A light-resistant ink, its preparation method and its application in light-resistant transfer film

A technology of light fastness and ink, applied in ink, application, household utensils, etc., can solve the problem that the pigment powder is heavy and difficult to print, and achieve the effect of reducing ink powder weight, color retention, and good wetting performance

Active Publication Date: 2015-12-09
DONGGUAN ZHUOYI PRINTING PROD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Another object of the present invention is to provide a method for preparing light-resistant ink, which can solve the problem of heavy pigment powder and is difficult to print, and has the characteristics of higher pigment fineness and good printing effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A light-resistant ink, its preparation method and its application in light-resistant transfer film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] like figure 1 As shown, a light-resistant transfer film includes a base film layer 1, a release layer 2 and an adhesive layer 5 from top to bottom, and an ultraviolet absorber is arranged between the base film layer 1 and the release layer 2. The material coating 3 is provided with a light-resistant ink coating between the ultraviolet absorbing material coating 3 and the adhesive layer 5 .

[0066] The ultraviolet absorbing material coating 3 is coated with an ultraviolet absorbing material, and the formula of the ultraviolet absorbing material is:

[0067] Ultraviolet absorber UV-P5 parts

[0068] Ultraviolet absorber UV-96 parts

[0069] UV absorber UV-3275 parts

[0070] Acrylic resin liquid 45 parts

[0071] Acetate butyl cellulose resin liquid 12 parts

[0072] 6 parts isopropanol

[0073] 20 parts of n-propyl acetate.

[0074] A light-resistant ink coated on the above-mentioned light-resistant ink coating 4, prepared from the following components in parts b...

Embodiment 2

[0090] like figure 1 As shown, a light-resistant transfer film includes a base film layer 1, a release layer 2 and an adhesive layer 5 from top to bottom, and an ultraviolet absorber is arranged between the base film layer 1 and the release layer 2. The material coating 3, the light-resistant ink coating 4 is arranged between the ultraviolet absorbing material coating 3 and the adhesive layer 5.

[0091] The ultraviolet absorbing material coating 3 is coated with an ultraviolet absorbing material, and the formula of the ultraviolet absorbing material is:

[0092] Ultraviolet absorber UV-P6 parts

[0093] Ultraviolet absorber UV-95 parts

[0094] Ultraviolet absorber UV-3276 parts

[0095] Acrylic resin liquid 48 parts

[0096] Acetate butyl cellulose resin liquid 14 parts

[0097] 5 parts isopropanol

[0098] 18 parts of n-propyl acetate.

[0099] A light-resistant ink coated on the above-mentioned light-resistant ink coating 4, prepared from the following components in...

Embodiment 3

[0115] likefigure 1 As shown, a light-resistant transfer film includes a base film layer 1, a release layer 2 and an adhesive layer 5 from top to bottom, and an ultraviolet absorber is arranged between the base film layer 1 and the release layer 2. The material coating 3, the light-resistant ink coating 4 is arranged between the ultraviolet absorbing material coating 3 and the adhesive layer 5.

[0116] The ultraviolet absorbing material coating 3 is coated with an ultraviolet absorbing material, and the formula of the ultraviolet absorbing material is:

[0117] Ultraviolet absorber UV-P6 parts

[0118] Ultraviolet absorber UV-95 parts

[0119] Ultraviolet absorber UV-3276 parts

[0120] Acrylic resin liquid 50 parts

[0121] Acetate butyl cellulose resin liquid 18 parts

[0122] 6 parts isopropanol

[0123] 15 parts of n-propyl acetate.

[0124] A light-resistant ink coated on the above-mentioned light-resistant ink coating 4, prepared from the following components in p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical fields of a transfer film and a printing ink formulation, and particularly relates to sun-proof printing ink as well as a preparation method and an application thereof in a sun-proof transfer film. The sun-proof printing ink is prepared from the following components in parts by mass: 18-20 parts of inorganic paint, 1-1.5 parts of a wetting agent, 45-50 parts of acrylic resin liquid, 12-18 parts of cellulose acetate resin liquid, 1-1.5 parts of a dispersing agent, 1-1.5 parts of fumed silica, 5-6 parts of isopropanol and 12-15 parts of n-propyl acetate. The inorganic paint and the wetting agent are mixed and ground, so as to obtain paint powder with high fineness; the printing ink is uniformly mixed. The sun-proof printing ink is applied to the sun-proof transfer film, has a sun-proof level up to an 8 level, and is particularly suitable for printing outdoor products.

Description

technical field [0001] The invention relates to the technical field of transfer printing film and its ink formulation, in particular to a sun-resistant ink, its preparation method and its application in the sun-resistant transfer film. Background technique [0002] Thermal transfer printing is an emerging printing process, which has been introduced from abroad for more than 10 years. Thermal transfer film refers to the graphic and text with adhesive, under the joint action of heat and pressure, it can be separated from the carrier film together with the protective layer, and is firmly transferred to the special functional printing film on the surface of the substrate. [0003] Therefore, the transfer film used in practice must have good detachability, thermal adhesion and beautiful graphics. In the process of transfer printing, it must be very good to show that the graphics and texts can be "loose" - that is, they can be separated from the carrier film, and can be "tight" -...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More