A kind of monolithic wall and floor tile paving film and preparation method thereof

A technology for molding walls and floor tiles, applied in the direction of adhesives, epoxy resin adhesives, adhesive types, etc., can solve the problems of huge manpower and material resources, cost, poor operation efficiency, etc., to improve paving efficiency and reduce transportation costs. , the obvious effect of transportation advantages

Inactive Publication Date: 2016-08-03
赵贤
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 2. Inconvenient transportation and storage
[0006] Because the characteristics of yellow sand cement determine its heavy weight, which determines that a huge amount of manpower and material resources must be spent in the transportation process.
This virtually increases the difficulty of laying the walls, transporting floor tiles, and storing yellow sand cement. Of course, more costs are incurred at the same time.
[0007] 3. Not waterproof
Although there are related waterproof additives on the market, it has been proved in actual use that they do not have reassuring waterproof performance
[0009] 4. The quality is uncontrollable
[0011] 5. Poor operating efficiency
[0013] 6. Unable to adhere to the surface layer of special materials
[0014] Today, with the rapid development of material science, the construction materials of building walls and floors are no longer limited to bricks, sand, and cement. However, our traditional wall and floor tile laying methods are effective for rough surfaces such as mortar, brick, and stone. In addition, it is impossible to form an effective connection to metal, painted panels, PVC and other types of composite surfaces.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of monolithic wall and floor tile paving film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Take the modified rubber with a ratio of 1:0.4:0.01 of rubber, quartz sand, and carbon black, add 0.1% of the total mass of sulfur, and then press it into a base layer with a thickness of 3 mm. Use phenolic resin as an adhesive to stick on the base layer. A layer of glass fiber mesh cloth with a thickness of 1mm. The mesh size of the mesh cloth is 5mm×5mm. Then spray glue with a spray gun on the base layer and the functional layer to form an adhesive layer. The adhesive layer is in the phenolic resin primer. Add 1 unit of polysulfide rubber, 0.5 unit of epoxy resin, 2 units of quartz powder, and 0.6 unit of calcium carbonate.

Embodiment 2

[0036] Take the modified rubber with a ratio of 1:0.4:0.01 of rubber, quartz sand, and carbon black, add 0.1% of the total mass of sulfur, and then press it into a base layer with a thickness of 3 mm. Use phenolic resin as an adhesive to stick on the base layer. A layer of glass fiber mesh cloth with a thickness of 1mm. The mesh size of the mesh cloth is 5mm×5mm. Then spray glue with a spray gun on the base layer and the functional layer to form an adhesive layer. The adhesive layer is in the phenolic resin primer. Add 1 unit of butyl latex, 0.4 unit of carbon black, 1 unit of calcium carbonate, 1 unit of mica, 0.2 unit of xylene, and 0.3 unit of pitch.

Embodiment 3

[0038] Take the modified rubber with a ratio of 1:0.4:0.01 of rubber, quartz sand, and carbon black, add 0.1% of the total mass of sulfur, and then press it into a base layer with a thickness of 3 mm. Use phenolic resin as an adhesive to stick on the base layer. A layer of glass fiber mesh cloth with a thickness of 1mm. The mesh size of the mesh cloth is 5mm×5mm. Then spray glue with a spray gun on the base layer and the functional layer to form an adhesive layer. The adhesive layer is in the phenolic resin primer. Add 1 unit of bisphenol A epoxy resin, 0.8 unit of T31 curing agent, 1 unit of calcium carbonate, and 0.6 unit of propylene oxide butyl ether.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an integral wall and floor tile paving film and a preparation method thereof, which belongs to the field of building materials, and in particular relates to the technical field of building paving film. The monolithic wall and floor tile paving film includes a base layer, an adhesive layer, and a functional layer. It is characterized by light weight, convenient transportation, high operating efficiency, and can be applied to various materials.

Description

technical field [0001] The invention relates to the technical field of building paving film. Background technique [0002] As far as the paving methods of wall and floor tiles and similar blocks at home and abroad are concerned, only yellow sand cement and water are commonly used to form a certain proportion of mixed mortar to bond the base and surface blocks. Other improved technical measures are only aimed at the performance of the mortar, and the paving effect is improved through various performance additives. Although this type of traditional paving method has certain advantages, its disadvantages are also obvious: [0003] 1. Heavy weight [0004] Generally, the specific gravity of the mixed mortar used for laying tiles is 1.6-1.8 tons / cubic meter. However, due to the limitation of process requirements for large blocks, taking 800mm×800mm floor tiles as an example, the leveling thickness used in construction is usually required to reach 5CM or even higher. On the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/02C09J181/04C09J163/00C09J123/22C09J163/02C09J11/04C08L21/00C08K3/36C08K3/04C08K3/06
Inventor 赵贤
Owner 赵贤