High-temperature resistant toxicity-reducing release agent and its preparation method

A technology of high temperature resistance and release agent, which is applied in the direction of manufacturing tools, casting molding equipment, metal processing equipment, etc., can solve the problems of poor release effect of release agent, harm to human health, complicated preparation methods, etc., and achieve the release effect Good, reduce the harm to human health, reduce the effect of preparation cost

Active Publication Date: 2014-02-26
HARBIN FRP INST
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problems that the preparation and application process of the existing release agent pollutes the environment, endangers human health, high preparation cost, complicated preparation method and poor release effect of the existing release agent, and provides a high-temperature-resistant and toxicity-reducing Release agent and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0019] Specific embodiment 1: The high temperature-resistant and toxic-reducing release agent of this embodiment is made of A, B, C and D; wherein A is silicone rubber, B is ethyl orthosilicate, and C is dibutyl dilauric acid A mixture of one or two of tin and dibutyltin dilaurate in any ratio, D is ethyl acetate, and the mass ratio of A, B, C and D is 100:1~50:1~50 : 1~50.

specific Embodiment approach 2

[0020] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the silicone rubber is room temperature vulcanized silicone rubber. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0021] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is that: the high-temperature-resistant and toxic-reducing release agent is made of A, B, C and D; wherein A is silicone rubber, and B is positive Ethyl silicate, C is dibutyltin dilaurate, D is ethyl acetate, and the mass ratio of A, B, C and D is 100:1-50:1-50:1-50. Others are the same as in the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A high-temperature resistant toxicity-reducing release agent and its preparation method relate to a release agent and its preparation method. According to the invention, the problem that preparation and application processes of a present release agent pollute the environment, are harmful to the health and require high preparation cost and complex preparation method and a present release agent has poor demoulding effects is solved. The high-temperature resistant toxicity-reducing release agent is prepared from A, B, C and D, wherein A is silicone rubber; B is tetraethyl orthosilicate; C is any one of dibutyltindilaurate and dibutyltin dilaurate or a mixture of the above two compounds according to any ratio; D is ethyl acetate; and the mass ratio of A to B to C to D is 100:1-50:1-50:1-50. The method comprises the following steps: 1, mixing A, B, C and D; and 2, preparing the high-temperature resistant toxicity-reducing release agent. The method is benefit for environmental protection, minimizes harm to human body, and requires low cost and simple technology. The prepared release agent has high temperature resistance and good demoulding effect. The release agent provided by the invention can be used in the fields of national defense, aerospace, chemical industry and civilian use.

Description

technical field [0001] The invention relates to a release agent and a preparation method thereof. Background technique [0002] The mold release agent is an important component in the molding process of composite materials. It not only affects the surface properties of composite materials, but also affects whether the product can be released from the mold. No matter how important the product and mold are, if the product sticks to the mold, If it cannot be released from the mold, the product and the mold can only be scrapped, so the role of the release agent is extremely important. [0003] The release agents in the molding process of composite materials are mainly divided into oil waxes, polyvinyl alcohols, silicon esters, etc., but they are used on plaster molds or sand molds. When making composite materials, after the product is demoulded, the plaster mold Or the blocky gypsum or blocky gravel in the sand mold is easy to stick or remain on the composite product, which not...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C33/64B29C33/62B29C33/60B22C3/00
Inventor 贾丽霞李晓光马俊龙
Owner HARBIN FRP INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products