Method for improving cold forming performance of GH4090 cold-rolled band

A cold-rolled strip and cold-forming technology, which is applied in the field of improving the cold-forming properties of GH4090 cold-rolled strips, can solve problems such as long holding time, and achieve the effects of less oxidation deformation, improved cold-forming properties, and low temperature.

Active Publication Date: 2014-02-05
AECC AVIATION POWER CO LTD
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention is used for structural steel. Since the structural steel and the high-temperature alloy involved in this patent belong to different metal material fields, the processing methods of the two alloys are essentially different, and the heat preservation time of this patent is very long, which is not applicable at all. Strip

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The method for improving the cold forming performance of GH4090 cold-rolled strip adopts the following steps in the present embodiment:

[0022] Step 1: Softening treatment before cold forming: first heat the air furnace to 960°C; then put the GH4090 cold-rolled strip into the air furnace, raise the temperature to 960°C, and keep it warm for 15 minutes; then take out the GH4090 cold-rolled strip and cool it in air To below 20°C; obtain softened GH4090 cold-rolled strip;

[0023] Step 2: cold-bending the GH4090 cold-rolled strip softened in step 1 according to the parts requirements;

[0024] Step 3: Aging treatment after cold forming: first raise the temperature of the air furnace to 680°C; then put the workpiece cold bent and formed in step 2 into the air furnace and keep it warm for 4 hours; then take out the workpiece and air cool it to below 20°C to obtain aging processed artifacts.

[0025] Table 1 shows the comparison between softening treatment and softening tr...

Embodiment 2

[0029] The method for improving the cold forming performance of GH4090 cold-rolled strip adopts the following steps in the present embodiment:

[0030] Step 1: Softening treatment before cold forming: first heat the air furnace to 970°C; then put the GH4090 cold-rolled strip into the air furnace, raise the temperature to 970°C, and keep it warm for 10 minutes; then take out the GH4090 cold-rolled strip and cool it in air To below 20°C; obtain softened GH4090 cold-rolled strip;

[0031] Step 2: cold-bending the GH4090 cold-rolled strip softened in step 1 according to the parts requirements;

[0032] Step 3: Aging treatment after cold forming: first raise the temperature of the air furnace to 700°C; then put the workpiece cold bent and formed in step 2 into the air furnace and keep it warm for 3 hours; then take out the workpiece and air cool it to below 20°C to obtain aging processed artifacts.

[0033] Table 2 shows the comparison between softening treatment and softening tr...

Embodiment 3

[0037] The method for improving the cold forming performance of GH4090 cold-rolled strip adopts the following steps in the present embodiment:

[0038] Step 1: Softening treatment before cold forming: first heat the air furnace to 990°C; then put the GH4090 cold-rolled strip into the air furnace, raise the temperature to 990°C, and keep it warm for 15 minutes; then take out the GH4090 cold-rolled strip and cool it in air To below 20°C; obtain softened GH4090 cold-rolled strip;

[0039] Step 2: cold-bending the GH4090 cold-rolled strip softened in step 1 according to the parts requirements;

[0040] Step 3: Aging treatment after cold forming: first raise the temperature of the air furnace to 720°C; then put the workpiece cold bent and formed in step 2 into the air furnace and keep it warm for 4 hours; then take out the workpiece and air cool it to below 20°C to obtain aging processed artifacts.

[0041] Table 3 shows the comparison between softening treatment and softening tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for improving the cold forming performance of a GH4090 cold-rolled band. The cold forming performance of the GH4090 cold-rolled band is improved by the three stages of softening treatment before cold forming, cold bending forming, and aging treatment after the cold forming. Before the cold forming of a GH4090 component, a new heat treatment system is adopted and a once softening treatment process is added to reduce the hardness of a material, so that the cold forming is performed smoothly. The method has the advantages that firstly, the temperature in the softening treatment method is lower than common softening treatment (solid solution annealing temperature), the oxidation deformation degree of the component is low, and moreover, crystal grains of the GH4090 material cannot grow; secondly, by adopting the new process method, the hardness of the material of the component is reduced properly on the basis that guaranteeing the mechanical performance of the material is guaranteed, so that the material has proper hardness (HV289-399 / HRC30-40), the hardness is reduced, and meanwhile, the plasticity of the material is improved, and the cold forming performance of the material is improved.

Description

technical field [0001] The invention relates to the field of materials and heat treatment, in particular to a method for improving the cold forming performance of GH4090 cold-rolled strip. Background technique [0002] GH4090 is an age-strengthened nickel-deformed superalloy, which contains a relatively high amount of cobalt and various strengthening elements. The alloy has high tensile strength and creep resistance at 815-870°C, good oxidation resistance and corrosion resistance, high fatigue strength and good formability and welding under the repeated alternating action of cold and heat. sex. Mainly supply hot-rolled and cold-drawn bars, cold-rolled plates, strips and cold-drawn wire. Used for turbine discs, blades, high-temperature fasteners, clamps, sealing rings and elastic components of turbine engines. [0003] GH4090 cold-rolled hard strip, the supply state is solution plus cold-rolled, with high hardness (HV460~466 / HRC46.5~47.0), which cannot be followed by cold ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22F1/10
Inventor 刘红斌杨辉霍世军吴博赵刚张晓鹏
Owner AECC AVIATION POWER CO LTD