A kind of uv-cured elastic touch paper varnish and its construction method

A construction method and light-curing technology, applied in papermaking, paper coatings, textiles and papermaking, etc., can solve the problems of limited application, slow film forming speed, high environmental cost, and achieve the effect of excellent elastic feel

Active Publication Date: 2016-11-02
HUIZHOU CHANGRUNFA PAINT
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, there are also restrictions on the construction conditions of traditional coatings during construction, which has the disadvantages of slow film formation, high energy consumption, low efficiency, and high environmental costs.
In the application of paper varnish, it cannot be applied to construction conditions such as high-speed roller coating, and can no longer meet people's high-speed and efficient work and life concepts, so it greatly limits its application in paper varnish.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A UV light-cured elastic touch paper varnish, consisting of the following components in parts by weight:

[0037] 20 parts of Taiwan double bond chemical UV elastic resin U-058;

[0038] 25 parts of monomer, the monomer is a mixture of isobornyl acrylate (IBOA) and 1,6-hexanediol diacrylate (HDDA) in a mass ratio of 2:1;

[0039] 10 parts of active amine;

[0040] 5 parts of mixed photoinitiators, described mixed photoinitiators are the mixture of photoinitiator BP and photoinitiator TPO;

[0041] 8 parts of Japanese elastic powder 5070D;

[0042] 5 parts of 20nm grade fumed silica matting powder;

[0043] 1 part of auxiliary agent, this auxiliary agent is made up of 0.5 part of dispersant and 0.5 part of defoamer;

[0044] 24 parts of solvent, the solvent selects environmental protection butyl acetate for use.

[0045] Put the above components into the stirring tank and disperse evenly at high speed before use.

[0046] The tested viscosity of the final finished ...

Embodiment 2

[0048] A UV light-cured elastic touch paper varnish, consisting of the following components in parts by weight:

[0049] 18 parts of Taiwan double bond chemical UV elastic resin U-058;

[0050] 28 parts of monomer, the monomer is a mixture of isobornyl acrylate (IBOA) and 1,6-hexanediol diacrylate (HDDA) in a mass ratio of 2:1;

[0051] 10 parts of active amine;

[0052] 4 parts of mixed photoinitiators, described mixed photoinitiators are the mixture of photoinitiator BP and photoinitiator TPO;

[0053] 10 parts of Japanese elastic powder 5070D;

[0054] 7 parts of 20nm grade fumed silica matting powder;

[0055] 1.5 parts of additives;

[0056] 26 parts solvent.

[0057] Put the above components into the stirring tank and disperse evenly at high speed before use.

[0058] The tested viscosity of the final finished paint is about 550~650cps, and the product is stable and can be stored at room temperature for 60 days without deterioration and without sediment. During ro...

Embodiment 3

[0060] A UV light-cured elastic touch paper varnish, consisting of the following components in parts by weight:

[0061] 22 parts of Taiwan double bond chemical UV elastic resin U-058;

[0062] 22 parts of monomer, the monomer is a mixture of isobornyl acrylate (IBOA) and 1,6-hexanediol diacrylate (HDDA) at a mass ratio of 2:1;

[0063] 12 parts of active amine;

[0064] 7 parts of mixed photoinitiator, described mixed photoinitiator is the mixture of photoinitiator BP and photoinitiator TPO;

[0065] 10 parts of Japanese elastic powder 5070D;

[0066] 7 parts of 20nm grade fumed silica matting powder;

[0067] 2 parts auxiliary;

[0068] 22 parts solvent.

[0069] Put the above components into the stirring tank and disperse evenly at high speed before use.

[0070] The tested viscosity of the final finished paint is about 550~650cps, and the product is stable and can be stored at room temperature for 60 days without deterioration and without sediment. During roller coa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of coatings, in particular to an elastic handle coating. A UV photocurable elastic touch paper varnish, which is composed of the following components in parts by weight: 18-22 parts of UV elastic resin; 22-28 parts of monomers, the monomers are isobornyl acrylate and A mixture of 1,6-hexanediol diacrylate; 8-12 parts of active amine; 3-7 parts of photoinitiator; 5-10 parts of elastic powder; 3-7 parts of fumed silica matting powder; 0.5~2 parts of additives; 22~26 parts of solvents. The UV light-cured elastic touch paper varnish of the present invention is suitable for high-speed roller coating, can improve work efficiency, reduce the difficulty of coating operation, and avoid personal injury.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an elastic handle coating. Background technique [0002] Traditional elastic touch paint has the characteristics of rich expressiveness, strong three-dimensional effect, flexibility, strong plasticity, strong adhesion, scrubbing, acid and alkali resistance, no fading, no peeling, no cracking, easy maintenance and recoating, etc. [0003] However, there are also restrictions on the construction conditions of traditional coatings during construction, which has the disadvantages of slow film formation, high energy consumption, low efficiency, and high environmental costs. In the application of paper varnish, it cannot be applied to construction conditions such as high-speed roller coating, and can no longer meet people's high-speed and efficient work and life concepts, so it greatly limits its application in paper varnish. Contents of the invention [0004] The technical problem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H19/16
Inventor 李东林李晓雷
Owner HUIZHOU CHANGRUNFA PAINT