyde-removing function.

Description

technical field [0001] The invention relates to the field of chemical industry, in particular to an anti-mildew and formaldehyde-removing coating. Background technique [0002] At present, in house decoration, due to the formaldehyde, benzene series, TVOC and other harmful substances brought by various decoration materials, the home decoration pollution and the harmful substances in the indoor air exceed the standard. It has seriously interfered with people's daily life. The long-term absorption of this formaldehyde-containing gas by the human body can cause various diseases, and even endanger human life in serious cases. Therefore, it is necessary to control the indoor air pollution of the renovated rooms and the newly purchased furniture, and eliminate the pollution of harmful gases brought by the new furniture. In order to ensure that the content of indoor harmful gases is within the range stipulated by the state, people can live in a healthy environment. [0003] In r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/08C09D133/02C09D131/04C09D5/14C09D7/12
Inventor 李聚刚钱振宇陈晓龙
Owner 苏州市东挺河智能科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com